Electrode wire for use in electric discharge machining and process for preparing same
Assignee: Fujikura Ltd
•
Filing: 1985-12-04
•
Granted: 1987-08-11
•
Expires: 2005-12-04
Abstract
Abstract An electrode wire for wire electric discharge machining a workpiece at high speed and high accuracy and a process for preparing the same are provided. The electrode wire comprises a core wire made of a copper clad steel wire, 10 to 70% of the sectional area of the copper clad steel wire being occupied by copper, and a copper-zinc alloy layer covering the core wire. The copper-zinc alloy layer is prepared by coating the core wire with zinc by electroplating or hot galvanizing, followed by heating to disperse copper in the zinc layer to convert the same into a copper-zinc alloy layer wherein the concentration of zinc is increased gradually along the radially outward direction. The preferable thickness of the copper-zinc alloy layer ranges from 0.1 to 15 microns and the average concentration of zinc in the copper-zinc alloy layer is preferably less than 50% by weight but not less than 10% by weight.
Inventors
- 👤 Haruo Tominaga
- 👤 Teruyuki Takayama
- 👤 Yoshio Ogura
- 👤 Tetsuo Yamaguchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 01:11
CPC Classifications
B; B23; B23H; B23H7/00; B23H7/02; B23H7/08; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/9335; Y10S428/941; Y10T; Y10T428/00; Y10T428/12; Y10T428/12458; Y10T428/12493; Y10T428/12771; Y10T428/12785; Y10T428/12792; Y10T428/12861; Y10T428/12903; Y10T428/1291; Y10T428/12917; Y10T428/12924
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
131 words
In an electrode wire for use in machining a workpiece by means of electric spark discharge, said electrode wire comprising: a core wire including steel wire having a copper cladding, said copper cladding having a cross-sectional area approximately 10 to 70 percent of the cross-sectional area of said core wire; a copper-zinc alloy layer over said core wire, said alloy layer having a thickness of from 0.1 to 15 microns, and an average zinc concentration being less than 50% by weight of the alloy layer weight, but not less than 10% by weight of the alloy layer weight, the concentration of zinc in said copper-zinc alloy layer increasing gradually in a radially outward direction to result in an alloy layer portion having a zinc concentration from 40% to 50% by weight.
Claim 2
Dependent Claim
131 words
In an electrode wire for use in machining a workpiece by means of electric spark discharge, said electrode wire comprising: a core wire including steel wire having a copper cladding, said copper cladding having a cross-sectional area approximately 10 to 70 percent of the cross-sectional area of said core wire; a copper-zinc alloy layer over said core wire, said alloy layer having a thickness of from 0.1 to 15 microns, and an average zinc concentration being less than 50% by weight of the alloy layer weight, but not less than 10% by weight of the alloy layer weight, the concentration of zinc in said copper-zinc alloy layer increasing gradually in a radially outward direction to result in an alloy layer portion having a zinc concentration from 40% to 50% by weight.
Claim 3
Dependent Claim
109 words
In an electrode wire for use in wire electric discharting machining a workpiece by means of electric spark discharge, said wire comprising an inner core portion of steel wire, an intermediate copper cladding, an outer copper-zinc alloy layer, said outer layer having a thickness of from 0.1 to 15 microns, said intermediate layer comprising 10 to 70% of the sectional area of said combined inner core portion and said intermediate layer, said outer layer having a concentration of zinc which radially increases gradually the average concentration of zinc in said outer layer being less than 50% by weight but not less than 10% by weight of said outer layer.
Claim 4
Dependent Claim
109 words
In an electrode wire for use in wire electric discharting machining a workpiece by means of electric spark discharge, said wire comprising an inner core portion of steel wire, an intermediate copper cladding, an outer copper-zinc alloy layer, said outer layer having a thickness of from 0.1 to 15 microns, said intermediate layer comprising 10 to 70% of the sectional area of said combined inner core portion and said intermediate layer, said outer layer having a concentration of zinc which radially increases gradually the average concentration of zinc in said outer layer being less than 50% by weight but not less than 10% by weight of said outer layer.
