US4409079A — Method of metallizing sintered ceramics

Claim 1

Independent Claim 107 words

A method for metallizing a sintered ceramic containing a silicon compound which is reactable with manganese at a temperature lower than the melting point of manganese, which comprises forming a manganese-containing metal layer on a desired surface of the ceramic and heating the metal layer to a temperature lower than the melting point of manganese to effect the metallization reaction between silicon atoms of the silicon compound and manganese atoms, wherein prior to the reaction the metal layer is brought into an intimate contact with the surface of the ceramic in a manner that there is substantially no minute gap between the metal layer and the ceramic.

Claim 2

Independent Claim 107 words

A method for metallizing a sintered ceramic containing a silicon compound which is reactable with manganese at a temperature lower than the melting point of manganese, which comprises forming a manganese-containing metal layer on a desired surface of the ceramic and heating the metal layer to a temperature lower than the melting point of manganese to effect the metallization reaction between silicon atoms of the silicon compound and manganese atoms, wherein prior to the reaction the metal layer is brought into an intimate contact with the surface of the ceramic in a manner that there is substantially no minute gap between the metal layer and the ceramic.

Claim 3

Dependent Claim 46 words

A method according to claim 1, wherein the metal layer is a film of a member selected from the group consisting of manganese, manganese-copper alloy, manganese-nickel alloy, manganese-titanium alloy and mixtures thereof, the film being formed by vacuum evaporation, sputtering or plasma spraying on the ceramic.

Claim 4

Dependent Claim 43 words

A method according to claim 1, wherein the metal layer is a melt of an alloy selected from the group consisting of manganese-copper, manganese-nickel and manganese-titanium, the metal layer being pressured to the surface of the ceramic by means of another solid member.

Claim 5

Dependent Claim 23 words

A method according to claim 3, wherein the metallization reaction takes place substantially at the same time of the formation of the melt.

Claim 6

Dependent Claim 53 words

A method according to claim 2 or 3, wherein the manganese alloy is selected from the group consisting of a manganese alloy containing 25 by 45% by weight of copper, a manganese alloy containing 50 to 70% by weight of nickel and a manganese alloy containing 42 to 43% by weight of titanium.

Claim 7

Independent Claim 101 words

A method metallizing sintered ceramics comprising the step of coating a desired surface of a sintered silicon carbide ceramic having a surface roughness of at most 5 μm with a paste, which comprises manganese powder dispersed in a dispersant, said manganese powder having a particle size smaller than the surface roughness, the step of removing the dispersant from said paste and forming a metal layer on the ceramic surface, and the step of heating the resultant structure to a temperature lower than the melting point of manganese for a time sufficient to effect a reaction between manganese atoms and silicon carbide.

Claim 8

Independent Claim 101 words

A method metallizing sintered ceramics comprising the step of coating a desired surface of a sintered silicon carbide ceramic having a surface roughness of at most 5 μm with a paste, which comprises manganese powder dispersed in a dispersant, said manganese powder having a particle size smaller than the surface roughness, the step of removing the dispersant from said paste and forming a metal layer on the ceramic surface, and the step of heating the resultant structure to a temperature lower than the melting point of manganese for a time sufficient to effect a reaction between manganese atoms and silicon carbide.

Claim 9

Dependent Claim 32 words

A method of metallizing sintered ceramics as defined in claim 6, wherein said paste contains at least one member selected from the group consisting of copper powder, nickel powder and titanium powder.

Claim 10

Independent Claim 127 words

A method of metallizing sintered ceramics comprising the step of placing a foil on a desired surface of a sintered silicon carbide ceramic, said foil being made of an alloy which contains 25 to 45% of manganese, the balance being copper, an alloy which contains 50 to 70% of manganese, the balance being nickel, or an alloy which contains 42 to 43% of manganese, the balance being titanium; and the step of heating said foil to a temperature of at least the melting point of said alloy, but lower than the melting point of manganese, under application of a pressure of at least 0.01 kg/mm 2 to melt said foil to form a liquefied metal layer and to cause a reaction between silicon carbide and manganese atoms.

Claim 11

Independent Claim 127 words

A method of metallizing sintered ceramics comprising the step of placing a foil on a desired surface of a sintered silicon carbide ceramic, said foil being made of an alloy which contains 25 to 45% of manganese, the balance being copper, an alloy which contains 50 to 70% of manganese, the balance being nickel, or an alloy which contains 42 to 43% of manganese, the balance being titanium; and the step of heating said foil to a temperature of at least the melting point of said alloy, but lower than the melting point of manganese, under application of a pressure of at least 0.01 kg/mm 2 to melt said foil to form a liquefied metal layer and to cause a reaction between silicon carbide and manganese atoms.

