Low temperature silicon nitride CVD process
Assignee: Anicon Inc
•
Filing: 1986-08-25
•
Granted: 1988-01-19
•
Expires: 2006-08-25
Abstract
Abstract Thermal CVD process for forming Si 3 N 4 -type films on substrates by reaction of gaseous NF 3 with gaseous disilane at a temperature in the range of 250°-500° C., at pressures of 0.1-10 Torr. The mole ratio of NF 3 to silane is in the range of 0.5-3.0 and the reaction zone is preferably isothermal (T controlled to within + 5° C.). The resulting films have RI's in the range of 1.4 to 3.0. The process parameters can be controlled to dope the film with H and/or F, or to create zones of differing properties within the film. The process does not cause radiation damage, metal migration, stored charge dissipation or high levels of impurities. Control of distance between adjacent wafers and wafer-to-wall spacing combined with laminar gas flow gives excellent film thickness uniformity, on the order of below about ±5% across the wafer face, both within (across) wafers and from wafer to wafer (batch uniformity).
Inventors
- 👤 Derrick W. Foster
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 09:09
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/34; C23C16/345
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
131 words
A thermal CVD process for forming silicon nitride-type films comprising the steps of: (a) introducing NF 3 and Si 2 H 6 as reactant gases into a CVD reaction zone containing a substrate on which a silicon nitride-type film is to be formed; (b) maintaining the temperature of said zone and said substrate within the range of from 250° C. to about 400° C.; (c) maintaining the pressure in said zone in the range of about 0.1 to about 10 Torr; and (d) passing said gases into contact with said substrate for a period of time sufficient to form a silicon nitride-type film thereon having a refractive index in the range of from about 1.4 to about 3.0; wherein the gases react to form the films without plasma activation or irradiation.
Claim 2
Dependent Claim
131 words
A thermal CVD process for forming silicon nitride-type films comprising the steps of: (a) introducing NF 3 and Si 2 H 6 as reactant gases into a CVD reaction zone containing a substrate on which a silicon nitride-type film is to be formed; (b) maintaining the temperature of said zone and said substrate within the range of from 250° C. to about 400° C.; (c) maintaining the pressure in said zone in the range of about 0.1 to about 10 Torr; and (d) passing said gases into contact with said substrate for a period of time sufficient to form a silicon nitride-type film thereon having a refractive index in the range of from about 1.4 to about 3.0; wherein the gases react to form the films without plasma activation or irradiation.
Claim 3
Dependent Claim
29 words
A thermal CVD process as in claim 1, wherein: (a) the mole ratio of NF 3 to silane is in the range of from about 0.5 to about 3.0.
Claim 4
Dependent Claim
37 words
A thermal CVD process as in claim 2, wherein: (a) said substrate is a silicon wafer, a metal object, a film having one or more Group III, IV or V elements or compounds, or a semiconductor device.
Claim 5
Dependent Claim
17 words
A thermal CVD process as in claim 1, wherein: (a) said reaction zone is maintained substantially isothermal.
Claim 6
Dependent Claim
52 words
A thermal CVD process as in claim 1, wherein: (a) the flow rate of said NF 3 gas is in the range of from about 100 Scc/min to about 1 Liter/min; and (b) the flow rate of said disilane is in the range of from about 100 Scc/min to about 400 Scc/min.
Claim 7
Dependent Claim
15 words
A thermal CVD process as in claim 2, wherein: (a) said mole ratio is 2.66±0.2.
Claim 8
Dependent Claim
15 words
A thermal CVD process as in claim 1, wherein: (a) said refractive index is 2.0±0.2.
Claim 9
Dependent Claim
24 words
A thermal CVD process as in claim 1, wherein: (a) said pressure is in the range from about 2 Torr to about 5 Torr.
Claim 10
Dependent Claim
27 words
A thermal CVD process as in claim 1, wherein: (a) said film formation rate is maintained in the range of from about 10 to about 500 Angstroms/minute.
Claim 11
Dependent Claim
26 words
A thermal CVD process as in claim 9, wherein: (a) said film formation rate is in the range of from about 30 to about 300 Angstroms/minute.
Claim 12
Dependent Claim
41 words
A thermal CVD process as in claim 1, wherein: (a) said substrate is disposed in a CVD boat; and (b) the substrate-to-wall and substrate-to-substrate distances are selected to substantially eliminate concavity or convexity in deposition of said film on said substrate.
Claim 13
Dependent Claim
33 words
A thermal CVD process as in claim 1, wherein said reaction zone is disposed in a reaction chamber or boat having a passivation film on at least a portion of the surface thereof.
Claim 14
Dependent Claim
44 words
A thermal CVD process as in claim 1, wherein said reaction zone is disposed in a reaction chamber or boat, said substrate is the reaction chamber surface or boat surface, and the silicon nitride-type film formed on the surface thereof is a passivation film.
Claim 15
Dependent Claim
35 words
A thermal CVD process as in claim 1, wherein: (a) the property of said resultant silicon nitride-type film is controlled by preselecting and maintaining the flow rates of said gaseous reactants for a preselected pressure.
Claim 16
Dependent Claim
52 words
A thermal CVD process as in claim 14, which includes the steps of: (a) controlling said flow rates to produce a film rich in Si; (b) increasing the pressure in said reaction zone to dope said film with a member selected from H, F and mixtures thereof to produce a semiconductive film.
Claim 17
Dependent Claim
44 words
A thermal CVD process as in claim 14, which includes the steps of: (a) selecting and maintaining a substantiall fixed sialne flow rate and reaction zone pressure; and (b) increasing said NF 3 flow rate to reduce the refractive index of said resultant film.
Claim 18
Dependent Claim
44 words
A thermal CVD process as in claim 14, which includes the steps of: (a) selecting and maintaining a substantially fixed NF 3 flow rate and reaction zone pressure; and (b) increasing said silane flow rate to increase the refractive index of said resultant film.
Claim 19
Dependent Claim
38 words
A thermal CVD process as in claim 14, wherein: (a) one more of said flow rate(s) and pressure is varied during the deposition of said film to produce a film having at least one refractive index gradient therein.
Claim 20
Dependent Claim
31 words
A thermal CVD process as in claim 5, wherein: (a) said mole ratio and flow rate and pressure are maintained to produce a film substantially stoichiometrically Si 3 N 4 .
References Cited (Backward Citations)
US4118539A
Cited
US4232063A
Cited
US4227907A
Cited
US4452874A
Cited
US4452875A
Cited
US4495218A
Cited
US4588610A
Cited
US4539933A
Cited
US4636401A
Cited
US4582020A
Cited
US4626449A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-01-18 | 1991-07-20 | 1992-01-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-01-18 | 1995-07-20 | 1996-01-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-01-18 | 1999-07-20 | 2000-01-19 | $7700.00 | Window Closed / Lapsed |