Solderable contact material
Assignee: The General Electric Company PLC
•
Filing: 1986-10-01
•
Granted: 1988-01-12
•
Expires: 2006-10-01
Abstract
Abstract It is often required to solder an electrical connection to a component or a lead thereto via a contact pad. At present pads are commonly of materials that tend to oxidize during any subsequent heat processing of the device, and are then difficult to solder. It has now been discovered that certain alloys of copper containing manganese may be used to construct contact pads that are both solderable and remain so even when ovened in air at 200 DEG C., and the invention provides a method of constructing solderable contact pads upon a chosen substrate, in which method there is formed on the relevant area of the substrate a layer of such a manganese/copper alloy.
Inventors
- 👤 Brian W. Ely
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 06:40
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/34; C03C17/36; C03C17/40; B; B23; B23K; B23K35/00; B23K35/001; C03C17/06; G; G02; G02F; G02F1/00; G02F1/01; G02F1/13; G02F1/133; G02F1/1333; G02F1/1345; H; H05; H05K; H05K3/00; H05K3/22; H05K3/24; C03C2217/00; C03C2217/20; C03C2217/25; C03C2217/251; C03C2217/253; C03C2217/268; C03C2217/27; C03C2218/00; C03C2218/10; C03C2218/15; C03C2218/151; C03C2218/154; C09; C09K; C09K2323/00; C09K2323/04; H05K2201/00; H05K2201/03; H05K2201/032; H05K2201/0326; H05K3/245; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49147; Y10T29/49149; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24917
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
65 words
A method of fabricating an electrical element comprising the steps of choosing a substrate selected from the group consisting of glass and a synthetic resin; bonding a contact pad to said substrate, said contact pad being formed by a layer which is overall an alloy consisting essentially of copper and manganese only; and soldering an electrical connector directly to the alloy forming said contact pad.
Claim 2
Independent Claim
65 words
A method of fabricating an electrical element comprising the steps of choosing a substrate selected from the group consisting of glass and a synthetic resin; bonding a contact pad to said substrate, said contact pad being formed by a layer which is overall an alloy consisting essentially of copper and manganese only; and soldering an electrical connector directly to the alloy forming said contact pad.
Claim 3
Dependent Claim
22 words
A method as claimed in claim 1 in which said substrate is glass, said glass being part of a liquid crystal cell.
Claim 4
Dependent Claim
32 words
A method as claimed in claim 1 which comprises the further step of forming a base adhesion layer on said substrate, said contact pad being then formed on said base adhesion layer.
Claim 5
Dependent Claim
23 words
A method as claimed in claim 3 wherein said base adhesion layer is selected from the group consisting of chromium and NICHROME IV.
Claim 6
Dependent Claim
17 words
A method as claimed in claim 1 wherein said contact pad is vacuum deposited onto said substrate.
Claim 7
Dependent Claim
33 words
A method as claimed in claim 5 wherein the source of manganese and copper in said contact pad is an alloy thereof having a manganese concentration of from 10 to 90 weight percent.
Claim 8
Dependent Claim
17 words
A method as claimed in claim 1 wherein said contact pad is screen printed onto said substrate.
Claim 9
Dependent Claim
33 words
A method as claimed in claim 7 wherein the source of manganese and copper in said contact pad is an alloy thereof having a maganese concentration of from 10 to 90 weight percent.
Claim 10
Dependent Claim
33 words
A method as claimed in claim 1 wherein the source of manganese and copper in said contact pad is an alloy thereof having a manganese concentration of more than about 20 weight percent.
Claim 11
Dependent Claim
48 words
A method as claimed in claim 1 wherein the step of bonding said contact pad to said substrate is performed by evaporating said alloy through a mask, whereby said contact pad is given a desired shape and said alloy is bonded only to selected areas of said subtrate.
Claim 12
Dependent Claim
25 words
A method as claimed in claim 1 wherein the alloy forming said contact pad contains approximately 50 weight percent manganese and 50 weight percent copper.
Claim 13
Dependent Claim
27 words
A method as claimed in claim 1 wherein the step of bonding a contact pad to a substrate is carried out at the lowest possible firing temperature.
Claim 14
Dependent Claim
96 words
A method as claimed in claim 1 wherein the step of bonding said contact pad to said substrate includes preparation of a paste of finely divided copper/manganese alloy and suspending it in a mixture of metal oxides, and then firing said suspension to (a) fuse said metal oxides to form a glass which wets the surface of said substrate and (b) sinter the particles of said alloy to produce a continuous conducting film, the temperature at which said firing is carried out depending upon the compositions of said metal oxides and being as low as possible.
Claim 15
Dependent Claim
38 words
A method as claimed in claim 13 wherein said metal oxides comprise a frit consisting essentially of lead oxide, boron oxide, silicon oxide and bismuth oxide, and wherein said firing is carried out at the lowest possible temperature.
Claim 16
Dependent Claim
57 words
An electrical element comprising a substrate selected from the group consisting of glass and a synthetic resin; a contact pad bonded to said substrate, said contact pad being formed by a layer which is overall an alloy consisting essentially of copper and manganese only; and an electrical connector soldered directly to the alloy forming said contact pad.
Claim 17
Dependent Claim
57 words
An electrical element comprising a substrate selected from the group consisting of glass and a synthetic resin; a contact pad bonded to said substrate, said contact pad being formed by a layer which is overall an alloy consisting essentially of copper and manganese only; and an electrical connector soldered directly to the alloy forming said contact pad.
Claim 18
Dependent Claim
22 words
An electrical element as claimed in claim 15 wherein said substrate is glass, said glass being part of a liquid crystal cell.
Claim 19
Dependent Claim
23 words
An electrical element as claimed in claim 15 which further comprises a base adhesion layer interposed between said substrate and said contact pad.
Claim 20
Dependent Claim
24 words
An electrical element as claimed in claim 17 wherein said base adhesion layer is selected from the group consisting of chromium and NICHROME IV.
Claim 21
Dependent Claim
22 words
An electrical element as claimed in claim 15 wherein said alloy has a manganese concentration of from 10 to 90 weight percent.
Claim 22
Dependent Claim
22 words
An electrical element as claimed in claim 15 wherein said alloy contains approximately 50 weight percent manganese and 50 weight percent copper.
References Cited (Backward Citations)
US3928658A
Cited
GB1579667A
Cited
US3922385A
Cited
US4229631A
Cited
US4436559A
Cited
US4409079A
Cited
GB2131831A
Cited
US4540970A
Cited
GB2139248A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-01-11 | 1991-07-13 | 1992-01-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-01-11 | 1995-07-13 | 1996-01-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-01-11 | 1999-07-13 | 2000-01-12 | $7700.00 | Window Closed / Lapsed |