Claim 5
Dependent Claim
170 words
A process for preparing an electrode wire for use in machining a workpiece by means of electric spark discharge, comprising the steps of: (a) preparing a core wire of copper clad steel wire having 10 to 70% of the cross-sectional area of said core wire being copper; (b) coating said core wire with a zinc layer by electroplating; (c) elongating said core wire coated with said zinc layer; and (d) heating said zinc coated core wire to disperse copper into said zinc layer, thereby converting said zinc layer into a copper-zinc alloy layer having a thickness of from about 0.1 to about 15 microns and an average concentration of zinc of less than 50% but not less than 10% by weight, heating said zinc coated core wire to gradually increase the concentration of zinc within said copper-zinc alloy layer in a radially outward direction thereby forming an integral layer in said copper-zinc alloy layer having a zinc concentration from about 40% to about 50% by weight of said integral layer.
Claim 6
Dependent Claim
170 words
A process for preparing an electrode wire for use in machining a workpiece by means of electric spark discharge, comprising the steps of: (a) preparing a core wire of copper clad steel wire having 10 to 70% of the cross-sectional area of said core wire being copper; (b) coating said core wire with a zinc layer by electroplating; (c) elongating said core wire coated with said zinc layer; and (d) heating said zinc coated core wire to disperse copper into said zinc layer, thereby converting said zinc layer into a copper-zinc alloy layer having a thickness of from about 0.1 to about 15 microns and an average concentration of zinc of less than 50% but not less than 10% by weight, heating said zinc coated core wire to gradually increase the concentration of zinc within said copper-zinc alloy layer in a radially outward direction thereby forming an integral layer in said copper-zinc alloy layer having a zinc concentration from about 40% to about 50% by weight of said integral layer.
Claim 7
Dependent Claim
177 words
A process for preparing an electrode wire for use in machining a workpiece by means of electric spark discharge, comprising the steps of: (a) preparing a core wire of a copper clad steel wire having 10 to 70% of the cross-sectional area of said core wire being copper; (b) coating said core wire with a zinc layer by electroplating; (c) heating said zinc coated core wire to disperse copper into said zinc layer, thereby converting said zinc layer into a copper-zinc alloy layer having an average concentration of zinc of less than 50% but not less than 10% by weight, heating said coated core wire to gradually increase the concentration of zinc within said copper-zinc alloy layer in a radially outward direction thereby forming an integral layer in said copper-zinc alloy layer having a zinc concentration from about 40% to about 50% by weight of said integral layer; and (d) elongating said core wire coated with said copper-zinc alloy layer so that the thickness of said copper-zinc alloy layer is from about 0.1 to about 15 microns.
Claim 8
Dependent Claim
177 words
A process for preparing an electrode wire for use in machining a workpiece by means of electric spark discharge, comprising the steps of: (a) preparing a core wire of a copper clad steel wire having 10 to 70% of the cross-sectional area of said core wire being copper; (b) coating said core wire with a zinc layer by electroplating; (c) heating said zinc coated core wire to disperse copper into said zinc layer, thereby converting said zinc layer into a copper-zinc alloy layer having an average concentration of zinc of less than 50% but not less than 10% by weight, heating said coated core wire to gradually increase the concentration of zinc within said copper-zinc alloy layer in a radially outward direction thereby forming an integral layer in said copper-zinc alloy layer having a zinc concentration from about 40% to about 50% by weight of said integral layer; and (d) elongating said core wire coated with said copper-zinc alloy layer so that the thickness of said copper-zinc alloy layer is from about 0.1 to about 15 microns.
Claim 9
Dependent Claim
194 words
A process for preparing an electrode wire for use in machining a workpiece by means of electric spark discharge, comprising the steps of: (a) preparing a core wire of copper clad steel wire wherein a 10 to 70% of cross-sectional area thereof is copper; (b) dipping said core wire in a molten zinc bath thereby forming a first copper-zinc alloy layer covering said core wire and a zinc layer on said first copper-zinc alloy layer; (c) elongating said coated core wire; and (d) heating said coated and elongated core wire to disperse copper into said first copper-zinc and zinc layers, thereby converting said zinc layer into a second copper-zinc alloy layer and increasing the zinc concentration in said first copper-zinc alloy layer, whereby the total thickness of said first and second copper-zinc alloy layers is from about 0.1 to about 15 microns, the concentration of zinc within said first and second copper-zinc alloys is gradually increased in a radially outward direction and an integral high zinc concentration is formed in said layer having a first and second copper-zinc alloy layers having a zinc concentration from 40% to 50% by weight of said integral layer.
