Asphalt surfacing mass
Assignee: LAXA BRUK BOX 111 S-C695 01 LAXA AB
•
Filing: 1985-08-12
•
Granted: 1986-09-23
•
Expires: 2005-08-12
Abstract
Abstract A surfacing mass especially for outdoor use and mainly comprising a mixture of asphalt and a stone material having a low content of fine material. The mixture comprises a little amount of fibres of a type which is not solved or softens in the asphalt, preferably mineral fibres. The fibre material has an average diameter of between 1 and 5 μm and is added in an amount of between 0.5 and 20% by weight calculated on the amount of asphalt. The invention also relates to a method of manufacturing such surfacing mass at a mixing temperature of 140°-170° C. or preferably 150°-160° C. both for the asphalt and the stone mass. Preferably the fibre material is admixed in the asphalt before the mixing thereof with the stone material. The fibre material may be admixed in the asphalt at an asphalt temperature which is higher than the mixing temperature for asphalt and stone material.
Inventors
- 👤 Nils-Olov Nilsson
- 👤 Ingmar Andersson
- 👤 Ulrik Sandberg
- 👤 Eils Karlsson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 21:12
CPC Classifications
E; E01; E01C; E01C11/00; E01C11/16; E01C11/165; C; C08; C08L; C08L95/00
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
120 words
A surfacing mass for streets, roads, parking places and the like having a draining activity comprising a mixture of a stone material, asphalt, and about 0.5 to 20% by weight of fibers having an average fiber diameter of about 1 and 5 μm, said fibers being pretreated with a cationic tenside wetting agent and said stone material comprising a course portion of material and a small portion of fine material in proportions that provide a surfacing mass having communicating cavities for draining, whereby the stone material mainly comprises stone particles having an average diameter of between 2 and 12 mm and in which about 50% of the stone material has an average particle size of between 8 and 12 mm.
Claim 2
Dependent Claim
120 words
A surfacing mass for streets, roads, parking places and the like having a draining activity comprising a mixture of a stone material, asphalt, and about 0.5 to 20% by weight of fibers having an average fiber diameter of about 1 and 5 μm, said fibers being pretreated with a cationic tenside wetting agent and said stone material comprising a course portion of material and a small portion of fine material in proportions that provide a surfacing mass having communicating cavities for draining, whereby the stone material mainly comprises stone particles having an average diameter of between 2 and 12 mm and in which about 50% of the stone material has an average particle size of between 8 and 12 mm.
Claim 3
Dependent Claim
77 words
Method of manufacturing the surface mass of claim 1 having draining activity comprising mixing a stone material with asphalt at a temperature of 140°-170° C. in the presence of 0.5-20% by weight of a fiber material of a type which does not dissolve or soften in the asphalt, said stone material comprising a course portion of material and a small portion of fine material in proportions that provide a surfacing mass having communicating cavities therein for draining.
Claim 4
Dependent Claim
52 words
Method according to claim 2, wherein the fiber material is a mineral fiber having an average diameter which is less than 5 μm and larger than 1 μm, and in that the mineral fibers are admixed so as to become substantially evenly distributed and separated from each other in the asphalt phase.
Claim 5
Dependent Claim
23 words
Method according to claim 2, wherein the fiber material is admixed in the asphalt before the asphalt is mixed with the stone material.
Claim 6
Dependent Claim
27 words
Method according to any of claims 4, wherein the fiber material is treated with a wetting agent before the fiber material is admixed in the asphalt phase.
Claim 7
Dependent Claim
21 words
Method according to any of claims 5 wherein the fiber material is completely dried before being admixed in the asphalt phase.
Claim 8
Dependent Claim
61 words
Method according to claim 5 wherein the asphalt is heated to a temperature of about 20°-40° C. over the mixing temperature for asphalt and stone material before the fiber material is admixed in the asphalt, and in that the mixture of asphalt and fiber material is cooled to the temperature of the stone material and is mixed with the stone material.
References Cited (Backward Citations)
US3617329A
Cited
US3615804A
Cited
US3868263A
Cited
US3870426A
Cited
US3808164A
Cited
US4052219A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-09-22 | 1990-03-24 | 1990-09-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-09-22 | 1994-03-24 | 1994-09-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-09-22 | 1998-03-24 | 1998-09-23 | $7700.00 | Window Closed / Lapsed |