Method and apparatus for forming ultrafine metal powders
Assignee: IIT Research Institute
•
Filing: 1985-07-03
•
Granted: 1987-08-25
•
Expires: 2005-07-03
Abstract
Abstract A method and apparatus for producing ultrafine metal powders in which a laser beam is focused on the surface of a workpiece or feedstock and moved thereacross so as to create a cavity within the workpiece through melting and vaporization that contains the metal melted to form the cavity. A subsonic pulsating blast of inert gas is directed at the cavity to atomize the molten metal, rapidly cool the resulting droplets, and transport the droplets to a collection area. The cavity formed by the laser beam is a "keyhole" of deep cavity having a depth approximately three to four times greater than its width. The focal point of the laser beam is moved across the workpiece at a rate from approximately 50 to 80 inches per minute to ensure that the molten metal remains in the cavity prior to the gas atomization. Alloy metal powders can be produced by this method of laser blast atomization providing an alloying metal at the base metal where the cavity is formed so that, upon melting of the base metal, the alloy metal will melt into solution with the molten base metal in the cavity prior to gas atomization. Additionally, nonmetallic impurities may be removed from the molten metal contained within the cavity formed by the laser beam by vaporization.
Inventors
- 👤 Frederic D. Seaman
- 👤 Srinivasan Rajagopal
- 👤 William H. Altergott
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 21:44
CPC Classifications
B; B22; B22F; B22F9/00; B22F9/02; B22F9/06; B22F9/08; B22F9/082; B22F2009/0816; B22F2009/0848
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
103 words
A method for producing metal powders from a pre-formed metal workpiece comprising: (a) focusing a laser beam through the plane at the surface to a focus below the surface of the workpiece; (b) moving the focal point of the laser beam relative to the workpiece; (c) creating a cavity below the surface of the workpiece through melting and vaporization with the laser beam, the cavity containing the metal melted to form the cavity; and (d) directing a pulsating blast of inert gas at the cavity to atomize the molten metal, rapidly cool the resulting droplets, and transport the droplets to a collection area.
Claim 2
Independent Claim
103 words
A method for producing metal powders from a pre-formed metal workpiece comprising: (a) focusing a laser beam through the plane at the surface to a focus below the surface of the workpiece; (b) moving the focal point of the laser beam relative to the workpiece; (c) creating a cavity below the surface of the workpiece through melting and vaporization with the laser beam, the cavity containing the metal melted to form the cavity; and (d) directing a pulsating blast of inert gas at the cavity to atomize the molten metal, rapidly cool the resulting droplets, and transport the droplets to a collection area.
Claim 3
Dependent Claim
19 words
The method of claim 1 including the step of preheating the workpiece to a temperature of approximately 400° F.
Claim 4
Dependent Claim
14 words
The method of claim 2 wherein the workpiece is preheated with a laser beam.
Claim 5
Dependent Claim
22 words
The method of claim 1 wherein the laser has a power density between approximately 10 5 and 10 6 W/cm 2 .
Claim 6
Dependent Claim
29 words
The method of claim 1 wherein the focal point of the laser beam is moved across the workpiece at a rate from approximately 50 to 80 inches per minute.
Claim 7
Dependent Claim
28 words
The method of claim 1 wherein the cavity created in the workpiece by the laser beam has a depth approximately 3 to 4 times greater than its width.
Claim 8
Dependent Claim
28 words
The method of claim 5 wherein the cavity created in the workpiece by the laser beam has a depth approximately 3 to 4 times greater than its width.
Claim 9
Dependent Claim
16 words
The method of claim 6 wherein the cavity is between approximately one-quarter to one-half inch deep.
Claim 10
Dependent Claim
16 words
The method of claim 7 wherein the cavity is between approximately one-quarter to one-half inch deep.
Claim 11
Dependent Claim
23 words
The method of claim 1 wherein the inert gas has a pressure of approximately 700 psig and is pulsed at approximately 172 Hz.
Claim 12
Dependent Claim
11 words
The method of claim 10 wherein the inert gas is helium.
Claim 13
Independent Claim
114 words
A method for producing metal powders from a pre-formed metal workpiece comprising: (a) focusing a laser beam below the surface of the workpiece; (b) moving the focal point of the laser beam relative to the workpiece; (c) creating a cavity within the workpiece through melting and vaporization with the laser beam, the cavity having a depth approximately 3 to 4 times greater than its width, the depth being between approximately one-quarter to one-half inch deep, the cavity containing the metal melted to form the cavity; (d) directing a pulsating blast of inert gas at the cavity to atomize the molten metal, rapidly cool the resulting droplets, and transport the droplets to a collection area.
