Method of preparing cerium and terbium activated aluminate phosphors
Assignee: EMI Group Ltd
•
Filing: 1977-02-07
•
Granted: 1978-06-20
•
Expires: 1997-02-07
Abstract
Abstract Phosphors having useful flourescent emission properties comprise aluminates of magnesium, zinc and/or lithium having an hexagonal or so-called "β-alumina" crystal structure and activated by cerium and terbium. In preferred phosphors the ratio of Mg:Al is from 0.01 to 0.5:1, Ce:Al from 0.001 to 0.1:1 and Tb:Al from 0.005:1 to 0.25:1. Where zinc or lithium wholly or partially replace the magnesium, chemically equivalent amounts may be used. A particuarly useful phosphor conforms substantially to the approximate formula (Ce,Tb) 1 Mg 1-2 Al 22 O x , where x is the number of atoms of oxygen required to satisfy the valencies of the metals. The invention also provides a valuable process for the preparation of such aluminate phosphors, giving a product of fine grain which may not require milling or other severe grinding (which is expensive and tends to harm emission properties) to bring it into the preferred particle size range for lamp manufacture. In this process the source of alumina is aluminium ammonium sulphate (ammonium alum) and this is mixed with oxides of the other constituent metals (or decomposable compounds thereof) and fired at temperatures above 1200° C and preferably at 1450° C and even higher. An increase in brightness may be obtained by a final heating in hydrogen in the region of 1050° C.
Inventors
- 👤 Peter Whitten Ranby
- 👤 Doreen Yvonne Hobbs
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 13:25
CPC Classifications
C; C09; C09K; C09K11/00; C09K11/08; C09K11/77; C09K11/7766; C09K11/7774
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
103 words
A method of making a magnesium, zinc and/or lithium aluminate phosphor activated by cerium and terbium and having a hexagonal (β-alumina) crystal structure, which comprises preparing a mixture of aluminum ammonium sulfate and the oxides of the magnesium, zinc and/or lithium and of the cerium and the terbium, or compounds which thermally decompose to such oxides and volatile components, and heating the mixture in air to a temperature above 1200° C, said phosphor having a ratio of Mg, Zn and/or Li 2 :Al of from 0.01 to 0.5:1, of Ce:Al of from 0.001 to 0.1:1 and of Tb:Al of from 0.005 to 0.25:1.
Claim 2
Independent Claim
103 words
A method of making a magnesium, zinc and/or lithium aluminate phosphor activated by cerium and terbium and having a hexagonal (β-alumina) crystal structure, which comprises preparing a mixture of aluminum ammonium sulfate and the oxides of the magnesium, zinc and/or lithium and of the cerium and the terbium, or compounds which thermally decompose to such oxides and volatile components, and heating the mixture in air to a temperature above 1200° C, said phosphor having a ratio of Mg, Zn and/or Li 2 :Al of from 0.01 to 0.5:1, of Ce:Al of from 0.001 to 0.1:1 and of Tb:Al of from 0.005 to 0.25:1.
Claim 3
Dependent Claim
16 words
A method according to claim 1 wherein the mixture is heated to at least 1450° C.
Claim 4
Dependent Claim
46 words
A method according to claim 2 wherein the mixture is subjected to two stages of heating at 1450° C or above by first heating to at least 1450° C in air, grinding the mixture, and again heating the mixture to at least 1450° C in air.
Claim 5
Dependent Claim
31 words
A method according to claim 2 wherein the mixture is initially heated in the temperature range 1000°-1100° C in air, ground, and then heated to at least 1450° C in air.
Claim 6
Dependent Claim
22 words
A method according to claim 2 wherein the heated product is thereafter subjected to a final heating in hydrogen at 1000°-1100° C.
Claim 7
Dependent Claim
86 words
The method of claim 1, wherein the phosphor has the formula (Ce, Tb).sub.z A.sub.y Al.sub.22 O.sub.x wherein z is the combined total amount of cerium and terbium and has a value of 0.3-2.2; A is selected from Mg, Zn, Li 2 and mixtures thereof; y has a value of from 0.9-2.2; and x is the number of atoms of oxygen required to satisfy the valencies of the constituent metals, calculated on the basis of trivalent Ce, Tb and Al, divalent Mg and Zn, and monovalent Li.
Claim 8
Dependent Claim
13 words
The method of claim 1, wherein the mixture is heated for 1 hour.
Claim 9
Dependent Claim
36 words
The method of claim 3, wherein the mixture is first heated to at least 1450° C in air, cooled, subjected to mild grinding to break down agglomerates, and reheated in air to at least 1450° C.
Claim 10
Dependent Claim
28 words
The method of claim 8, wherein the first heating is conducted for about one hour in air and the reheating is conducted for about 1 hour in air.
Claim 11
Independent Claim
171 words
A method for preparing luminescent material having the following formula: (Ce,Tb).sub.z A.sub.y Al.sub.22 O.sub.x wherein z is the combined total amount of cerium and terbium and has a value of about 1; A is selected from Mg, Zn, Li 2 and mixtures thereof; y has a value of from about 0.9-2.2; and x is the number of atoms of oxygen required to satisfy the valencies of the constituent metals, calculated on the basis of trivalent Ce, Tb and Al, divalent Mg and Zn, and monovalent Li; said material having a hexagonal (β-alumina) crystal structure, and having an ultimate particle size as prepared and without harmful milling, of about 3 to 30 microns, said cerium and terbium being present in a ratio of about 0.47 atoms of cerium per 0.53 atoms of terbium, comprising preparing a mixture of aluminum ammonium sulfate and the oxides of the other constituent metals, or compounds which thermally decompose to such oxides and volatile components, and heating the mixture to a temperature above 1200° C in air.
Claim 12
Independent Claim
171 words
A method for preparing luminescent material having the following formula: (Ce,Tb).sub.z A.sub.y Al.sub.22 O.sub.x wherein z is the combined total amount of cerium and terbium and has a value of about 1; A is selected from Mg, Zn, Li 2 and mixtures thereof; y has a value of from about 0.9-2.2; and x is the number of atoms of oxygen required to satisfy the valencies of the constituent metals, calculated on the basis of trivalent Ce, Tb and Al, divalent Mg and Zn, and monovalent Li; said material having a hexagonal (β-alumina) crystal structure, and having an ultimate particle size as prepared and without harmful milling, of about 3 to 30 microns, said cerium and terbium being present in a ratio of about 0.47 atoms of cerium per 0.53 atoms of terbium, comprising preparing a mixture of aluminum ammonium sulfate and the oxides of the other constituent metals, or compounds which thermally decompose to such oxides and volatile components, and heating the mixture to a temperature above 1200° C in air.
References Cited (Backward Citations)
GB689683A
Cited
DE2353943A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-19 | 1981-12-19 | 1982-06-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-19 | 1985-12-19 | 1986-06-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-19 | 1989-12-19 | 1990-06-20 | $7700.00 | Window Closed / Lapsed |