Method of producing an article which comprises a first zone of a nonoxide ceramic material and a second zone of a softer material
Assignee: Volkswagen AG
•
Filing: 1975-11-26
•
Granted: 1980-07-29
•
Expires: 1995-11-26
Abstract
Abstract The method produces an article which has a first zone comprising a nonoxide ceramic material (which materials cannot be soldered or welded) and a second zone comprising a different, softer material such as one which can be soldered or welded to other parts. A transition layer between the zones of the article comprises both materials for bonding the zones together. The method forms the article from powders with heat and pressure.
Inventors
- 👤 Manfred Langer
- 👤 Johann Siebels
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 19:35
CPC Classifications
B; B23; B23K; B23K1/00; B23K1/20; B22; B22F; B22F7/00; B22F7/06; B23K1/19; B32; B32B; B32B18/00; C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/593; C04B35/597; C04B2235/00; C04B2235/65; C04B2235/658; C04B2237/00; C04B2237/02; C04B2237/04; C04B2237/08; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/343; C04B2237/36; C04B2237/361; C04B2237/365; C04B2237/368; C04B2237/50; C04B2237/60; C04B2237/76; C04B2237/84; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12021
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
197 words
A method of producing an article, such as a turbine blade including a first zone of nonoxide ceramic material and a second zone of a different material, which is softer than the nonoxide ceramic material, comprising the steps of introducing powders of a first material, which is at least capable of forming nonoxide ceramic material, and powders of a second material, which is different from and softer than the first material, into respective portions of a mold corresponding, respectively, to the first and second zones of the article; mingling powders of the first material with powders of the second material to form a transition region between the introduced powders of the first and second materials; and molding, by at least the common application of pressure, the introduced powders of the first and second materials, including the mingled powders, into a solid article having a first zone of a nonoxide ceramic material formed from the first material, a second zone of a different, softer material formed from the second material and a transition layer formed between the first and second zones from the mingled powders in the transition region for bonding the first zone to the second zone.
Claim 2
Independent Claim
197 words
A method of producing an article, such as a turbine blade including a first zone of nonoxide ceramic material and a second zone of a different material, which is softer than the nonoxide ceramic material, comprising the steps of introducing powders of a first material, which is at least capable of forming nonoxide ceramic material, and powders of a second material, which is different from and softer than the first material, into respective portions of a mold corresponding, respectively, to the first and second zones of the article; mingling powders of the first material with powders of the second material to form a transition region between the introduced powders of the first and second materials; and molding, by at least the common application of pressure, the introduced powders of the first and second materials, including the mingled powders, into a solid article having a first zone of a nonoxide ceramic material formed from the first material, a second zone of a different, softer material formed from the second material and a transition layer formed between the first and second zones from the mingled powders in the transition region for bonding the first zone to the second zone.
Claim 3
Dependent Claim
13 words
A method as in claim 1 wherein the first material is a nitride.
Claim 4
Dependent Claim
30 words
A method as set forth in claim 1 wherein the first material is selected from the group consisting of Si 3 N 4 , SiC, boron nitride, and sialons compounds.
Claim 5
Dependent Claim
36 words
A method as set forth in claim 1 wherein the second material is selected from the group consisting of Al 2 O 3 , 52%Cu--35%Cr--13%Ni, 35%Cu--15%Ni, Co-Ni-Fe Compounds, Co-Ni-Fe-Mo compounds, transition metals, and transition metal compounds.
Claim 6
Dependent Claim
25 words
A method as in claim 2 wherein the first material is a nonoxide ceramic material and the molding step is carried out by hot molding.
Claim 7
Dependent Claim
50 words
A method as set forth in claim 5 wherein the pressure of the hot molding step is in a range of from about 50 to about 1000 kg/cm 2 and the temperature of the hot molding step is in a range of from about 1200° C. to about 1850° C.
Claim 8
Dependent Claim
27 words
A method as set forth in claim 6 wherein the pressure is from 300 to 500 kg/cm 2 and the temperature from 1600° C. to 1750° C.
Claim 9
Dependent Claim
83 words
A method as set forth in claim 5 further comprising the step of introducing particles of a third material in the transition region, the third material being capable of forming a solid compound with a gas liberated from one of the other materials by the heat generated by the hot molding step and being selected from the group consisting of Al, Mo, and B, thereby substantially preventing the formation of gas bubbles which the gas would otherwise have formed in the transition layer.
Claim 10
Dependent Claim
52 words
A method as set forth in claim 5 wherein the second material forms a solid compound with a gas liberated from the nonoxide ceramic material by the heat generated by the hot molding step, thereby substantially preventing the formation of gas bubbles which the gas would otherwise have formed in the article.
Claim 11
Dependent Claim
28 words
A method as set forth in claim 5 wherein the nonoxide ceramic material is Si 3 N 4 and the second material is a silicide or nitride former.
Claim 12
Dependent Claim
42 words
A method as set forth in claim 10 wherein the second material is Al 2 O 3 which forms a sialon compound and nitrides at least in the transition layer with gases liberated from the Si 3 N 4 by the heat.
Claim 13
Dependent Claim
79 words
A method as set forth in claim 1 wherein the molding step is carried out by cold molding and the first material is one which is capable of forming nonoxide ceramic material upon further treatment, the method further comprising the step of treating the first material and the mingled first and second materials with heat in a gas atmosphere, after they have been cold molded, to form the first zone of a nonoxide ceramic material and the transition layer.
Claim 14
Dependent Claim
22 words
A method as set forth in claim 12 wherein the first material is Si and the gas atmosphere is a nitrating atmosphere.
Claim 15
Dependent Claim
32 words
A method as set forth in claim 13 wherein the heat supplied during the treating step is at a temperature in a range of from about 1200° C. to about 1600° C.
Claim 16
Dependent Claim
54 words
A method as set forth in claim 12 wherein the first material is SiC and the gas atmosphere is a non-oxidizing atmosphere which is capable of producing, with the heat generated by the treating step, a diffusion of grain interfaces in the first material to form the first zone of a nonoxide ceramic material.
Claim 17
Dependent Claim
25 words
A method as set forth in claim 13 wherein the nitrating atmosphere is selected from the group consisting of N 2 and NH 3 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-07-29 | 1984-01-28 | 1984-07-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-07-29 | 1988-01-28 | 1988-07-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-07-29 | 1992-01-28 | 1992-07-29 | $7700.00 | Window Closed / Lapsed |