Claim 14
Independent Claim
114 words
A method for producing metal powders from a pre-formed metal workpiece comprising: (a) focusing a laser beam below the surface of the workpiece; (b) moving the focal point of the laser beam relative to the workpiece; (c) creating a cavity within the workpiece through melting and vaporization with the laser beam, the cavity having a depth approximately 3 to 4 times greater than its width, the depth being between approximately one-quarter to one-half inch deep, the cavity containing the metal melted to form the cavity; (d) directing a pulsating blast of inert gas at the cavity to atomize the molten metal, rapidly cool the resulting droplets, and transport the droplets to a collection area.
Claim 15
Independent Claim
126 words
A method for producing alloy metal powders by means of laser blast atomization, the steps comprising: (a) forming a workpiece of the base metal; (b) providing an alloying metal to the base metal; (c) focusing a laser beam below the surface of the workpiece; (d) moving the focal point of the laser beam relative to the workpiece; (e) creating a cavity within the workpiece through melting and vaporization with the laser beam; (f) melting the alloying material within the cavity and combining the melted alloy material with the base metal to form a molten metal solution; (g) directing a pulsating blast of inert gas at the cavity to atomize the molten metal solution, rapidly cool the resulting droplets, and transport the droplets to a collection area.
Claim 16
Independent Claim
126 words
A method for producing alloy metal powders by means of laser blast atomization, the steps comprising: (a) forming a workpiece of the base metal; (b) providing an alloying metal to the base metal; (c) focusing a laser beam below the surface of the workpiece; (d) moving the focal point of the laser beam relative to the workpiece; (e) creating a cavity within the workpiece through melting and vaporization with the laser beam; (f) melting the alloying material within the cavity and combining the melted alloy material with the base metal to form a molten metal solution; (g) directing a pulsating blast of inert gas at the cavity to atomize the molten metal solution, rapidly cool the resulting droplets, and transport the droplets to a collection area.
Claim 17
Independent Claim
191 words
A method for producing alloy metal powders by means of laser blast atomization wherein the alloying metal has a higher vapor pressure in its molten state than the base metal, the steps comprising: (a) forming a workpiece of the base metal with a layer of alloying material a pre-determined distance below the surface thereof; (b) focusing a laser beam below the surface of the workpiece; (c) moving the focal point of the laser beam relative to the workpiece; (d) creating a cavity within the workpiece with the laser beam to the depth of the layer of alloying material, the cavity containing the metal and alloy addition melted during the formation of the cavity; (e) melting the layer of alloying material at the base of the cavity, where high vapor pressures, caused by the weight of the molten metal that forms the cavity walls, to prevent the alloying material from vaporizing prior to forming a solution with the molten base metal; and (f) directing a pulsating blast of inert gas at the cavity to atomize the molten metal solution, rapidly cool the resulting droplets, and transport the droplets to a collection area.
Claim 18
Independent Claim
191 words
A method for producing alloy metal powders by means of laser blast atomization wherein the alloying metal has a higher vapor pressure in its molten state than the base metal, the steps comprising: (a) forming a workpiece of the base metal with a layer of alloying material a pre-determined distance below the surface thereof; (b) focusing a laser beam below the surface of the workpiece; (c) moving the focal point of the laser beam relative to the workpiece; (d) creating a cavity within the workpiece with the laser beam to the depth of the layer of alloying material, the cavity containing the metal and alloy addition melted during the formation of the cavity; (e) melting the layer of alloying material at the base of the cavity, where high vapor pressures, caused by the weight of the molten metal that forms the cavity walls, to prevent the alloying material from vaporizing prior to forming a solution with the molten base metal; and (f) directing a pulsating blast of inert gas at the cavity to atomize the molten metal solution, rapidly cool the resulting droplets, and transport the droplets to a collection area.
Claim 19
Independent Claim
134 words
A method of producing alloy metal powders by means of laser blast atomization wherein the alloying metal has a melting temperature higher than the base metal, the steps comprising: (a) distributing the alloying metal over the surface of a workpiece made of the base metal; (b) focusing a laser beam below the surface of the workpiece; (c) moving the focal point of the laser beam relative to the workpiece; (d) creating a cavity within the workpiece through melting and vaporization with the laser beam, the cavity containing the metal and alloy addition melted to form a molten solution during the formation of the cavity; and (e) directing a pulsating blast of inert gas at the cavity to atomize the molten solution, rapidly cool the resulting droplets, and transport the droplets to a collection area.
