Composite metallic and non-metallic articles
Assignee: Rolls Royce PLC
•
Filing: 1983-03-04
•
Granted: 1985-01-08
•
Expires: 2003-03-04
Abstract
Abstract The invention is concerned with the problem of joining ceramic components to metal components. A composite ceramic-metal component is proposed, e.g. a rotor disc for a gas turbine engine (see FIG. 2), in which the main body of the component is made from a ceramic, e.g. Silicon Nitride, but the areas at which attachment is to be made to a metal component is formed from metal compacted onto the ceramic by a hot isostatic pressing process. The method of manufacture described is to form a ceramic core with holes appropriately positioned in it where a connection is to be made to another component, surround the core with a powdered metal, e.g. a Nickel-based superalloy, ensuring that the holes also fill with powder, compacting the powder by hot isostatic pressing, and then machining away unwanted metal.
Inventors
- 👤 Ralph I. Conolly
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 18:04
CPC Classifications
B; B22; B22F; B22F7/00; B22F7/06; B22F7/08; B23; B23P; B23P15/00; B23P15/006; F; F01; F01D; F01D5/00; F01D5/12; F01D5/28; F01D5/284; F05; F05D; F05D2200/00; F05D2200/20; F05D2200/26; F05D2200/261; Y; Y10; Y10S; Y10S29/00; Y10S29/031; Y10T; Y10T29/00; Y10T29/49; Y10T29/49316; Y10T29/4932; Y10T29/49336; Y10T29/49337; Y10T29/53; Y10T29/53657; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12049; Y10T428/12056
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
196 words
A method for manufacturing a composite component having a pre-formed body made from a base material chosen from the group consisting of a ceramic, a high temperature glass/ceramic composite and a carbon-in-carbon composite, and a metallic component bonded to a selected area on the pre-formed body, comprising the steps of: placing the pre-formed body in a peripherally walled can, with the pre-formed body spaced throughout substantially its entire extent, from the can wall, to define a space therebetween; filling the space between the pre-formed body and the can wall with a powdered metal, thereby completely surrounding the pre-formed body with the powdered metal; sealing and evacuating the can; applying hot isostatic pressure to the can to compact and sinter the metal powder and to bond the metal powder to the pre-formed body; removing the can from the exterior of the completely coated body; and removing the bonded metal powder from selected areas on the surface of the pre-formed body to expose areas of the base material and to leave the bonded metal powder at other areas, whereby the composite component can be directly connected to another metal component through a portion of the bonded metal powder.
Claim 2
Independent Claim
196 words
A method for manufacturing a composite component having a pre-formed body made from a base material chosen from the group consisting of a ceramic, a high temperature glass/ceramic composite and a carbon-in-carbon composite, and a metallic component bonded to a selected area on the pre-formed body, comprising the steps of: placing the pre-formed body in a peripherally walled can, with the pre-formed body spaced throughout substantially its entire extent, from the can wall, to define a space therebetween; filling the space between the pre-formed body and the can wall with a powdered metal, thereby completely surrounding the pre-formed body with the powdered metal; sealing and evacuating the can; applying hot isostatic pressure to the can to compact and sinter the metal powder and to bond the metal powder to the pre-formed body; removing the can from the exterior of the completely coated body; and removing the bonded metal powder from selected areas on the surface of the pre-formed body to expose areas of the base material and to leave the bonded metal powder at other areas, whereby the composite component can be directly connected to another metal component through a portion of the bonded metal powder.
Claim 3
Dependent Claim
21 words
The method of claim 1, wherein the can comprises a material chosen from the group consisting of glass, ceramic and metal.
Claim 4
Dependent Claim
19 words
The method of claim 1, wherein the applied temperature during hot isostatic pressing is in excess of 800° C.
Claim 5
Dependent Claim
14 words
The method of claim 1, wherein the applied pressure is limited to 25 ksi.
Claim 6
Dependent Claim
14 words
The method of claim 1, wherein the powdered metal is a nickel-based super alloy.
Claim 7
Dependent Claim
13 words
The method of claim 1, wherein the ceramic preformed body consists of SiN.
Claim 8
Dependent Claim
22 words
The method of claim 1, wherein the bonded metal powder is removed from the surface of the pre-formed body by chemical etching.
Claim 9
Dependent Claim
22 words
The method of claim 1, wherein the bonded metal powder is removed from the surface of the pre-formed body by electro-chemical machining.
Claim 10
Dependent Claim
29 words
The method of claim 1, wherein the pre-formed body is a non-continuous body and the powdered metal fills in the space between the non-continuous portions of the pre-formed body.
Claim 11
Dependent Claim
35 words
The method of claim 1, wherein a portion of the metal powder is pre-pressed into an intermediate form thereby imparting green strength and functions as a partial positioner of the pre-formed body within the can.
