Aluminate phosphor
Assignee: General Electric Co
•
Filing: 1985-03-25
•
Granted: 1986-12-23
•
Expires: 2005-03-25
Abstract
Abstract A class of non-stoichiometric class of cerium and terbium co-activated magnesium aluminate phosphors is disclosed which are particularly useful in low pressure type fluorescent lamps. Said phosphor materials can be further combined with other phosphors to produce white color illumination in said type lamps. A general method for preparation of said phosphor materials is disclosed wherein the emission characteristics can be regulated to advantage.
Inventors
- 👤 William W. Beers
- 👤 Thomas G. Parham
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 22:58
CPC Classifications
H; H01; H01J; H01J61/00; H01J61/02; H01J61/38; H01J61/42; H01J61/44; C; C09; C09K; C09K11/00; C09K11/08; C09K11/77; C09K11/7766; C09K11/7774
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
118 words
A fluorescent lamp phosphor comprising a plurality of fine-sized crystals having the general formula: Ce.sub.1-x-y La.sub.x Tb.sub.y Mg.sub.z Al.sub.11 O.sub.19 wherein La is an optional constituent and x is in an amount up to about 0.50, y is in the range from about 0.20 up to about 0.50, and z is in the range from about 0.60 up to about 0.87, said crystals having a median particle size of about 5.0 microns diameter and being further characterized by a ratio between its 544 nanometers wavelength peak emission to its 490 nanometers wavelength peak emission of at least 5.0 along with exhibiting trichromatic coordinate values in the range X=0.3190-0.3202 and Y=0.5377-0.5402 in a low pressure mercury vapor discharge lamp.
Claim 2
Dependent Claim
118 words
A fluorescent lamp phosphor comprising a plurality of fine-sized crystals having the general formula: Ce.sub.1-x-y La.sub.x Tb.sub.y Mg.sub.z Al.sub.11 O.sub.19 wherein La is an optional constituent and x is in an amount up to about 0.50, y is in the range from about 0.20 up to about 0.50, and z is in the range from about 0.60 up to about 0.87, said crystals having a median particle size of about 5.0 microns diameter and being further characterized by a ratio between its 544 nanometers wavelength peak emission to its 490 nanometers wavelength peak emission of at least 5.0 along with exhibiting trichromatic coordinate values in the range X=0.3190-0.3202 and Y=0.5377-0.5402 in a low pressure mercury vapor discharge lamp.
Claim 3
Dependent Claim
28 words
A phosphor as in claim 1 having the general formula: Ce.sub.0.65 Tb.sub.0.35 Mg.sub.z Al.sub.11 O.sub.19 wherein z is in the range from about 0.60 up to about 0.87.
Claim 4
Dependent Claim
12 words
A phosphor as in claim 1 having essentially no secondary alumina phase.
Claim 5
Dependent Claim
26 words
A phosphor as in claim 1 having its principal visible emission in the wavelength range from about 520 nanometers wavelength up to about 565 nanometers wavelength.
Claim 6
Dependent Claim
21 words
A phosphor as in claim 1 having trichromatic coordinates of approximately X=0.320 and Y=0.540 when excited by 254 nanometers ultraviolet radiation.
Claim 7
Independent Claim
175 words
A method for the preparation of a phosphor in the form of a plurality of fine-sized crystals having the general formula: Ce.sub.1-x-y La.sub.x Tb.sub.y Mg.sub.z Al.sub.11 O.sub.19 wherein La is an optional constituent and x is in an amount up to about 0.50, y is in the range from about 0.20 up to about 0.50, and z is in the range from about 0.60 up to about 0.87, said crystals having a median particle size of about 5.0 microns diameter and being further characterized by a ratio between its 544 nanometers wavelength peak emission to its 490 nanometers wavelength peak emission of at least 5.0 which comprises (1) mixing a batch of ingredients which will yield said phosphor material upon firing wherein the batch proportions of all metal ions are as set forth in said formula, and (2) firing the batch at a temperature range from about 1400° C. up to about 1600° C. for a time period up to about 4 hours in a reducing atmosphere containing up to 5% hydrogen chloride by volume.
Claim 8
Independent Claim
175 words
A method for the preparation of a phosphor in the form of a plurality of fine-sized crystals having the general formula: Ce.sub.1-x-y La.sub.x Tb.sub.y Mg.sub.z Al.sub.11 O.sub.19 wherein La is an optional constituent and x is in an amount up to about 0.50, y is in the range from about 0.20 up to about 0.50, and z is in the range from about 0.60 up to about 0.87, said crystals having a median particle size of about 5.0 microns diameter and being further characterized by a ratio between its 544 nanometers wavelength peak emission to its 490 nanometers wavelength peak emission of at least 5.0 which comprises (1) mixing a batch of ingredients which will yield said phosphor material upon firing wherein the batch proportions of all metal ions are as set forth in said formula, and (2) firing the batch at a temperature range from about 1400° C. up to about 1600° C. for a time period up to about 4 hours in a reducing atmosphere containing up to 5% hydrogen chloride by volume.
Claim 9
Dependent Claim
21 words
A method as in claim 6 wherein the reducing atmosphere comprises forming gas containing up to 5% hydrogen chloride by volume.
Claim 10
Dependent Claim
14 words
A method as in claim 6 wherein the batch ingredients are all metal oxides.
Claim 11
Independent Claim
215 words
A method for the preparation of a phosphor in the form of a plurality of fine-sized crystals having the general formula: Ce.sub.1-x-y La.sub.x Tb.sub.y Mg.sub.z Al.sub.11 O.sub.19 wherein La in an optional constituent and x is in an amount up to about 0.50, y is in the range from about 0.20 up to about 0.50, and z is in the range from about 0.60 up to about 0.87, said crystals having a median particle size of up to about 5.0 and being further characterized by a ratio between its 544 nanometers wavelength peak emission to its 490 nanometers wavelength peak emission of at least 5.0 which comprises (1) mixing a batch of ingredients which will yield said phosphor material upon firing wherein the batch proportions of all metal ions are as set forth in said formula, (2) heating the batch to a temperature in the range from about 1400° C. up to about 1600° C. and firing said batch at said temperature for a time period up to about 4 hours in a reducing atmosphere containing up to 5% hydrogen chloride by volume, and (3) withholding the introduction of hydrogen chloride into the reducing atmosphere until the heating temperature has reached at least 1200° C. to minimize formation of secondary alumina phases in said phosphor.
Claim 12
Independent Claim
215 words
A method for the preparation of a phosphor in the form of a plurality of fine-sized crystals having the general formula: Ce.sub.1-x-y La.sub.x Tb.sub.y Mg.sub.z Al.sub.11 O.sub.19 wherein La in an optional constituent and x is in an amount up to about 0.50, y is in the range from about 0.20 up to about 0.50, and z is in the range from about 0.60 up to about 0.87, said crystals having a median particle size of up to about 5.0 and being further characterized by a ratio between its 544 nanometers wavelength peak emission to its 490 nanometers wavelength peak emission of at least 5.0 which comprises (1) mixing a batch of ingredients which will yield said phosphor material upon firing wherein the batch proportions of all metal ions are as set forth in said formula, (2) heating the batch to a temperature in the range from about 1400° C. up to about 1600° C. and firing said batch at said temperature for a time period up to about 4 hours in a reducing atmosphere containing up to 5% hydrogen chloride by volume, and (3) withholding the introduction of hydrogen chloride into the reducing atmosphere until the heating temperature has reached at least 1200° C. to minimize formation of secondary alumina phases in said phosphor.
Claim 13
Dependent Claim
14 words
A method as in claim 9 wherein the batch ingredients are all metal oxides.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-22 | 1990-06-23 | 1990-12-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-22 | 1994-06-23 | 1994-12-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-22 | 1998-06-23 | 1998-12-23 | $7700.00 | Window Closed / Lapsed |