Stable ohmic contacts for gallium arsenide semiconductors
Assignee: University of Dayton
•
Filing: 1984-10-17
•
Granted: 1986-02-18
•
Expires: 2004-10-17
Abstract
Abstract Ohmic contacts are formed on an n-type gallium arsenide semiconductor by applying a layer of nickel to a contact surface of the semiconductor, bombarding the nickel layer with a beam of germanium ions to drive nickel and germanium atoms into the contact area of the semiconductor, annealing the semiconductor by means of lamp annealing techniques, and then forming a layer of gold to at least a portion of the irradiated nickel layer to facilitate connection of an electrical conductor thereto. Tellerium may be used in place of germanium for n-type semiconductors. For p-type gallium arsenide semiconductors, ohmic contacts may be formed by bombarding a nickel layer with either zinc or copper ions.
Inventors
- 👤 Steven R. Smith
- 👤 James S. Solomon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 16:39
CPC Classifications
H; H10; H10D; H10D62/00; H10D62/80; H10D62/85; H10D64/00; H10D64/01; H10D64/011; H10D64/0116; H10D64/60; H10D64/62
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
147 words
A method of making an ohmic contact to a gallium arsenide semiconductor comprising the following steps: applying a layer of nickel to a selected contact area of a surface of said semiconductor; irradiating at least a portion of said nickel layer with ions of an electrically active material whereby atoms of nickel and atoms of said electrically active material are driven into said semiconductor to form an ohmic contact to said semiconductor; transient annealing said semiconductor; and applying a layer of gold to at least a portion of the irradiated portion of said nickel layer to facilitate connection of an electrical conductor thereto whereby said nickel layer forms a boundary between said gold layer and said semiconductor to prevent the diffusion of said gold to the surface of said semiconductor and the resultant formation of a rectifying barrier which would destroy the ohmic nature of said contact.
Claim 2
Independent Claim
147 words
A method of making an ohmic contact to a gallium arsenide semiconductor comprising the following steps: applying a layer of nickel to a selected contact area of a surface of said semiconductor; irradiating at least a portion of said nickel layer with ions of an electrically active material whereby atoms of nickel and atoms of said electrically active material are driven into said semiconductor to form an ohmic contact to said semiconductor; transient annealing said semiconductor; and applying a layer of gold to at least a portion of the irradiated portion of said nickel layer to facilitate connection of an electrical conductor thereto whereby said nickel layer forms a boundary between said gold layer and said semiconductor to prevent the diffusion of said gold to the surface of said semiconductor and the resultant formation of a rectifying barrier which would destroy the ohmic nature of said contact.
Claim 3
Dependent Claim
27 words
The method as claimed in claim 1 further comprising the step of applying an additional layer of nickel to said selected contact area after annealing said semiconductor.
Claim 4
Dependent Claim
19 words
The method as claimed in claim 2 wherein said semiconductor is n-type and said electrically active material comprises germanium.
Claim 5
Dependent Claim
19 words
The method as claimed in claim 2 wherein said semiconductor is n-type and said electrically active material comprises tellerium.
Claim 6
Dependent Claim
19 words
The method as claimed in claim 2 wherein said semiconductor is p-type and said electrically active material comprises zinc.
Claim 7
Dependent Claim
19 words
The method as claimed in claim 2 wherein said semiconductor is p-type and said electrically active material comprises copper.
Claim 8
Dependent Claim
23 words
The method as claimed in claim 3 wherein the step of transient annealing comprises annealing for a period of 15 to 20 seconds
Claim 9
Dependent Claim
23 words
The method as claimed in claim 4 wherein the step of transient annealing comprises annealing for a period of 15 to 20 seconds.
Claim 10
Dependent Claim
23 words
The method as claimed in claim 5 wherein the step of transient annealing comprises annealing for a period of 15 to 20 seconds.
Claim 11
Dependent Claim
23 words
The method as claimed in claim 6 wherein the step of transient annealing comprises annealing for a period of 15 to 20 seconds.
References Cited (Backward Citations)
US3245848A
Cited
US3600797A
Cited
US3532562A
Cited
US4033788A
Cited
US4265934A
Cited
US4188710A
Cited
US4330343A
Cited
US4377030A
Cited
US4298403A
Cited
US4398963A
Cited
US4426765A
Cited
US4426767A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-02-17 | 1989-08-19 | 1990-02-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-02-17 | 1993-08-19 | 1994-02-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-02-17 | 1997-08-19 | 1998-02-18 | $7700.00 | Window Closed / Lapsed |