Claim 12
Dependent Claim
77 words
The method of claim 1, wherein the composite component comprises an integral hub portion and blade portion for a turbine wheel, whereby the method further comprises manufacturing a plurality of integral hub portions and blade portions and after removing the bonded metal powder from selected areas on the surface of the integral hub and blade portions, said other areas of the bonded metal powder are mechanically fixed to said another metal component to form a turbine wheel.
Claim 13
Dependent Claim
76 words
The method of claim 1, wherein the composite component comprises an integral blade portion and root portion for a rotor turbine, whereby the method further comprises manufacturing a plurality of integral blade and root portions and after removing the bonded metal powder from selected areas on the surface of the individual blade and root portions, said other areas of the bonded metal powder are mechanically fixed to said another metal component to form a rotor turbine.
Claim 14
Dependent Claim
32 words
The method of claim 1, wherein the composite component comprises a flame tube, whereby said other areas of the bonded metal powder comprise supporting ribs which effectively strengthen the pre-formed body portion.
Claim 15
Dependent Claim
22 words
The method of claim 1, wherein the bonded metal powder is removed from the surface of the pre-formed body by mechanical machining.
Claim 16
Dependent Claim
34 words
The method of claim 14, wherein holes are mechanically machined through portions of the bonded metal powder allowing for a means for directly anchoring the bonded metal powder portion to said another metal component.
Claim 17
Dependent Claim
35 words
The method of claim 15, wherein a portion of the metal powder is pre-pressed into an intermediate form thereby imparting green strength and functions as a partial positioner of the pre-formed body within the can.
Claim 18
Dependent Claim
195 words
A composite component comprising a pre-formed body made from a base material chosen from the group consisting of a ceramic, a high temperature glass/ceramic composite and a carbon-in-carbon composite and a metallic component bonded to a selected area upon the pre-formed body, the method for making the composite component comprising: placing the pre-formed body in a peripherally walled can, with the pre-formed body spaced throughout its entire extent, from the can wall, to define a space therebetween; filling the space between the pre-formed body and the can wall with a powdered metal, thereby completely surrounding the pre-formed body with the powdered metal; sealing and evacuating the can; applying hot isostatic pressure to the can to compact and sinter the metal powder, and to bond the metal powder to the pre-formed body; removing the can from the exterior of the completely coated body; and removing the bonded metal powder from selected areas on the surface of the pre-formed body to expose areas of the base material and to leave the bonded metal powder at other areas, whereby the composite component can be directly connected to another metal component through a portion of the bonded metal powder.
Claim 19
Dependent Claim
195 words
A composite component comprising a pre-formed body made from a base material chosen from the group consisting of a ceramic, a high temperature glass/ceramic composite and a carbon-in-carbon composite and a metallic component bonded to a selected area upon the pre-formed body, the method for making the composite component comprising: placing the pre-formed body in a peripherally walled can, with the pre-formed body spaced throughout its entire extent, from the can wall, to define a space therebetween; filling the space between the pre-formed body and the can wall with a powdered metal, thereby completely surrounding the pre-formed body with the powdered metal; sealing and evacuating the can; applying hot isostatic pressure to the can to compact and sinter the metal powder, and to bond the metal powder to the pre-formed body; removing the can from the exterior of the completely coated body; and removing the bonded metal powder from selected areas on the surface of the pre-formed body to expose areas of the base material and to leave the bonded metal powder at other areas, whereby the composite component can be directly connected to another metal component through a portion of the bonded metal powder.
Claim 20
Dependent Claim
60 words
The composite component of claim 17, wherein the composite component comprises an integral hub portion and blade portion for a turbine wheel, portions of said other areas of bonded metal powder having holes drilled therethrough for receiving metal portions which are fixed to said another metal component, the turbine wheel comprising a plurality of integral hub portions and blade portions.
Claim 21
Dependent Claim
36 words
The composite component of claim 17, wherein the composite component comprises an integral aerofoil blade portion and root portion for a rotor turbine, the rotor turbine comprising a plurality of integral blade portions and root portions.
Claim 22
Dependent Claim
32 words
The composite component of claim 17, wherein the composite component comprises a flame tube, said other areas of the bonded metal powder comprise supporting ribs which effectively strengthen the pre-formed body portion.
References Cited (Backward Citations)
US2267954A
Cited
GB1012162A
Cited
FR1321788A
Cited
JPS501908A
Cited
GB1490773A
Cited
US4214906A
Cited
DE2456435A1
Cited
US4362471A
Cited
US4063939A
Cited
US4097276A
Cited
GB1488762A
Cited
US4314007A
Cited
GB1588920A
Cited
US4137619A
Cited
JPS5562103A
Cited
US4293619A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-08 | 1988-07-09 | 1989-01-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-08 | 1992-07-09 | 1993-01-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-08 | 1996-07-09 | 1997-01-08 | $7700.00 | Window Closed / Lapsed |