Steel bonded dense silicon nitride compositions and method for their fabrication
Assignee: United States Department of Energy
•
Filing: 1986-11-20
•
Granted: 1987-11-03
•
Expires: 2006-11-20
Abstract
Abstract A two-stage bonding technique for bonding high density silicon nitride and other ceramic materials to stainless steel and other hard metals, and multilayered ceramic-metal composites prepared by the technique are disclosed. The technique involves initially slurry coating a surface of the ceramic material at about 1500 DEG C. in a vacuum with a refractory material and the stainless steel is then pressure bonded to the metallic coated surface by brazing it with nickel-copper-silver or nickel-copper-manganese alloys at a temperature in the range of about 850 DEG to 950 DEG C. in a vacuum. The two-stage bonding technique minimizes the temperature-expansion mismatch between the dissimilar materials.
Inventors
- 👤 Richard L. Landingham
- 👤 Thomas E. Shell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 17:51
CPC Classifications
C; C04; C04B; C04B37/00; C04B37/02; C04B37/023; C04B37/026; B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/32; B23K35/327; C04B37/003; C04B37/006; C04B2237/00; C04B2237/02; C04B2237/04; C04B2237/09; C04B2237/12; C04B2237/123; C04B2237/30; C04B2237/32; C04B2237/36; C04B2237/368; C04B2237/40; C04B2237/403; C04B2237/405; C04B2237/406; C04B2237/407; C04B2237/408; C04B2237/50; C04B2237/52; C04B2237/70; C04B2237/704; C04B2237/706; C04B2237/72
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
103 words
A method of fabricating a multilayered ceramic-metal composite comprising: (a) polishing a surface of a dense ceramic material to enhance wetting and reaction with molten reactive material; (b) applying a thin slurry coating of a fine powder mixture of a refractory material comprising a mixture of powdered nickel and molybdenum silicide and bonding it to said surface of said ceramic material; (c) grinding said layer of refractory material to uniform thickness; (d) brazing a surface of said layer of refractory material with a metal alloy at elevated temperatures; and (e) pressure bonding a metal piece to said metal alloy to form the composite.
Claim 2
Independent Claim
103 words
A method of fabricating a multilayered ceramic-metal composite comprising: (a) polishing a surface of a dense ceramic material to enhance wetting and reaction with molten reactive material; (b) applying a thin slurry coating of a fine powder mixture of a refractory material comprising a mixture of powdered nickel and molybdenum silicide and bonding it to said surface of said ceramic material; (c) grinding said layer of refractory material to uniform thickness; (d) brazing a surface of said layer of refractory material with a metal alloy at elevated temperatures; and (e) pressure bonding a metal piece to said metal alloy to form the composite.
Claim 3
Dependent Claim
28 words
The method of claim 1, wherein said refractory material is melted on to said surface of said ceramic material at a temperature of about 1500° C. in vacuum.
Claim 4
Dependent Claim
21 words
The method of claim 2, wherein said brazing alloy is selected from the group consisting of nickel-copper-siler, nickel-copper-manganese, nickel-copper-gold, nickel-copper-palladium alloys.
Claim 5
Dependent Claim
13 words
The method of claim 3, wherein said brazing alloy is nickel-copper-silver or nickel-copper-manganese.
Claim 6
Dependent Claim
23 words
The method of claim 4, wherein said brazing is carried out at a temperature in the range of about 850° to 950° C.
Claim 7
Dependent Claim
28 words
The method of claim 5, wherein the metal piece is selected from the group consisting of iron, steel, stainless steel, nickel, tungsten, copper, brass, platinum, titanium, and zirconium.
Claim 8
Dependent Claim
12 words
The method of claim 6, wherein the metal piece is stainless steel.
Claim 9
Dependent Claim
12 words
The method of claim 7, wherein said stainless steel is Greek Ascaloy.
Claim 10
Independent Claim
110 words
A method of fabricating a multilayered ceramic-metal composite comprising: (a) polishing a surface of a dense, sintered silicon nitride material to enhance wetting; (b) slurry coating and bonding to said surface of said silicon nitride material, a layer of a refractory material comprising a mixture of powdered nickel and molydenum silicide; (c) grinding said layer of said refractory material to uniform thickness; (d) slurry coating and brazing said layer of said refractory material with a nickel-copper-silver or nickel-copper-manganese alloy at elevated temperatures; and (e) pressure bonding a stainless steel metal piece to said metal alloy in the temperature range above the melting point of said alloy, to form the composite.
