Plasma etching of blind vias in printed wiring board dielectric
Assignee: Texas Instruments Inc
•
Filing: 1987-04-13
•
Granted: 1988-01-19
•
Expires: 2007-04-13
Abstract
Abstract A method of plasma etching blind vias in printed wiring board dielectric which comprises the steps of providing a printed wiring board of organic material having a buried electrically conductive pattern in the organic material and an electrically conductive layer on the surface of the board, removing predetermined portions of the electrically conductive layer to expose the organic material thereunder and define at least one via location thereat, providing a plasma etching chamber having one or more pairs of spaced parallel electrodes, positioning the board between the said electrodes, electrically connecting the board to one of said electrodes and having the surface facing and parellel to the electrodes, filling the chamber with a mixture of an oxidizing gas and a fluorocarbon gas, etching the organic material from the exposed organic material at the surface to the buried pattern to expose the buried pattern by applying an RF signal across the electrodes, and forming an electrically conductive layer of the exposed surfaces of the organic material contacting the exposed buried pattern and the conductive layer.
Inventors
- 👤 Paula K. Tiffin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 11:07
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/0011; H05K3/0017; H05K3/0041; H05K2201/00; H05K2201/02; H05K2201/0275; H05K2201/0278; H05K2201/09; H05K2201/09209; H05K2201/095; H05K2201/09509; H05K2203/00; H05K2203/05; H05K2203/0548; H05K2203/0554; H05K3/46; H05K3/4644; H05K3/4652; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49155; Y10T29/49165
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
180 words
A method of forming blind vias in an organic printed wiring board, comprising the steps of: (a) providing a printed wiring board of organic material having a buried electrically conductive pattern in said organic material and an electrically conductive layer on the surface of said board; (b) removing predetermined portions of said electrically conductive layer to expose said organic material thereunder and define at least one via location thereat; (c) providing a plasma etching chamber having at least one pair of spaced parallel electrodes; (d) positioning said board between said electrodes, electrically connecting said board to one of said electrodes and having said surface facing and parallel to the said electrodes; (e) filling said chamber with a mixture of an oxidizing gas and a fluorocarbon gas; (f) etching said organic material from said exposed organic material at said surface to said buried pattern to expose said buried pattern by applying an RF signal across said electrodes; and (g) forming an electrically conductive layer on the exposed surfaces of said organic material contacting said exposed buried pattern and said conductive layer.
Claim 2
Independent Claim
180 words
A method of forming blind vias in an organic printed wiring board, comprising the steps of: (a) providing a printed wiring board of organic material having a buried electrically conductive pattern in said organic material and an electrically conductive layer on the surface of said board; (b) removing predetermined portions of said electrically conductive layer to expose said organic material thereunder and define at least one via location thereat; (c) providing a plasma etching chamber having at least one pair of spaced parallel electrodes; (d) positioning said board between said electrodes, electrically connecting said board to one of said electrodes and having said surface facing and parallel to the said electrodes; (e) filling said chamber with a mixture of an oxidizing gas and a fluorocarbon gas; (f) etching said organic material from said exposed organic material at said surface to said buried pattern to expose said buried pattern by applying an RF signal across said electrodes; and (g) forming an electrically conductive layer on the exposed surfaces of said organic material contacting said exposed buried pattern and said conductive layer.
Claim 3
Dependent Claim
34 words
A method as set forth in claim 1 wherein said organic material is taken from the class consisting of an epoxy resin filled with a material taken from the class consisting of aramid fibers.
Claim 4
Dependent Claim
19 words
A method as set forth in claim 1 wherein said layer and said pattern are each formed of copper.
Claim 5
Dependent Claim
19 words
A method as set forth in claim 2 wherein said layer and said pattern are each formed of copper.
Claim 6
Dependent Claim
34 words
A method as set forth in claim 1 further including the step of heating said board prior to step (f) to a temperature of from about 120 degrees C. to about 130 degrees C.
Claim 7
Dependent Claim
34 words
A method as set forth in claim 2 further including the step of heating said board prior to step (f) to a temperature of from about 120 degrees C. to about 130 degrees C.
Claim 8
Dependent Claim
34 words
A method as set forth in claim 3 further including the step of heating said board prior to step (f) to a temperature of from about 120 degrees C. to about 130 degrees C.
Claim 9
Dependent Claim
34 words
A method as set forth in claim 4 further including the step of heating said board prior to step (f) to a temperature of from about 120 degrees C. to about 130 degrees C.
Claim 10
Dependent Claim
20 words
A method as set forth in claim 1 wherein said oxidizing gas is oxygen and said fluorocarbon is carbon tetrafluoride.
Claim 11
Dependent Claim
20 words
A method as set forth in claim 2 wherein said oxidizing gas is oxygen and said fluorocarbon is carbon tetrafluoride.
Claim 12
Dependent Claim
20 words
A method as set forth in claim 7 wherein said oxidizing gas is oxygen and said fluorocarbon is carbon tetrafluoride.
Claim 13
Dependent Claim
20 words
A method as set forth in claim 8 wherein said oxidizing gas is oxygen and said fluorocarbon is carbon tetrafluoride.
Claim 14
Dependent Claim
23 words
A method as set forth in claim 9 wherein the ratio of said oxidizing gas to said fluocarbon is about 7 to 3.
Claim 15
Dependent Claim
23 words
A method as set forth in claim 10 wherein the ratio of said oxidizing gas to said fluocarbon is about 7 to 3.
Claim 16
Dependent Claim
23 words
A method as set forth in claim 11 wherein the ratio of said oxidizing gas to said fluocarbon is about 7 to 3.
Claim 17
Dependent Claim
23 words
A method as set forth in claim 12 wherein the ratio of said oxidizing gas to said fluocarbon is about 7 to 3.
Claim 18
Dependent Claim
39 words
A method as set forth in claim 1 wherein said RF signal is from about 40 kilohertz to about 13.56 megahertz at a power of about 2.5 watts per square inch of energized area of one of said electrodes.
Claim 19
Dependent Claim
39 words
A method as set forth in claim 2 wherein said RF signal is from about 40 kilohertz to about 13.56 megahertz at a power of about 2.5 watts per square inch of energized area of one of said electrodes.
Claim 20
Dependent Claim
39 words
A method as set forth in claim 15 wherein said RF signal is from about 40 kilohertz to about 13.56 megahertz at a power of about 2.5 watts per square inch of energized area of one of said electrodes.
Claim 21
Dependent Claim
39 words
A method as set forth in claim 16 wherein said RF signal is from about 40 kilohertz to about 13.56 megahertz at a power of about 2.5 watts per square inch of energized area of one of said electrodes.
References Cited (Backward Citations)
US4517050A
Cited
US4496420A
Cited
US4567062A
Cited
US4572764A
Cited
US4642160A
Cited
US4676865A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-01-18 | 1991-07-20 | 1992-01-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-01-18 | 1995-07-20 | 1996-01-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-01-18 | 1999-07-20 | 2000-01-19 | $7700.00 | Window Closed / Lapsed |