Manufacturing method of release paper
Assignee: Goyo Paper Working Co Ltd
•
Filing: 1985-06-06
•
Granted: 1987-10-27
•
Expires: 2005-06-06
Abstract
Abstract The present invention relates to a method of manufacturing a release paper characterized in that a mixture of polyolefin and a silicone release agent compatible therewith comprising a reaction product of polymethyl hydrogen siloxane, vinyl group-containing poly-dimethyl siloxane and at least one of olefins or polyolefins having one or more double-bonds is extruded onto a substrate of paper, fabric, film etc., the laminate is heat treated for the release agent contained in the mixed layer of the above-mentioned laminate to bleed onto the surface of the mixed layer to be thus localized and the localized release agent is fixed by curing. The release agent's compatibility with the polyolefin, and this film forming and stretching properties are improved, and since the release agent of high concentration is localized and fixed by curing on the surface of the release agent layer, only a small amount of the release agent is needed.
Inventors
- 👤 Shuzo Ohara
- 👤 Ryoichi Kitamura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 09:23
CPC Classifications
B; B32; B32B; B32B38/00; B32B38/0036; B29; B29C; B29C33/00; B29C33/56; B29C33/60; B29C33/62; B29C33/64; B29C33/68; B29C37/00; B29C37/0067; B29C37/0075; B32B27/00; B32B27/06; B32B27/10; B32B27/18; B32B27/32; B32B7/00; B32B7/04; B32B7/06; D; D21; D21H; D21H25/00; D21H25/04; D21H25/06; B29K; B29K2083/00; B29L; B29L2009/00
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
137 words
A method of manufacturing a release paper comprising: (1) extruding a mixture of a polyolefin resin A and a silicone release agent B compatible therewith onto a substrate to prepare a laminate, said silicone release agent comprising a reaction product obtained by reacting (a) a polymethyl hydrogen silicone, (b) a vinyl group-containing poly-dimethyl siloxane, and (c) at least one compound selected from the group consisting of olefins and polyefins having at least one double bond, said reaction being stopped at the start of gelling; (2) heat treating the obtained laminate to cause the silicone release agent B contained in the extruded mixture of the polyolefin A and the silicone release agent B to bleed onto the surface of the mixture and thus become localized; and then (3) curing the localized silicone release agent B to fix it.
Claim 2
Independent Claim
137 words
A method of manufacturing a release paper comprising: (1) extruding a mixture of a polyolefin resin A and a silicone release agent B compatible therewith onto a substrate to prepare a laminate, said silicone release agent comprising a reaction product obtained by reacting (a) a polymethyl hydrogen silicone, (b) a vinyl group-containing poly-dimethyl siloxane, and (c) at least one compound selected from the group consisting of olefins and polyefins having at least one double bond, said reaction being stopped at the start of gelling; (2) heat treating the obtained laminate to cause the silicone release agent B contained in the extruded mixture of the polyolefin A and the silicone release agent B to bleed onto the surface of the mixture and thus become localized; and then (3) curing the localized silicone release agent B to fix it.
Claim 3
Dependent Claim
38 words
A manufacturing method as recited in claim 1, wherein said polyolefin (c) having at least one double bond is at least one selected from the group consisting of 1,4-polybutadiene, a mixture of 1,4-polybutadiene and 1,2-polybutadiene polyisoprene and polybutene.
Claim 4
Dependent Claim
31 words
A manufacturing method as recited in claim 1, wherein said polyolefin resin A is selected from the group consisting of polyethylene, polypropyrene, 4-methylpentene-1 resin, ethylene-vinyl acetate copolymer resin and mixtures thereof.
Claim 5
Dependent Claim
34 words
A manufacturing method as recited in claim 1, wherein said release agent B is mixed with the polyolefin resin A at approximately 1-10 weight percents based on the weight of said polyolefin resin (A).
Claim 6
Dependent Claim
32 words
A manufacturing method as recited in claim 1, wherein said heat treatment is carried out by leaving said laminate for approximately 10-60 minutes after its surface temperature has reached approximately 70°-120° C.
References Cited (Backward Citations)
US3393106A
Cited
US3826677A
Cited
US4052495A
Cited
US4160798A
Cited
US4222973A
Cited
US4244912A
Cited
US4301103A
Cited
SU1054069A1
Cited
US4557887A
Cited
US4454266A
Cited
JPS6032610A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-10-26 | 1991-04-27 | 1991-10-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-10-26 | 1995-04-27 | 1995-10-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-10-26 | 1999-04-27 | 1999-10-27 | $7700.00 | Window Closed / Lapsed |