Claim 11
Independent Claim
110 words
A method of fabricating a multilayered ceramic-metal composite comprising: (a) polishing a surface of a dense, sintered silicon nitride material to enhance wetting; (b) slurry coating and bonding to said surface of said silicon nitride material, a layer of a refractory material comprising a mixture of powdered nickel and molydenum silicide; (c) grinding said layer of said refractory material to uniform thickness; (d) slurry coating and brazing said layer of said refractory material with a nickel-copper-silver or nickel-copper-manganese alloy at elevated temperatures; and (e) pressure bonding a stainless steel metal piece to said metal alloy in the temperature range above the melting point of said alloy, to form the composite.
Claim 12
Dependent Claim
18 words
The method of claim 9, wherein said surface of a dense ceramic material is a plurality of surfaces.
Claim 13
Dependent Claim
27 words
The method of claim 9, wherein said refractory material is slurry coated on said silicon nitride surface at a temperature of about 1500° C. in a vacuum.
Claim 14
Dependent Claim
21 words
The method of claim 11, wherein said brazing is carried out in the temperature range of about 850° to 950° C.
Claim 15
Dependent Claim
12 words
The method of claim 12, wherein said stainless steel is Greek Ascaloy.
Claim 16
Dependent Claim
176 words
In a method for the fabrication of a ceramic-metal composite by (a) contacting as a bonding agent, a layer of molybdenum silicide with a portion of a silicon nitride substrate and with a portion of a refractory metal substrate; (b) heating the layer of molybdenum silicide to a temperature of between about 1000° C. to about 1300° C. and (c) simultaneously compressing said silicon nitride substrate and said refractory metal substrate with said layer of molybdenum silicide therebetween with a pressure of at least 4,350psi, the improvement comrising: (a) melt coating a portion of a silicon nitride substrate with a mixture of nickel and molybdenum silicide as the bonding agent at a temperature of about 1500° C.; (b) slurry coating a brazing alloy onto said silicon nitride substrate and brazing at a temperature in the range above the melting point of said alloy; and (c) compressing said silicon nitride substrate and said refractory metal substrate with said layer of said bonding agent therebetween with a pressure in the range of about 50 to about 1000 psi.
Claim 17
Dependent Claim
176 words
In a method for the fabrication of a ceramic-metal composite by (a) contacting as a bonding agent, a layer of molybdenum silicide with a portion of a silicon nitride substrate and with a portion of a refractory metal substrate; (b) heating the layer of molybdenum silicide to a temperature of between about 1000° C. to about 1300° C. and (c) simultaneously compressing said silicon nitride substrate and said refractory metal substrate with said layer of molybdenum silicide therebetween with a pressure of at least 4,350psi, the improvement comrising: (a) melt coating a portion of a silicon nitride substrate with a mixture of nickel and molybdenum silicide as the bonding agent at a temperature of about 1500° C.; (b) slurry coating a brazing alloy onto said silicon nitride substrate and brazing at a temperature in the range above the melting point of said alloy; and (c) compressing said silicon nitride substrate and said refractory metal substrate with said layer of said bonding agent therebetween with a pressure in the range of about 50 to about 1000 psi.
Claim 18
Dependent Claim
13 words
The improvement of claim 14, wherein said brazing alloy is nickel-copper-silver or nickel-copper-manganese.
Claim 19
Dependent Claim
12 words
The improvement of claim 15, wherein said refractory metal is stainless steel.
Claim 20
Dependent Claim
12 words
The improvement of claim 10, wherein said stainless steel is Greek Ascaloy.
References Cited (Backward Citations)
CA500750A
Cited
CA556614A
Cited
US2972808A
Cited
US3915369A
Cited
US4055451A
Cited
DE2534777A1
Cited
US4131459A
Cited
US4263353A
Cited
US4325647A
Cited
US4293619A
Cited
US4394170A
Cited
US4505418A
Cited
US4469658A
Cited
US4343865A
Cited
US4347089A
Cited
US4404262A
Cited
US4470537A
Cited
US4492737A
Cited
US4553472A
Cited
US4626451A
Cited
US4614689A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-11-02 | 1991-05-04 | 1991-11-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-11-02 | 1995-05-04 | 1995-11-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-11-02 | 1999-05-04 | 1999-11-03 | $7700.00 | Window Closed / Lapsed |