Electroless copper plating bath and method
Assignee: C Uyemura & Co Ltd
•
Filing: 1984-09-24
•
Granted: 1987-03-17
•
Expires: 2004-09-24
Abstract
Abstract An electroless copper plating bath is prepared by adding both a metal-cyano-complex used as a stabilizer and an agent for complexing the metal of the metal-cyano-complex to an electroless copper plating bath containing cupric ion, an agent for complexing the cupric ion and a reducing agent, and an article to be plated is immersed in the bath.
Inventors
- 👤 Akemi Kinoshita
- 👤 Ken Araki
- 👤 Hidemi Nawafune
- 👤 Shozo Mizumoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 12:48
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/31; C23C18/38; C23C18/40
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
61 words
An electroless copper plating bath, comprising: a cupric ion complexing agent for complexing cupric ion wherein the cupric ion complexing agent is an ethylenediamine derivative selected from the group consisting of ethylenediaminetetraacetic acid, tetrahydroxy propyl ethylenediamine, N-hydroxy ethyl ethylenediaminetriacetic acid and salts thereof; a reducing agent; a metal-cyano-complex stabilizer; and a metal complexing agent for complexing the metal of said metal-cyano-complex.
Claim 2
Dependent Claim
61 words
An electroless copper plating bath, comprising: a cupric ion complexing agent for complexing cupric ion wherein the cupric ion complexing agent is an ethylenediamine derivative selected from the group consisting of ethylenediaminetetraacetic acid, tetrahydroxy propyl ethylenediamine, N-hydroxy ethyl ethylenediaminetriacetic acid and salts thereof; a reducing agent; a metal-cyano-complex stabilizer; and a metal complexing agent for complexing the metal of said metal-cyano-complex.
Claim 3
Dependent Claim
22 words
The electroless copper plating bath as set forth in claim 1, wherein the ethylenediamine derivative is ethylenediaminetetraacetic acid or a salt thereof.
Claim 4
Dependent Claim
21 words
The electroless copper plating bath as set forth in claim 1, wherein the reducing agent is formaldehyde or a derivative thereof.
Claim 5
Dependent Claim
53 words
The electroless copper plating bath as set forth in claim 1, wherein the concentration of cupric ion is 0.01 to 1 mole/1, the molar concentration of the cupric-ion-complexing agent is equal to or higher than the molar concentration of cupric ion and the concentration of the reducing agent is 0.02 to 0.5 mole/l.
Claim 6
Dependent Claim
56 words
The electroless copper plating bath as set forth in claim 1, wherein the metal-cyano-complex is selected from the group consisting of an alkali metal ferrocyanide, ammonium ferrocyanide, an alkali metal nickelcyanide, ammonium nickelcyanide, an alkali metal cobaltcyanide, ammonium, cobaltcyanide and mixtures thereof, and the agent for complexing the metal of the metal-cyano-complex is an alkanol amine.
Claim 7
Dependent Claim
52 words
The electroless copper plating bath as set forth in claim 1, wherein the concentration of the metal-cyano-complex is 1×10 -5 to 5×10 -2 mole/l and the molar concentration of the metal complexing agent for complexing the metal of the metal-cyano-complex is equal to or higher than the molar concentration of the metal-cyano-complex.
Claim 8
Dependent Claim
54 words
The electroless copper plating bath as set forth in claim 1, wherein a water-soluble nitrogen compound having at least two polar groups is added and at least one of the polar groups is a --NH 2 group or a═NH group which can react with formaldehyde or a derivative thereof to form an addition product.
Claim 9
Dependent Claim
33 words
The electroless copper plating bath as set forth in claim 7, wherein the water-soluble nitrogen compound is an aliphatic compound having the --NH 2 group or the ═NH group and a --COOH group.
Claim 10
Dependent Claim
31 words
The electroless copper plating bath as set forth in claim 7, wherein the concentration of the water-soluble nitrogen compound is 0.1 to 2 moles per one mole quantity of total formaldehyde.
Claim 11
Dependent Claim
18 words
An electroless copper plating method comprising immersing an article to be plated in the bath of claim 1.
Claim 12
Dependent Claim
70 words
An electroless copper plating method comprising immersing an article to be plated in the bath of claim 2, determining the pH or alkalinity of the plating bath from both the absorbance of the plating bath of a pH level higher than 8 and concentration of copper ion in the plating bath, and delivering a signal when the determined pH or alkalinity is lower than a set pH or alkalinity level.
Claim 13
Dependent Claim
43 words
The electroless copper plating method as set forth in claim 11, wherein the concentration of copper ion in the plating bath is determined by measuring the absorbence of the plating bath adjusted to a pH level of below 8 by addition of acid.
Claim 14
Dependent Claim
18 words
The electroless copper plating method comprising immersing an article to be plated in the bath of claim 7.
Claim 15
Dependent Claim
42 words
The electroless copper plating method as set forth in claim 13, which comprises maintaining the deposition rate of said electroless copper plating and the physical properties of the deposit at given levels by maintaining the concentration of free formaldehyde a given level.
