US4014964A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for making metal powder using a laser
Assignee: Federal Mogul LLC
•
Filing: 1975-07-16
•
Granted: 1977-03-29
•
Expires: 1995-07-16
Abstract
Abstract A process for producing high purity metal powders in which a metal or metal alloy of the desired composition is molten and introduced into a chamber in the form of a stream of a controlled cross sectional area which is fragmentized into a plurality of molten droplets by the impingement of a transversely excited laser having a preselected power to achieve the desired magnitude of fragmentation. The resultant droplets are cooled during their free-fall through the chamber and the solidified metal powder is subsequently recovered from the bottom of the chamber.
Inventors
- 👤 Robert L. Probst
- 👤 Barry P. Fairand
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 13:42
CPC Classifications
B; B22; B22F; B22F9/00; B22F9/02; B22F9/06; B22F9/08; B01; B01J; B01J2/00; B01J2/02; B22F2999/00
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
87 words
A process for producing metal powder which comprises the steps of providing a supply of molten metal, introducing said molten metal in the form of a stream having a preselected cross sectional area into a chamber, directing a transversely excited laser beam in impinging relationship against said stream and controlling the pulse rate and power of said laser beam to effect a fragmentation of said stream into a plurality of molten droplets, cooling said droplets to effect a solidification thereof, and recovering the resultant metal powder product.
Claim 2
Dependent Claim
87 words
A process for producing metal powder which comprises the steps of providing a supply of molten metal, introducing said molten metal in the form of a stream having a preselected cross sectional area into a chamber, directing a transversely excited laser beam in impinging relationship against said stream and controlling the pulse rate and power of said laser beam to effect a fragmentation of said stream into a plurality of molten droplets, cooling said droplets to effect a solidification thereof, and recovering the resultant metal powder product.
Claim 3
Dependent Claim
28 words
The process as defined in claim 1, wherein the cross sectional area of said stream is fixed within a range of about 0.0003 to about 1 square inch.
Claim 4
Dependent Claim
31 words
The process as defined in claim 1, wherein a plurality of lasers are directed in impinging relationship against the same portion of said stream at directions angularly spaced from each other.
Claim 5
Dependent Claim
25 words
The process as defined in claim 1, in which said stream is formed by the free gravitational fall of said molten metal through an orifice.
Claim 6
Dependent Claim
28 words
The process as defined in claim 1, in which the cooling of said droplets is accomplished during the free-fall of said droplets toward the bottom of said chamber.
Claim 7
Dependent Claim
14 words
The process as defined in claim 1, in which said stream is substantially continuous.
Claim 8
Dependent Claim
26 words
The process as defined in claim 1, in which said chamber is substantially devoid of any atmosphere having a vacuum of less than about 1 Torr.
Claim 9
Dependent Claim
19 words
The process as defined in claim 1, in which said chamber is filled with an inert argon gas atmosphere.
Claim 10
Dependent Claim
15 words
The process as defined in claim 1, in which said chamber is filled with air.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-03-28 | 1980-09-27 | 1981-03-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-03-28 | 1984-09-27 | 1985-03-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-03-28 | 1988-09-27 | 1989-03-29 | $7700.00 | Window Closed / Lapsed |