Claim 20
Independent Claim
134 words
A method of producing alloy metal powders by means of laser blast atomization wherein the alloying metal has a melting temperature higher than the base metal, the steps comprising: (a) distributing the alloying metal over the surface of a workpiece made of the base metal; (b) focusing a laser beam below the surface of the workpiece; (c) moving the focal point of the laser beam relative to the workpiece; (d) creating a cavity within the workpiece through melting and vaporization with the laser beam, the cavity containing the metal and alloy addition melted to form a molten solution during the formation of the cavity; and (e) directing a pulsating blast of inert gas at the cavity to atomize the molten solution, rapidly cool the resulting droplets, and transport the droplets to a collection area.
Claim 21
Independent Claim
112 words
A method of removing nonmetallic impurities from a workpiece when producing metal powders comprising: (a) focusing a laser beam below the surface of the workpiece; (b) slowly moving the focal point of the laser beam across the workpiece; (c) creating a cavity within the workpiece through melting and vaporization with the laser beam, the cavity containing the metal melted to form the cavity; (d) suspending the impurities in the molten metal within the cavity; (e) vaporizing the impurities with the laser beam; and (f) directing a pulsating blast of inert gas at the cavity to atomize the molten metal, rapidly cool the resulting droplets, and transport the droplets to a collection area.
Claim 22
Independent Claim
112 words
A method of removing nonmetallic impurities from a workpiece when producing metal powders comprising: (a) focusing a laser beam below the surface of the workpiece; (b) slowly moving the focal point of the laser beam across the workpiece; (c) creating a cavity within the workpiece through melting and vaporization with the laser beam, the cavity containing the metal melted to form the cavity; (d) suspending the impurities in the molten metal within the cavity; (e) vaporizing the impurities with the laser beam; and (f) directing a pulsating blast of inert gas at the cavity to atomize the molten metal, rapidly cool the resulting droplets, and transport the droplets to a collection area.
Claim 23
Independent Claim
74 words
An apparatus for producing ultrafine metal powders comprising, in combination, (a) containment means having an inert gas atmosphere therein; (b) means for supporting and moving a workpiece associated with the containment means; (c) laser beam means associated with the containment vessel so that the focal point of the laser beam is coincident with and penetrating into the workpiece; and (d) pulsating gas jet means associated with the containment vessel and directed toward the workpiece.
Claim 24
Independent Claim
74 words
An apparatus for producing ultrafine metal powders comprising, in combination, (a) containment means having an inert gas atmosphere therein; (b) means for supporting and moving a workpiece associated with the containment means; (c) laser beam means associated with the containment vessel so that the focal point of the laser beam is coincident with and penetrating into the workpiece; and (d) pulsating gas jet means associated with the containment vessel and directed toward the workpiece.
Claim 25
Dependent Claim
58 words
The combination of claim 17 wherein the pulsating gas jet means comprises nozzle means, flow interrupter means having a plurality of apertures therein movable into alignment with the nozzle means to permit the flow of gas toward the workpiece and out of alignment with the nozzle to obstruct such flow, and means for moving the flow interrupter means.
Claim 26
Dependent Claim
25 words
The combination of claim 18 wherein the pulsating gas jet means pulses helium at aproximately 172 hz and at a pressure of approximately 700 psig.
Claim 27
Dependent Claim
23 words
The combination of claim 17 wherein the laser beam means has power density between appoximately 10 5 and 10 6 W/cm 2 .
Claim 28
Dependent Claim
37 words
The combination of claim 17 wherein the workpiece supporting and moving means moves the workpiece at a rate between approximately 50 and 80 inches per minute with respect to the focal point of the laser beam means.
References Cited (Backward Citations)
DE1291842B
Cited
US3275787A
Cited
US4036568A
Cited
US4218410A
Cited
US4295808A
Cited
US4014964A
Cited
JPS54100599A
Cited
US4415512A
Cited
US4394332A
Cited
US4383852A
Cited
US4374075A
Cited
US4482375A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-24 | 1991-02-23 | 1991-08-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-24 | 1995-02-23 | 1995-08-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-24 | 1999-02-23 | 1999-08-25 | $7700.00 | Window Closed / Lapsed |