Hydrofining process employing a phosphorus containing catalyst
Assignee: Phillips Petroleum Co
•
Filing: 1986-01-29
•
Granted: 1987-03-10
•
Expires: 2006-01-29
Abstract
Abstract A catalyst composition is prepared by dissolving a suitable oxygen containing compound of a Group VIB metal (preferably Mo), a suitable compound of a Group VIII metal (preferably Ni) and phosphorous acid in water, mixing this solution with an alumina containing support material, and calcining this mixture. This catalyst composition is used primarily for hydrotreating of hydrocarbon feed stream, which contain nitrogen and sulfur impurities, particularly heavy cycle oils.
Inventors
- 👤 Simon G. Kutes
- 👤 Stephen L. Parrott
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 10:00
CPC Classifications
C; C10; C10G; C10G45/00; C10G45/02; C10G45/04; C10G45/06; C10G45/08; B; B01; B01J; B01J27/00; B01J27/14; B01J27/186; B01J27/188
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
207 words
A process for hydrotreating a hydrocarbon containing feed stream comprising the step of intimately contacting a substantially liquid hydrocarbon containing feed stream, which also contains compounds of sulfur and nitrogen, with a free hydrogen containing gas and a catalyst composition under such hydrotreating conditions as to produce a hydrocarbon containing stream having reduced levels of sulfur and nitrogen, wherein said catalyst composition has been prepared by a process comprising the steps of: (A) mixing (a) at least one oxygen containing compound of a metal belonging to Group VIB of the Periodic Table, (b) at least one compound of a Group VIII metal selected from the group consisting of iron, cobalt and nickel, (c) phosphorous acid containing material, and (d) water, in such amounts and under such conditions as to obtain a solution; (B) mixing the solution obtained in step (A) with an alumina-containing support material; (C) heating the mixture obtained in step (B) at a first temperature under such conditions as to at least partially dry said mixture; and (D) heating the at least partially dried mixture obtained in step (C) in an inert, non-oxidizing and non-reducing atmosphere at a second temperature, which is higher than said first temperature, under such conditions as to activate said mixture.
Claim 2
Dependent Claim
207 words
A process for hydrotreating a hydrocarbon containing feed stream comprising the step of intimately contacting a substantially liquid hydrocarbon containing feed stream, which also contains compounds of sulfur and nitrogen, with a free hydrogen containing gas and a catalyst composition under such hydrotreating conditions as to produce a hydrocarbon containing stream having reduced levels of sulfur and nitrogen, wherein said catalyst composition has been prepared by a process comprising the steps of: (A) mixing (a) at least one oxygen containing compound of a metal belonging to Group VIB of the Periodic Table, (b) at least one compound of a Group VIII metal selected from the group consisting of iron, cobalt and nickel, (c) phosphorous acid containing material, and (d) water, in such amounts and under such conditions as to obtain a solution; (B) mixing the solution obtained in step (A) with an alumina-containing support material; (C) heating the mixture obtained in step (B) at a first temperature under such conditions as to at least partially dry said mixture; and (D) heating the at least partially dried mixture obtained in step (C) in an inert, non-oxidizing and non-reducing atmosphere at a second temperature, which is higher than said first temperature, under such conditions as to activate said mixture.
Claim 3
Dependent Claim
74 words
A process in accordance with claim 1, wherein said Group VIB metal is molybdenum, said Group VIII metal is nickel, said alumina-containing support material has a surface area in the range of from about 20 m 2 /g to about 350 m 2 /g, and said heating in step (D) is carried out in an inert gas selected from the group consisting of N 2 , He, Ne, Ar, Kr, Xe and mixtures thereof.
Claim 4
Dependent Claim
97 words
A process in accordance with claim 2, wherein said compound of molybdenum is selected from the group consisting of molybdenum oxides and hydroxides, molybdenum blue, ammonium and alkali metal orthomolybdates, ammonium and alkali metal dimolybdates, ammonium and alkali metal heptamolybdates, ammonium and alkali metal isomolybdates, phosphomolybdic acid and ammonium salts thereof; and said compound of nickel is selected from the group consisting of nickel(II) oxide, nickel(II) hydroxide, nickel(II) carbonate, nickel(II) hydrogen carbonate, basic nickel(II) carbonate, nickel(II) nitrate, nickel(II) sulfate, nickel(II) halides, nickel(II) acetate, nickel(II) formate, nickel(II) oxalate, nickel(II) carboxylates containing from 3-12 carbon atoms and nickel acetylacetonate.
Claim 5
Dependent Claim
28 words
A process in accordance with claim 2, wherein said solution obtained in step (A) comprises about 0.01-10.0 mole/l Mo, about 0.01-5.0 mole/l Ni and about 0.01-5.0 mole/l P.
Claim 6
Dependent Claim
56 words
A process in accordance with claim 2, wherein said oxygen containing compound of molybdenum is MoO 3 , said compound of nickel is NiCO 3 , and said phosphorous acid containing material is selected from the group consisting of H 3 PO 3 and mixtures of H 3 PO 3 and H 3 PO 4 .
