Method of making a double heterostructure laser
Assignee: RCA Corp
•
Filing: 1985-08-30
•
Granted: 1987-02-10
•
Expires: 2005-08-30
Abstract
Abstract A semiconductor laser comprising a substrate having a plurality of closely spaced channels in the surface thereof with mesas separating the channels to form a channelled region in the surface of the substrate. A first cladding layer overlies the surface of the substrate and the channels and has a surface layer over the channelled region which is not coplanar with the surface of this layer over the surrounding substrate. A cavity region comprising a guide layer and an active layer overlies the first cladding layer and a second cladding layer overlies the active layer. The active layer and guide layer taper in thickness in the lateral direction. The invention also includes a method of fabricating this laser which includes the steps of forming a plurality of corrugations in the surface of the substrate, forming a solution having a super-saturated growth condition for planar and concave surfaces and an under-saturated growth condition for convex surfaces, contacting the corrugated surface to the solution thereby partially melting the convex portions of the corrugations and forming mesas therebetween. Growth over the corrugations is delayed thereby providing a planar surface of the first layer over a central portion of the channelled region which is non-planar with respect to the surface of the layer over the remainder of the substrate. The trough thus formed by the delayed growth over the channelled region provides a curved surface upon which the remaining layers of the laser are then sequentially deposited.
Inventors
- 👤 John C. Connolly
- 👤 Dan Botez
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 11:24
CPC Classifications
H; H01; H01S; H01S5/00; H01S5/20; H01S5/22; H01S5/223; H01S5/2232; H01S5/2234; H01S5/2237; Y; Y10; Y10S; Y10S438/00; Y10S438/978
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
217 words
A method of fabricating a laser which includes a body of semiconductor material including end facets and a substrate, and having a guide layer and an active layer which taper in thickness in the lateral direction, which method comprises the steps of: forming a plurality of corrugations comprising adjacent vee-shaped channels in a major surface of the substrate and which extend between the end facets; forming a first solution, comprising the elements to be deposited and an element which is also a solvent for the substrate material, having a super-saturated growth condition for planar and concave surfaces and an under-saturated growth condition for convex surfaces; contacting the surface of the substrate having the corrugations therein to the first solution thereby causing a melting of the convex portions of the corrugations to form a plurality of mesas between the concave portions of the corrugations, wherein the surfaces of the mesas are below the surface of the substrate, thereby forming a trough in the surface of the substrate and causing deposition of a first layer to occur over the concave portions of the corrugations and the mesas and the surrounding substrate; and sequentially contacting the substrate with the first layer thereon to different solutions to deposit the remaining layers of the laser over the surface of the first layer.
Claim 2
Independent Claim
217 words
A method of fabricating a laser which includes a body of semiconductor material including end facets and a substrate, and having a guide layer and an active layer which taper in thickness in the lateral direction, which method comprises the steps of: forming a plurality of corrugations comprising adjacent vee-shaped channels in a major surface of the substrate and which extend between the end facets; forming a first solution, comprising the elements to be deposited and an element which is also a solvent for the substrate material, having a super-saturated growth condition for planar and concave surfaces and an under-saturated growth condition for convex surfaces; contacting the surface of the substrate having the corrugations therein to the first solution thereby causing a melting of the convex portions of the corrugations to form a plurality of mesas between the concave portions of the corrugations, wherein the surfaces of the mesas are below the surface of the substrate, thereby forming a trough in the surface of the substrate and causing deposition of a first layer to occur over the concave portions of the corrugations and the mesas and the surrounding substrate; and sequentially contacting the substrate with the first layer thereon to different solutions to deposit the remaining layers of the laser over the surface of the first layer.
Claim 3
Dependent Claim
33 words
The method of claim 1 wherein the step of forming the solution comprises the steps of equilibrating the first solution at an equilibration temperature and cooling the first solution to a lower temperature.
Claim 4
Dependent Claim
13 words
The method of claim 2 wherein the substrate is at said lower temperature.
Claim 5
Dependent Claim
19 words
The method of claim 3 wherein the substrate is GaAs, and the first solution includes aluminum, arsenic and gallium.
Claim 6
Dependent Claim
33 words
The method of claim 4 wherein said lower temperature at which the first solution in contact with a planar portion of the surface is saturated is between about 700° C. and 800° C.