Claim 12

Independent Claim 41 words

A method of metallizing sintered ceramics as defined in any one of claims 6 to 8, wherein a metal material to be bonded is placed on said metal layer, and the resultant structure is heated under pressure to cause the reaction.

Claim 13

Independent Claim 75 words

A method of metallizing sintered ceramics comprising the step of forming a metal layer of manganese or a mixed metal layer of manganese and another metal on a desired surface of sintered aluminum oxide by vacuum evaporation or sputtering, and the step of heating the resultant structure to a temperature lower than the melting point of manganese for a time sufficient to perform a reaction between manganese atoms and silicon oxide in the alumina ceramic.

Claim 14

Independent Claim 75 words

A method of metallizing sintered ceramics comprising the step of forming a metal layer of manganese or a mixed metal layer of manganese and another metal on a desired surface of sintered aluminum oxide by vacuum evaporation or sputtering, and the step of heating the resultant structure to a temperature lower than the melting point of manganese for a time sufficient to perform a reaction between manganese atoms and silicon oxide in the alumina ceramic.

Claim 15

Independent Claim 105 words

A method of metallizing sintered ceramics comprising the step of coating a desired surface of a sintered alumina ceramic having a surface roughness of at most 5 μm with a paste which comprises manganese powder dispersed in a dispersant, said manganese powder having a particle size smaller than the surface roughness, the step of removing the dispersant of said paste and forming a metal layer on the alumina surface, and the step of heating the resultant structure to a temperature lower than the melting point of manganese for a time sufficient to effect a reaction between manganese atoms and silicon oxide in the alumina ceramic.

Claim 16

Independent Claim 105 words

A method of metallizing sintered ceramics comprising the step of coating a desired surface of a sintered alumina ceramic having a surface roughness of at most 5 μm with a paste which comprises manganese powder dispersed in a dispersant, said manganese powder having a particle size smaller than the surface roughness, the step of removing the dispersant of said paste and forming a metal layer on the alumina surface, and the step of heating the resultant structure to a temperature lower than the melting point of manganese for a time sufficient to effect a reaction between manganese atoms and silicon oxide in the alumina ceramic.

Claim 17

Dependent Claim 32 words

A method of metallizing sintered ceramics as defined in claim 11, wherein said paste contains at least one member selected from the group consisting of copper powder, nickel powder and titanium powder.

Claim 18

Independent Claim 138 words

A method of metallizing sintered ceramics comprising the step of placing a foil on a desired surface of a sintered alumina ceramic containing silicon oxide, said foil being made of an alloy which contains 25 to 40% of manganese, the balance being copper, an alloy which contains 50 to 70% of manganese, the balance being nickel, or an alloy which contains 42 to 43% of manganese, the balance being titanium; and the step of heating said foil to a temperature of at least the melting point of said alloy but lower than the melting point of manganese under application of a pressure of at least 0.01 kg/mm 2 to melt said foil to form a liquefied metal layer and to cause a reaction betwen the silicon oxide in the alumina ceramic and manganese atoms in the manganese alloy.

Claim 19

Independent Claim 138 words

A method of metallizing sintered ceramics comprising the step of placing a foil on a desired surface of a sintered alumina ceramic containing silicon oxide, said foil being made of an alloy which contains 25 to 40% of manganese, the balance being copper, an alloy which contains 50 to 70% of manganese, the balance being nickel, or an alloy which contains 42 to 43% of manganese, the balance being titanium; and the step of heating said foil to a temperature of at least the melting point of said alloy but lower than the melting point of manganese under application of a pressure of at least 0.01 kg/mm 2 to melt said foil to form a liquefied metal layer and to cause a reaction betwen the silicon oxide in the alumina ceramic and manganese atoms in the manganese alloy.

Claim 20

Independent Claim 53 words

A method of metallizing sintered ceramics as defined in any one of claims 10 to 13, wherein a metal material to be bonded is placed on said metal layer, and the resultant structure is heated to a temperature lower than the melting point of the metal material under pressure to cause the reaction.

Claim 21

Dependent Claim 24 words

A method of metallizing sintered ceramics according to claim 1, wherein the silicon compound contained in the sintered ceramic is SiC or silicon oxide.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1986-10-10	1987-04-11	1987-10-11	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1990-10-10	1991-04-11	1991-10-11	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	1994-10-10	1995-04-11	1995-10-11	$7700.00	Window Closed / Lapsed

Method of metallizing sintered ceramics

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag