Multiple-layer, multiple-phase titanium/nitrogen adhesion/diffusion barrier layer structure for gold-base microcircuit interconnection
Assignee: Intersil Corp
•
Filing: 1986-06-16
•
Granted: 1987-10-27
•
Expires: 2006-06-16
Abstract
Abstract To securely attach a narrow line width electrodeposited layer of gold to an underlying semiconductor structure a thin multiphase adhesion film of nitrogen-modified titanium is formed between a titanium nitride diffusion barrier layer and an overlying gold seed layer. This additional layer nitrogen-modified titanium layer provides a titanium base to ensure adhesion of the gold, yet contains sufficient nitrogen interstitially dispersed in the thin titanium film to prevent formation of unetchable gold-titanium compounds.
Inventors
- 👤 Jimmy C. Black
- 👤 Bruce E. Roberts
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 14:00
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/042; H10P; H10P14/00; H10P14/40; H10P14/412; H10W20/0375; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12528; Y10T428/12535; Y10T428/12576; Y10T428/12771; Y10T428/12806; Y10T428/12861; Y10T428/12896
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
96 words
A multiple layer structure for adhering gold to an underlying substrate comprising: a first layer of titanium overlying said substrate; a second layer of titanium nitride overlying said first layer; a third layer of nitrogen-modified titanium overlying said second layer and being of a thickness large enough to provide sufficient titanium for adherence with an overlying gold layer to be formed thereon but less than that which would cause titanium-gold compounds to be formed on the surface of said overlying gold layer as a result of subsequent heating; and a gold layer overlying said third layer.
Claim 2
Dependent Claim
96 words
A multiple layer structure for adhering gold to an underlying substrate comprising: a first layer of titanium overlying said substrate; a second layer of titanium nitride overlying said first layer; a third layer of nitrogen-modified titanium overlying said second layer and being of a thickness large enough to provide sufficient titanium for adherence with an overlying gold layer to be formed thereon but less than that which would cause titanium-gold compounds to be formed on the surface of said overlying gold layer as a result of subsequent heating; and a gold layer overlying said third layer.
Claim 3
Dependent Claim
29 words
A multiple layer structure according to claim 1, wherein the thickness of said third layer of nitrogen-modified titanium lies in a range of from 100 Å to 400 Å.
Claim 4
Dependent Claim
20 words
A multiple layer structure according to claim 2, wherein said gold layer has a thickness of at least 500 Å.
Claim 5
Dependent Claim
26 words
A multiple layer structure according to claim 2, wherein the thickness of said gold layer lies in a range of from 500 Å to 1000 Å.
Claim 6
Dependent Claim
41 words
A multiple layer structure according to claim 1, wherein the bulk of said third layer of nitrogen-modified titanium is characterized by the absence of a nitride compound of titanium, but contains nitrogen interstitially distributed in the titanium of said third layer.
Claim 7
Dependent Claim
32 words
A multiple layer structure according to claim 1, wherein the thickness of said first layer is greater than 100 Å and the thickness of said second layer is greater than 1000 Å.
Claim 8
Independent Claim
98 words
A method adhering gold to an underlying substrate comprising the steps of: (a) forming a multiple layer arrangement of titanium and titanium nitride on said substrate; (b) forming a layer of nitrogen-modified titanium on said multiple layer arrangement, said layer having a thickness large enough to provide sufficient titanium for adherence with an overlying gold layer to be formed thereon but less than that which would cause titanium-gold compounds to be formed on the surface of said overlying gold layer as a result of subsequent heating; and (c) forming a gold layer on said layer of nitrogen-modified titanium.
Claim 9
Independent Claim
98 words
A method adhering gold to an underlying substrate comprising the steps of: (a) forming a multiple layer arrangement of titanium and titanium nitride on said substrate; (b) forming a layer of nitrogen-modified titanium on said multiple layer arrangement, said layer having a thickness large enough to provide sufficient titanium for adherence with an overlying gold layer to be formed thereon but less than that which would cause titanium-gold compounds to be formed on the surface of said overlying gold layer as a result of subsequent heating; and (c) forming a gold layer on said layer of nitrogen-modified titanium.
Claim 10
Dependent Claim
35 words
A method according to claim 7, wherein step (a) comprises the steps of: (a-1) forming a layer of titanium on said substrate; and (a-2) forming a layer of titanium nitride on said layer of titanium.
Claim 11
Dependent Claim
52 words
A method according to claim 7, wherein step (b) comprises the steps of depositing titanium on said multiple layer while introducing nitrogen into the deposited titanium such that the bulk of said layer of nitrogen-modified titanium is absent a nitride compound of titanium, but contains nitrogen interstitially distributed in the deposited titanium.
Claim 12
Dependent Claim
27 words
A method according to claim 9, wherein step (b) comprises forming said nitrogen-modified titanium to a thickness in a range of from 100 Å to 400 Å.
Claim 13
Dependent Claim
52 words
A method according to claim 8, wherein step (b) comprises the steps of depositing titanium on said multiple layer while introducing nitrogen into the deposited titanium such that the bulk of said layer of nitrogen-modified titanium is absent a nitride compound of titanium, but contains nitrogen interstitially distributed in the deposited titanium.
Claim 14
Dependent Claim
27 words
A method according to claim 11, wherein step (b) comprises forming said nitrogen-modified titanium to a thickness in a range of from 100 Å to 400 Å.
Claim 15
Dependent Claim
131 words
For use in a semiconductor device wherein a gold seed layer used in electroplating a gold interconnect layer is provided over the surface of a semiconductor structure, a method of adhering said gold interconnect layer to said structure comprising the steps of: (a) forming a first layer of titanium on said semiconductor structure; (b) forming a second layer of titanium nitride on said first layer of titanium; (c) forming a third layer of nitrogen-modified titanium on said second layer, said third layer having a thickness large enough to provide sufficient titanium for adherence with an overlying gold layer to be formed thereon but less than that which would cause titanium-gold compounds to be formed with said overlying gold layer; and forming a gold layer on said third layer of nitrogen-modified titanium.
Claim 16
Dependent Claim
131 words
For use in a semiconductor device wherein a gold seed layer used in electroplating a gold interconnect layer is provided over the surface of a semiconductor structure, a method of adhering said gold interconnect layer to said structure comprising the steps of: (a) forming a first layer of titanium on said semiconductor structure; (b) forming a second layer of titanium nitride on said first layer of titanium; (c) forming a third layer of nitrogen-modified titanium on said second layer, said third layer having a thickness large enough to provide sufficient titanium for adherence with an overlying gold layer to be formed thereon but less than that which would cause titanium-gold compounds to be formed with said overlying gold layer; and forming a gold layer on said third layer of nitrogen-modified titanium.
Claim 17
Dependent Claim
49 words
A method according to claim 13, wherein step (c) comprises depositing titanium on said second layer while introducing nitrogen into the deposited titanium such that bulk of said third layer of nitrogen-modified titanium is absent a nitride compound of titanium, but contains nitrogen interstitially distributed in the deposited titanium.
Claim 18
Dependent Claim
27 words
A method according to claim 14, wherein step (b) comprises forming said nitrogen-modified titanium to a thickness in a range of from 100 Å to 400 Å.
Claim 19
Dependent Claim
25 words
A method according to claim 15, wherein step (c) comprises forming said gold layer to a thickness in a range of at least 500 Å.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-10-26 | 1991-04-27 | 1991-10-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-10-26 | 1995-04-27 | 1995-10-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-10-26 | 1999-04-27 | 1999-10-27 | $7700.00 | Window Closed / Lapsed |