Claim 7
Dependent Claim
28 words
A process in accordance with claim 5, wherein said solution obtained in step (A) comprises about 0.1-5.0 mole/l Mo, about 0.05-3.0 mole/l Ni and about 0.05-2.0 mole/l P.
Claim 8
Dependent Claim
75 words
A process in accordance with claim 2, wherein said catalyst composition comprises from about 0.2 to about 20 weight-% Mo, based on the weight of the entire catalyst composition; from about 0.2 to about 10 weight-% Ni, based on the entire catalyst composition; from about 0.2 to about 10 weight-% P, based on the entire catalyst composition; and has a surface area in the range of from about 20 to about 350 m 2 /g.
Claim 9
Dependent Claim
72 words
A process in accordance with claim 2, wherein said catalyst composition comprises from about 6.0 to about 15 weight-% Mo, based on the entire catalyst composition; from about 2.0 to about 6.0 weight-% Ni, based on the entire catalyst composition; from about 0.5 to about 3.0 weight-% P, based on the entire catalyst composition; and has a surface area in the range of from about 100 to about 250 m 2 /g.
Claim 10
Dependent Claim
30 words
A process in accordance with claim 1, wherein said hydrocarbon containing feed stream contains about 0.02-2 weight-% nitrogen and 0.1-5 weight-% sulfur, and has API 60 gravity of about 10-30.
Claim 11
Dependent Claim
23 words
A process in accordance with claim 9, wherein said hydrocarbon containing feed additionally contains about 5-500 ppmw vanadium and about 3-300 ppmw nickel.
Claim 12
Dependent Claim
45 words
A process in accordance with claim 9 wherein said hydrocarbon containing feed stream is selected from the group consisting of crude oil, crude oil fractions, petroleum products, heavy oil extracts, coal pyrolyrates, liquefied coal products, products from tar sand, shale oil and shale oil products.
Claim 13
Dependent Claim
17 words
A process in accordance with claim 11 wherein said hydrocarbon containing feed stream is heavy cycle oil.
Claim 14
Dependent Claim
83 words
A process in accordance with claim 1, wherein said hydrotreating conditions comprise a reaction temperature in the range of from about 250° to about 550° C., a reaction pressure in the range of from about 0 to 5,000 psig, a reaction time in the range of from about 0.05 to about 10 hours, and an amount of added hydrogen gas in the range of from about 100 to about 10,000 standard cubic feet H 2 per barrel of the hydrocarbon containing feed stream.
Claim 15
Dependent Claim
96 words
A process in accordance with claim 1 wherein said hydrotreating conditions comprise a reaction temperature in the range of from about 250° to about 550° C., a reaction pressure in the range of from about 0 to about 5,000 psig, a reaction time in the range of from about 0.05 to about 10 hours, and an amount of added hydrogen gas in the range of from about 100 to about 10,000 standard cubic feet H 2 per barrel of hydrocarbon containing feed stream; said Group VIB metal is molybdenum, and said Group VIII metal is nickel.
Claim 16
Dependent Claim
84 words
A process in accordance with claim 14, wherein said hydrotreating conditions comprise a reaction temperature in the range of from about 300° to about 450° C., a reaction pressure in the range of from about 100 to about 2,500 psig, a reaction time in the range of from about 0.25 to about 5 hours, and an amount of added hydrogen gas in the range of from about 1,000 to about 6,000 standard cubic feet H 2 per barrel of the hydrocarbon containing feed stream.
Claim 17
Dependent Claim
55 words
A process in accordance with claim 1, wherein the preparation of said catalyst composition further comprises a presulfiding step of: (F) contacting the material that has been heated in step (D) with a suitable sulfur compound under such conditions as to at least partially convert the transition metal compound contained in said material to sulfides.
Claim 18
Dependent Claim
35 words
A process in accordance with claim 1 further comprising the step of catalytically cracking said hydrocarbon containing stream having reduced levels of sulfur and nitrogen under such conditions as to produce lower boiling hydrocarbon materials.
Claim 19
Dependent Claim
36 words
A process in accordance with claim 1, wherein said hydrotreating process is carried out in the presence of a decomposable transition metal compound selected from the group consisting of molybdenum hexacarbonyl, molybdenum dithiophosphate and molybdenum dithiocarbamate.
References Cited (Backward Citations)
US3287280A
Cited
US3749664A
Cited
US3755150A
Cited
US3897365A
Cited
US3928176A
Cited
US4003828A
Cited
US4191635A
Cited
US4396500A
Cited
US4444905A
Cited
US4462897A
Cited
US4381993A
Cited
US4431527A
Cited
US4483764A
Cited
US4581129A
Cited
US4540483A
Cited
US4513097A
Cited
US4568449A
Cited
US4539101A
Cited
US4457835A
Cited
US4520128A
Cited
US4579649A
Cited
US4560468A
Cited
US4582594A
Cited
US4560466A
Cited
US4534852A
Cited
US4588706A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-09 | 1990-09-08 | 1991-03-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-09 | 1994-09-08 | 1995-03-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-09 | 1998-09-08 | 1999-03-10 | $7700.00 | Window Closed / Lapsed |