Crucibleless preparation of rapidly solidified fine particulates
Assignee: Battelle Memorial Institute Inc
•
Filing: 1981-10-29
•
Granted: 1983-07-19
•
Expires: 2001-10-29
Abstract
Abstract A mass of normally solid material, e.g. metal or metal alloy, which at a temperature within 25 percent of its equilibrium melting point °K has a surface tension of 10 to 2500 dynes/cm. and a viscosity of 0.001 to 1 poise, is changed into fine solid particulates, preferably flake-like to almost spherical shape. A solid mass of the material has a portion thereof, e.g. tip or edge, unconfined by a crucible or the like, heated, such as by a flame or electron beam to alter that portion to a molten state whereby molten droplets or globules fall therefrom to contact a rapidly moving wall of a centrifugally disposed rotating liquid quench fluid, e.g. water or oil, and upon contacting are disrupted and broken up into finer globules or particles which are swept away with and quenched in the rapidly moving quench fluid to become rapidly solidified as fine particulates. These fine particulates subsequently are separated from the quench fluid and classified to find utility for example in powder metallurgical applications.
Inventors
- 👤 Ramaswamy V. Raman
- 👤 Robert S. Carbonara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 13:18
CPC Classifications
B; B22; B22F; B22F9/00; B22F9/02; B22F9/06; B22F9/08; B22F9/10; B22F2009/0804; B22F2009/0812
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
179 words
A method of making solid fine particulates from a normally solid material, which at a temperature within 25 percent of its equilibrium melting point °K has a surface tension in the range of 10 to 2500 dynes/cm. and a viscosity in the range of 0.001 to 1 poise when a molten material, comprising the steps of: (a) heating an unconfined portion of a mass of the solid material to a molten state so as to permit droplets of molten material to fall therefrom; (b) providing a moving ring-like mass of a centrifugally disposed rotating liquid quench fluid; (c) positioning said portion subjected to heating and said moving ring-like mass in relation to each other that the droplets of molten material fall into contact with said moving ring-like mass of the centrifugally disposed rotating liquid quench fluid; (d) breaking said droplets through said contact into fragments and cooling said fragments into solid fine particulates by said moving ring-like mass of the centrifugally disposed rotating liquid quench fluid; and (e) subsequently separating the solid fine particulates from the liquid quench fluid.
Claim 2
Independent Claim
179 words
A method of making solid fine particulates from a normally solid material, which at a temperature within 25 percent of its equilibrium melting point °K has a surface tension in the range of 10 to 2500 dynes/cm. and a viscosity in the range of 0.001 to 1 poise when a molten material, comprising the steps of: (a) heating an unconfined portion of a mass of the solid material to a molten state so as to permit droplets of molten material to fall therefrom; (b) providing a moving ring-like mass of a centrifugally disposed rotating liquid quench fluid; (c) positioning said portion subjected to heating and said moving ring-like mass in relation to each other that the droplets of molten material fall into contact with said moving ring-like mass of the centrifugally disposed rotating liquid quench fluid; (d) breaking said droplets through said contact into fragments and cooling said fragments into solid fine particulates by said moving ring-like mass of the centrifugally disposed rotating liquid quench fluid; and (e) subsequently separating the solid fine particulates from the liquid quench fluid.
Claim 3
Dependent Claim
20 words
The method of claim 1 in which the moving ring-like mass travels at a speed of at least 3750 ft./min.
Claim 4
Dependent Claim
31 words
The method of claim 2 including a providing of an inert gas environment in the immediate vicinity of said molten state of the solid mass and the droplets of molten material.
Claim 5
Dependent Claim
20 words
The method of claim 2 in which the unconfined portion of the mass of the normally solid material is tin.
Claim 6
Dependent Claim
12 words
The method of claim 4 employing water as said liquid quench fluid.
Claim 7
Dependent Claim
20 words
The method of claim 2 in which the breaking of said droplets into said fragments is at least one hundred-fold.
Claim 8
Independent Claim
140 words
A method of preparing solid fine particulates from a normally solid material, which at a temperature within 25 percent of its equilibrium melting point °K has a surface tension in the range of 10 to 2500 dynes/cm. and a viscosity in the range of 0.001 to 1 poise when a molten material, comprising the steps of: (a) disintegrating a molten globule of the solid material into fragments of less than one-hundredth of the volume of the molten globule through the molten globule contacting a moving ring-like mass of a centrifugally disposed rotating liquid quench fluid; and (b) quenching and cooling said fragments into solid fine particulates by the fragments being swept up and wisked into the moving ring-like mass of the centrifugally disposed rotating liquid quench fluid; and (c) subsequently separating the solid fine particulates from the liquid quench fluid.
Claim 9
Independent Claim
140 words
A method of preparing solid fine particulates from a normally solid material, which at a temperature within 25 percent of its equilibrium melting point °K has a surface tension in the range of 10 to 2500 dynes/cm. and a viscosity in the range of 0.001 to 1 poise when a molten material, comprising the steps of: (a) disintegrating a molten globule of the solid material into fragments of less than one-hundredth of the volume of the molten globule through the molten globule contacting a moving ring-like mass of a centrifugally disposed rotating liquid quench fluid; and (b) quenching and cooling said fragments into solid fine particulates by the fragments being swept up and wisked into the moving ring-like mass of the centrifugally disposed rotating liquid quench fluid; and (c) subsequently separating the solid fine particulates from the liquid quench fluid.
Claim 10
Dependent Claim
34 words
The method of claim 7 employing the normally solid material which is a metal or metal alloy and in which the rapidly moving ring-like mass travels at a speed of at least 3750 ft./min.
Claim 11
Dependent Claim
24 words
The method of claim 8 including a providing of an inert gas environment in the vicinities of said disintegrating and of the molten globule.
Claim 12
Dependent Claim
17 words
A method of claim 9 which employs titanium or a titanium-base alloy for the normally solid material.
References Cited (Backward Citations)
US1782038A
Cited
US2040168A
Cited
US2439772A
Cited
US3041672A
Cited
DE1224125B
Cited
US3320338A
Cited
US3896203A
Cited
US4124664A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-07-18 | 1987-01-17 | 1987-07-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-07-18 | 1991-01-17 | 1991-07-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-07-18 | 1995-01-17 | 1995-07-19 | $7700.00 | Window Closed / Lapsed |