Claim 16
Dependent Claim
53 words
The electroless copper plating bath according to claim 1, wherein the concentration of cupric ion is 0.02 to 0.5 mole/1, the molar concentration of the cupric ion complexing agent is equal to or higher than the molar concentration of cupric ion and the concentration of the reducing agent is 0.02 to 0.1 mole/1.
Claim 17
Dependent Claim
28 words
The bath according to claim 1, comprising a stabilizer in addition to the metal-cyano-complex having a nitrogen atom which can bind to cuprous ion to form a complex.
Claim 18
Dependent Claim
30 words
The electrOless copper plating bath according to claim 16, wherein the stabilizer is selected from the group consisting of cyanides, thiocyanates, pyridyl derivatives, phenantroline and its derivatives and organic nitriles.
Claim 19
Dependent Claim
26 words
The electroless copper plating bath according to claim 16, wherein the stabilizer is selected from the group consisting of sodium cyanide, potassium cyanide, α,α'-dipridyl and 2,9-dimethyl-1,10-phenantroline.
Claim 20
Dependent Claim
24 words
The electroless copper plating bath according to claim 7, wherein the nitrogen compound for 1 mole of total formaldehyde is 0.4 to 1.2 moles.
Claim 21
Dependent Claim
20 words
The electroless copper plating bath according to claim 1, wherein the pH is within the range of 11.5 to 12.5.
Claim 22
Dependent Claim
22 words
The electroless copper plating bath according to claim 1, wherein the deposition rate is within the range of 1 to 6 μm/h.
Claim 23
Dependent Claim
64 words
An electroless copper plating bath, comprising: cupric ion; a cupric ion complexing agent for complexing cupric ion wherein the cupric ion complexing agent is selected from the group consisting of diethylenetriaminetriacetic acid, diethylenetriaminepentaacetic acid, nitrotriacetic acid. cyclohexylenediaminetetraacetic acid, citric acid, tataric acid and the salts thereof; a reducing agent; a metal-cyano-complex stabilizer; and a metal complexing agent for complexing the metal of said metal-cyano-complex.
Claim 24
Dependent Claim
64 words
An electroless copper plating bath, comprising: cupric ion; a cupric ion complexing agent for complexing cupric ion wherein the cupric ion complexing agent is selected from the group consisting of diethylenetriaminetriacetic acid, diethylenetriaminepentaacetic acid, nitrotriacetic acid. cyclohexylenediaminetetraacetic acid, citric acid, tataric acid and the salts thereof; a reducing agent; a metal-cyano-complex stabilizer; and a metal complexing agent for complexing the metal of said metal-cyano-complex.
Claim 25
Dependent Claim
87 words
An electroless copper plating bath, comprising cupric ion; a cupric ion complexing agent for complexing cupric ion; a reducing agent; 1×10 -5 to 5×10 -2 mole/1 of a metal-cyano-complex stabilizer selected from the group consisting of an alkali metal ferrocyanide, ammonium ferrocyanide, an alkali metal nickelcyanide, ammonium nickelcyanide, an alkali metal cobaltcyanide, ammonium cobaltcyanide and mixtures thereof; and an alkanol amine for complexing a metal of the metal-cyano-complex, wherein the molar concentration of the alkanol amine is one to three times the molar concentration of the metal-cyano-complex.
Claim 26
Dependent Claim
87 words
An electroless copper plating bath, comprising cupric ion; a cupric ion complexing agent for complexing cupric ion; a reducing agent; 1×10 -5 to 5×10 -2 mole/1 of a metal-cyano-complex stabilizer selected from the group consisting of an alkali metal ferrocyanide, ammonium ferrocyanide, an alkali metal nickelcyanide, ammonium nickelcyanide, an alkali metal cobaltcyanide, ammonium cobaltcyanide and mixtures thereof; and an alkanol amine for complexing a metal of the metal-cyano-complex, wherein the molar concentration of the alkanol amine is one to three times the molar concentration of the metal-cyano-complex.
Claim 27
Dependent Claim
35 words
An electroless copper plating bath, comprising: cupric ion; a cupric ion complexing agent for complexing cupric ion; a reducing agent; a metal cyano-complex stabilizer; and an alkanol amine for complexing the metal of said metal-cyano-complex:
Claim 28
Dependent Claim
35 words
An electroless copper plating bath, comprising: cupric ion; a cupric ion complexing agent for complexing cupric ion; a reducing agent; a metal cyano-complex stabilizer; and an alkanol amine for complexing the metal of said metal-cyano-complex:
Claim 29
Dependent Claim
28 words
The electroless copper plating bath according to claim 24, wherein the molar concentration of tbe alkanol amine is one to three times the molar concentration of a metal-cyano-complex.
Claim 30
Dependent Claim
40 words
The electroless copper plating bath according to claim 24, wherein the metal-cyano-complex stabilizer is selected from the group consisting of alkali metal ferrocyanide, ammonium ferrocyanide, an alkali metal nickelcyanide, ammonium nickelcyanide, an alkali metaL cobaltcyanide, ammonium colbaltcyanide and mixtures thereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-16 | 1990-09-15 | 1991-03-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-16 | 1994-09-15 | 1995-03-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-16 | 1998-09-15 | 1999-03-17 | $7700.00 | Window Closed / Lapsed |