Composition and process for delustering plastisol films

Claim 2

A process of treating a carrier cloth for use in the production of plastisol film having a delustered surface, said process comprising the steps of: removing the sizing from said cloth; adjusting the ph of said cloth to about 6.0-7.5; preparing a first mixture of a silicone polyester resin, an effective amount of a fluorotelemer dispersed in a solvent for delustering the surface of said plastisol and permitting ready release of said film from said cloth during the production of said plastisol film, an effective amount of an inert flatting agent for reducing the gloss of said plastisol surface during said production, an effective amount of an anti-settling agent to prevent settling of said flatting agent prior to curing of said resin, and an aromatic solvent; blending said first mixture to disperse the particulate solids therein to maintain the sizes thereof no greater than about 25 microns; preparing a delustering agent by admixing with said blended first mixture a curing agent for curing said resin upon application of an effective amount of heat, an effective amount of a catalyst solution to initiate reaction between said resin and said curing agent upon application of said heat, and an additional aromatic solvent to maintain said delustering agent in solution and to enable ready application thereof to said cloth; coating the surfaces of said cloth with said delustering agent solution to fill the interstices therein; and drying said coated cloth at an elevated temperature sufficient to cure said resin.

Claim 3

The process as described in claim 1, wherein the sizing is removed from said cloth by scouring said cloth with caustic material, the pH of said cloth being adjusted to insure complete removal of the alkali solvents therein.

Claim 4

The process as described in claim 2, wherein said cloth is dryed and heat set at approximately 200° C. to prevent shrinkage during subsequent heating of said cloth after coating thereof with said delustering agent solution.

Claim 5

The process as described in claim 1, wherein said carrier cloth comprises a woven viscose rayon cloth.

Claim 6

The process as described in claim 1, wherein said first mixture is blended to disperse the particulate solids therein to maintain sizes thereof at approximately 20 microns.

Claim 7

The process as described in claim 1, wherein a first surface of said cloth is coated with said delustering agent solution and then heat dryed at approximately 175-180° C. for about 2-4 minutes, and then a second surface of said cloth is coated with said delustering agent solution and then heat dryed at approximately 175-180° C. for approximately 2-4 minutes.

Claim 8

The process as described in claim 1, wherein said cloth is coated with said delustering agent by saturating said cloth from both sides with said delustering agent and then heat drying said saturated cloth at approximately 175-180° C. for approximately 2-4 minutes to cure said resin.

Claim 9

A process of manufacturing a plastisol resin film having a delustered surface, said process comprising the steps of: applying to the surfaces of a continuous roll of woven cloth, which cloth has been desized and has a pH of about 6.0-7.5, a solution of a delustering agent comprising a mixture of about 25-60% by weight of a silicone polyester resin, about 1-20% by weight of a fluorotelemer dispersed in a solvent, an effective amount of a curing agent for reacting with and curing said resin upon application of an effective amount of heat, an effective amount of a catalyst solution to initiate reaction between said resin and said curing agent upon application of said heat, an effective amount of an inert flatting agent for reducing the gloss of said plastisol, an effective amount of an anti-settling agent comprising a thixotrop in solution to prevent settling of said flatting agent prior to curing of said resin and to prevent foaming of said delustering agent when applied to said carrier cloth, and an effective amount of an aromatic solvent to maintain said mixture in solution prior to application of said heat and to permit ready application of said delustering agent to said cloth; drying the coated cloth at an elevated temperature sufficient to cure said resin; applying a film-forming plastisol agent to one surface of said coated carrier cloth; curing said plastisol agent to form a solid film on said cloth; and separating said plastisol film from said carrier cloth, said separated carrier cloth being reusable without further coating or treatment.

Claim 10

A process of manufacturing a plastisol resin film having a delustered surface, said process comprising the steps of: applying to the surfaces of a continuous roll of woven cloth, which cloth has been desized and has a pH of about 6.0-7.5, a solution of a delustering agent comprising a mixture of about 25-60% by weight of a silicone polyester resin, about 1-20% by weight of a fluorotelemer dispersed in a solvent, an effective amount of a curing agent for reacting with and curing said resin upon application of an effective amount of heat, an effective amount of a catalyst solution to initiate reaction between said resin and said curing agent upon application of said heat, an effective amount of an inert flatting agent for reducing the gloss of said plastisol, an effective amount of an anti-settling agent comprising a thixotrop in solution to prevent settling of said flatting agent prior to curing of said resin and to prevent foaming of said delustering agent when applied to said carrier cloth, and an effective amount of an aromatic solvent to maintain said mixture in solution prior to application of said heat and to permit ready application of said delustering agent to said cloth; drying the coated cloth at an elevated temperature sufficient to cure said resin; applying a film-forming plastisol agent to one surface of said coated carrier cloth; curing said plastisol agent to form a solid film on said cloth; and separating said plastisol film from said carrier cloth, said separated carrier cloth being reusable without further coating or treatment.

Claim 11

The process as described in claim 1, wherein said cloth is desized by scouring said cloth until said cloth has a pH of 6.0-7.5, and then drying and heat setting said cloth at approximately 200° C. in order to prevent shrinkage of said cloth during subsequent heating during said process.

Claim 12

The process as described in claim 1, wherein said solution of delustering agent is applied to a first surface of said cloth and then dryed at a temperature of about 175-180° C. for approximately 2-4 minutes, and then a second side of said cloth is coated with said delustering agent and then dryed at approximately 175-180° C. for about 2-4 minutes.

Claim 13

The process as described in claim 1, wherein said woven cloth is saturated from both sides thereof with said delustering agent and then heat dryed at a temperature of about 175-180° C. to cure said resin.

Claim 14

The process as described in claim 1, wherein said plastisol agent is cured on said coated cloth by heating said agent to approximately 175-180° C. for about 1-4 minutes.

Claim 15

The process as described in claim 1, wherein said plastisol film is separated from said carrier cloth by physically pulling the two layers apart, said plastisol film readily releasing from said carrier cloth due to the presence of said fluorotelemer in said delustering agent at the interface between said carrier cloth and said plastisol film.