Claim 7
Dependent Claim
13 words
The method of claim 5 wherein said lower temperature is about 760° C.
Claim 8
Dependent Claim
34 words
The method of claim 5 wherein the difference between said equilibration and lower temperatures is between about 2° and 10° C. and the cooling rate is between about 0.5° and 5° C. per minute.
Claim 9
Dependent Claim
25 words
The method of claim 7 wherein said difference is between about 4° and 5° C. and the cooling rate is about 1° C. per minute.
Claim 10
Dependent Claim
13 words
The method of claim 1 wherein the corrugations are adjacent to one another.
Claim 11
Independent Claim
189 words
A method of locally delaying the deposition of a layer on a surface of a body comprising the steps of: forming a plurality of corrugations on the surface comprising adjacent vee-shaped channels; forming a first solution, comprising the elements to be deposited and an element which is a solvent for the material of the body, having a super-saturated growth condition for planar and concave portions of the surface and an under-saturated growth condition for convex portions of the surface of the substrate; contacting the surface having the corrugations therein to the first solution thereby causing a melting of the convex portions of the corrugations to form a plurality of mesas between the concave portions, wherein the surfaces of the mesas are below the surface of the substrate, thereby forming a trough in the surface of the substrate and causing deposition of the layer to occur over the concave portions of the corrugations and the mesas and the surrounding substrate; whereby the initial rate of deposition of the layer over the corrugated portion of the surface is less than the rate of deposition over the uncorrugated portion of the substrate.
Claim 12
Independent Claim
189 words
A method of locally delaying the deposition of a layer on a surface of a body comprising the steps of: forming a plurality of corrugations on the surface comprising adjacent vee-shaped channels; forming a first solution, comprising the elements to be deposited and an element which is a solvent for the material of the body, having a super-saturated growth condition for planar and concave portions of the surface and an under-saturated growth condition for convex portions of the surface of the substrate; contacting the surface having the corrugations therein to the first solution thereby causing a melting of the convex portions of the corrugations to form a plurality of mesas between the concave portions, wherein the surfaces of the mesas are below the surface of the substrate, thereby forming a trough in the surface of the substrate and causing deposition of the layer to occur over the concave portions of the corrugations and the mesas and the surrounding substrate; whereby the initial rate of deposition of the layer over the corrugated portion of the surface is less than the rate of deposition over the uncorrugated portion of the substrate.
Claim 13
Dependent Claim
33 words
The method of claim 10 wherein the step of forming the solution comprises the steps of equilibrating the first solution at an equilibration temperature and cooling the first solution to a lower temperature.
Claim 14
Dependent Claim
13 words
The method of claim 11 wherein the substrate is at said lower temperature.
Claim 15
Dependent Claim
19 words
The method of claim 12 wherein the substrate is GaAs, and the first solution includes aluminum, arsenic and gallium.
Claim 16
Dependent Claim
31 words
The method of claim 13 wherein said lower temperature at which the first solution in contact with a planar portion of the surface is saturated is between 700° and 800° C.
Claim 17
Dependent Claim
13 words
The method of claim 14 wherein said lower temperature is about 760° C.
Claim 18
Dependent Claim
34 words
The method of claim 14 wherein the difference between the equilibration and lower temperatures is between about 2° and 10° C. and the cooling rate is between about 0.5° and 5° C. per minute.
Claim 19
Dependent Claim
25 words
The method of claim 16 wherein said difference is between about 4° and 5° C. and the cooling rate is about 1° C. per minute.
Claim 20
Dependent Claim
13 words
The method of claim 10 wherein the corrugations are adjacent to one another.
References Cited (Backward Citations)
US3701047A
Cited
US3741825A
Cited
US3753801A
Cited
US4073676A
Cited
US3960618A
Cited
US4023993A
Cited
US3978428A
Cited
US4178564A
Cited
US4092659A
Cited
US4255717A
Cited
US4321556A
Cited
US4280106A
Cited
US4302729A
Cited
US4347486A
Cited
US4383320A
Cited
US4373989A
Cited
US4547396A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-02-09 | 1990-08-11 | 1991-02-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-02-09 | 1994-08-11 | 1995-02-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-02-09 | 1998-08-11 | 1999-02-10 | $7700.00 | Window Closed / Lapsed |