EDM wire electrode
Assignee: General Electric Co
•
Filing: 1986-07-24
•
Granted: 1988-01-05
•
Expires: 2006-07-24
Abstract
Abstract An improved electrical discharge machining electrode permitting increased cutting speed of the metal workpiece being machined and which improves the operation of the electrical discharge machining equipment in other respects. The improvement is atrributable to an adherent carbon surface coating deposited on an electrically conductive metal wire length which serves to transfer energy efficiently to the workpiece from the spark discharge as well as enhance the flushing of materials removed by said discharge during the machining operation. The method and apparatus for employment of said improved electrode is also described.
Inventors
- 👤 D. S. Tomalin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 23:33
CPC Classifications
B; B23; B23H; B23H7/00; B23H7/02; B23H7/08
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
45 words
An electrical discharge machining electrode which comprises a composite member having an electrically conductive entirely metal wire length of ferrous alloy metal for its core and with said core being clad with a layer of copper whose outer surface is oxidized and coated with graphite.
Claim 2
Dependent Claim
45 words
An electrical discharge machining electrode which comprises a composite member having an electrically conductive entirely metal wire length of ferrous alloy metal for its core and with said core being clad with a layer of copper whose outer surface is oxidized and coated with graphite.
Claim 3
Dependent Claim
16 words
The electrode of claim 1 wherein said oxidized outer surface of said copper comprises cuprous oxide.
Claim 4
Dependent Claim
69 words
An electrical discharge machining electrode which comprises a composite member having an electrically conductive entirely metal wire exhibiting both a relatively high mechanical strength and a relatively high melting point for its core, a metal containing innerlayer exhibiting a lower melting point bonded to the metal core whose outer surface is oxidized, and an adherent preformed solid carbon surface coating bonded to said oxidized surface of said inner layer.
Claim 5
Dependent Claim
69 words
An electrical discharge machining electrode which comprises a composite member having an electrically conductive entirely metal wire exhibiting both a relatively high mechanical strength and a relatively high melting point for its core, a metal containing innerlayer exhibiting a lower melting point bonded to the metal core whose outer surface is oxidized, and an adherent preformed solid carbon surface coating bonded to said oxidized surface of said inner layer.
Claim 6
Dependent Claim
149 words
An electrical discharge machining process which comprises moving an electrically charged wire electrode member in close proximity to a metal workpiece so as to cause a spark discharge therebetween, said wire electrode member having a composite construction comprising an electrically conductive entirely metal wire length exhibiting both a relatively high mechanical strength and a relatively high melting point for its core, a metal innerlayer exhibiting a lower melting point bonded to said metal core whose outer surface is oxidized and an adherent preformed solid carbon surface deposit or coating bonded to said oxidized surface of said inner layer, contacting the gap space between said workpiece surface and the moving wire electrode member with a moving dielectric liquid, removing metal from the workpiece and carbon from the wire electrode member with said spark discharge, and displacing the removed metal and carbon from the gap space in the moving dielectric fluid.
Claim 7
Dependent Claim
149 words
An electrical discharge machining process which comprises moving an electrically charged wire electrode member in close proximity to a metal workpiece so as to cause a spark discharge therebetween, said wire electrode member having a composite construction comprising an electrically conductive entirely metal wire length exhibiting both a relatively high mechanical strength and a relatively high melting point for its core, a metal innerlayer exhibiting a lower melting point bonded to said metal core whose outer surface is oxidized and an adherent preformed solid carbon surface deposit or coating bonded to said oxidized surface of said inner layer, contacting the gap space between said workpiece surface and the moving wire electrode member with a moving dielectric liquid, removing metal from the workpiece and carbon from the wire electrode member with said spark discharge, and displacing the removed metal and carbon from the gap space in the moving dielectric fluid.
Claim 8
Dependent Claim
13 words
A process as in claim 4 wherein said surface carbon coating is graphite.
Claim 9
Dependent Claim
20 words
A process as in claim 5 wherein the spark discharge causes removal of both carbon and some innerlayer by volatilization.
Claim 10
Dependent Claim
122 words
An electrical discharge machining process which comprises moving an electrically charged wire electrode member in close proximity to a metal workpiece so as to cause a spark discharge therebetween, said wire electrode member comprising a composite member having an electrically conductive entirely metal wire length of ferrous alloy metal for its core and with said core being clad with a layer of copper whose outer surface is oxidized and coated with graphite, contacting the space between said workpiece surface and the moving wire electrode member with a moving dielectric liquid, removing metal from the workpiece and carbon from the wire electrode member with said spark discharge, and displacing the removed metal end carbon from the gap space with the moving dielectric fluid.
Claim 11
Dependent Claim
122 words
An electrical discharge machining process which comprises moving an electrically charged wire electrode member in close proximity to a metal workpiece so as to cause a spark discharge therebetween, said wire electrode member comprising a composite member having an electrically conductive entirely metal wire length of ferrous alloy metal for its core and with said core being clad with a layer of copper whose outer surface is oxidized and coated with graphite, contacting the space between said workpiece surface and the moving wire electrode member with a moving dielectric liquid, removing metal from the workpiece and carbon from the wire electrode member with said spark discharge, and displacing the removed metal end carbon from the gap space with the moving dielectric fluid.
Claim 12
Dependent Claim
16 words
The process of claim 7 wherein said oxide coating on said copper layer comprises cuprous oxide.
Claim 13
Dependent Claim
115 words
An electrical discharge machining process which comprises moving an electrically charged wire electrode member in close proximity to a metal workpiece so as to cause a spark discharge therebetween, said wire electrode member comprising a wire having molybdenum or alloy thereof for its core, said molybdenum core containing an adherent coating of molybdenum oxide which, in turn, is coated with a preformed coating of carbon, contacting the space between said workpiece surface and the moving wire electrode member with a moving dielectric liquid, removing metal from the workpiece and carbon from the wire electrode member with said spark discharge, and displacing the removed metal end carbon from the gap space with the moving dielectric fluid.
Claim 14
Dependent Claim
115 words
An electrical discharge machining process which comprises moving an electrically charged wire electrode member in close proximity to a metal workpiece so as to cause a spark discharge therebetween, said wire electrode member comprising a wire having molybdenum or alloy thereof for its core, said molybdenum core containing an adherent coating of molybdenum oxide which, in turn, is coated with a preformed coating of carbon, contacting the space between said workpiece surface and the moving wire electrode member with a moving dielectric liquid, removing metal from the workpiece and carbon from the wire electrode member with said spark discharge, and displacing the removed metal end carbon from the gap space with the moving dielectric fluid.
Claim 15
Dependent Claim
11 words
The process of claim 9 wherein said carbon coating comprises graphite.
References Cited (Backward Citations)
US2526423A
Cited
US2906853A
Cited
US3600981A
Cited
GB1408801A
Cited
JPS5322930A
Cited
US4287404B1
Cited
US4287404A
Cited
US4341939A
Cited
US4422918A
Cited
US4392042A
Cited
CH645831A5
Cited
JPS5894925A
Cited
SU1060383A1
Cited
JPS6067026A
Cited
US4686153A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-01-04 | 1991-07-06 | 1992-01-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-01-04 | 1995-07-06 | 1996-01-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-01-04 | 1999-07-06 | 2000-01-05 | $7700.00 | Window Closed / Lapsed |