Claim 10
Dependent Claim
194 words
A process for preparing an electrode wire for use in machining a workpiece by means of electric spark discharge, comprising the steps of: (a) preparing a core wire of copper clad steel wire wherein a 10 to 70% of cross-sectional area thereof is copper; (b) dipping said core wire in a molten zinc bath thereby forming a first copper-zinc alloy layer covering said core wire and a zinc layer on said first copper-zinc alloy layer; (c) elongating said coated core wire; and (d) heating said coated and elongated core wire to disperse copper into said first copper-zinc and zinc layers, thereby converting said zinc layer into a second copper-zinc alloy layer and increasing the zinc concentration in said first copper-zinc alloy layer, whereby the total thickness of said first and second copper-zinc alloy layers is from about 0.1 to about 15 microns, the concentration of zinc within said first and second copper-zinc alloys is gradually increased in a radially outward direction and an integral high zinc concentration is formed in said layer having a first and second copper-zinc alloy layers having a zinc concentration from 40% to 50% by weight of said integral layer.
Claim 11
Dependent Claim
199 words
A process for preparing an electrode wire for use in machining a workpiece by means of electric spark discharge, comprising the steps of: (a) preparing a core wire of a copper clad steel wire having 10 to 70% of the cross-sectional area of said core wire being copper; (b) dipping said core wire in a molten zinc bath thereby forming a first copper-zinc alloy layer on said core wire and a zinc layer on said first copper-zinc alloy layer; (c) heating said coated core wire to disperse copper into said first copper-zinc and zinc layers and thereby converting said zinc layer into a second copper-zinc alloy layer and increasing the zinc concentration in said first copper-zinc alloy layer, whereby the concentration of zinc within said first and second copper-zinc alloy layers is gradually increased in a radially outward direction and said first and second copper-zinc alloy layers include an integral layer having a zinc concentration from about 40% to about 50% by weight of said integral layer; and (d) elongating said coated core wire so that the total thickness of said first and second copper-zinc alloy layers is within the range of from about 0.1 to about 15 microns.
Claim 12
Dependent Claim
199 words
A process for preparing an electrode wire for use in machining a workpiece by means of electric spark discharge, comprising the steps of: (a) preparing a core wire of a copper clad steel wire having 10 to 70% of the cross-sectional area of said core wire being copper; (b) dipping said core wire in a molten zinc bath thereby forming a first copper-zinc alloy layer on said core wire and a zinc layer on said first copper-zinc alloy layer; (c) heating said coated core wire to disperse copper into said first copper-zinc and zinc layers and thereby converting said zinc layer into a second copper-zinc alloy layer and increasing the zinc concentration in said first copper-zinc alloy layer, whereby the concentration of zinc within said first and second copper-zinc alloy layers is gradually increased in a radially outward direction and said first and second copper-zinc alloy layers include an integral layer having a zinc concentration from about 40% to about 50% by weight of said integral layer; and (d) elongating said coated core wire so that the total thickness of said first and second copper-zinc alloy layers is within the range of from about 0.1 to about 15 microns.
References Cited (Backward Citations)
US2392456A
Cited
US2378458A
Cited
US2918722A
Cited
SU476125A1
Cited
US4424432A
Cited
US4287404A
Cited
US4287404B1
Cited
US4304113A
Cited
US4341939A
Cited
JPS5662730A
Cited
JPS56126528A
Cited
GB2069396A
Cited
CH645831A5
Cited
JPS59736A
Cited
JPS59129626A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-10 | 1991-02-09 | 1991-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-10 | 1995-02-09 | 1995-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-10 | 1999-02-09 | 1999-08-11 | $7700.00 | Window Closed / Lapsed |