US4552615A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for forming a high density metallurgy system on a substrate and structure thereof
Assignee: International Business Machines Corp
•
Filing: 1984-05-21
•
Granted: 1985-11-12
•
Expires: 2004-05-21
Abstract
Abstract A process for forming a top surface metallurgy pattern on a green unsintered ceramic substrate including the steps of forming indented lines on the surface of the substrate, sintering the substrate, depositing a blanket layer over the top surface of the substrate with a thickness less than the depth of the indented lines, applying a masking layer over the metal layer, removing the masking layer over all portions except the indented lines, removing the exposed areas of the metal layer, and removing the remaining portions of the masking layer.
Inventors
- 👤 Albert Amendola
- 👤 Arnold F. Schmeckenbecher
- 👤 Joseph T. Sobon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 15:24
CPC Classifications
H; H10; H10W; H10W70/00; H10W70/01; H10W70/05; H05; H05K; H05K3/00; H05K3/02; H05K3/06; H05K3/061; H05K3/10; H05K3/107; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K1/09; H05K1/092; H05K1/11; H05K1/111; H05K1/112; H05K1/113; H05K2201/00; H05K2201/03; H05K2201/0302; H05K2201/0317; H05K2201/09; H05K2201/09009; H05K2201/09036; H05K2203/00; H05K2203/01; H05K2203/0104; H05K2203/0108; H05K2203/02; H05K2203/025; H05K2203/07; H05K2203/0756; H05K2203/0759; H05K2203/0769; H05K3/14; H05K3/146; H05K3/38; H05K3/388; H05K3/46; H05K3/4611; H05K3/4626; H05K3/4629; H05K3/4644; H05K3/467; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49155; Y10T29/49163
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
243 words
A process for forming a top surface metallurgy pattern on a ceramic substrate comprising providing an unsintered green ceramic substrate, forming indented lines in the surface of the ceramic substrate that defines the desired surface metallurgy pattern, sintering the ceramic substrate, depositing a substantially uniform blanket metal layer of at least one metal over at least a portion of the surface of the ceramic substrate including said indented lines, the thickness of said metal layer being less than the depth of said indented lines, the metal being relatively thin on the side walls of the indented lines, applying a masking layer of material of a thickness in excess of the depth of said indented lines over the metal layer, which material of said masking layer is resistant to an etchant of the metal of the metal layer, and presents a relatively planar top surface, reducing the thickness of said masking layer by removing a relatively uniform layer portion from the surface, thereby exposing the metal layer portions that overlie the upper surface of said substrate, but leaving intact the masking layer portions overlying the metal layer portions in the indented lines, exposing the top surface of said ceramic substrate to an etchant for the metal of the metal layer thereby removing the exposed metal areas but leaving intact the metal layer portions in the indented lines that are covered by said masking layer portions, and removing the remaining portions of the masking layer.
Claim 2
Dependent Claim
243 words
A process for forming a top surface metallurgy pattern on a ceramic substrate comprising providing an unsintered green ceramic substrate, forming indented lines in the surface of the ceramic substrate that defines the desired surface metallurgy pattern, sintering the ceramic substrate, depositing a substantially uniform blanket metal layer of at least one metal over at least a portion of the surface of the ceramic substrate including said indented lines, the thickness of said metal layer being less than the depth of said indented lines, the metal being relatively thin on the side walls of the indented lines, applying a masking layer of material of a thickness in excess of the depth of said indented lines over the metal layer, which material of said masking layer is resistant to an etchant of the metal of the metal layer, and presents a relatively planar top surface, reducing the thickness of said masking layer by removing a relatively uniform layer portion from the surface, thereby exposing the metal layer portions that overlie the upper surface of said substrate, but leaving intact the masking layer portions overlying the metal layer portions in the indented lines, exposing the top surface of said ceramic substrate to an etchant for the metal of the metal layer thereby removing the exposed metal areas but leaving intact the metal layer portions in the indented lines that are covered by said masking layer portions, and removing the remaining portions of the masking layer.
Claim 3
Dependent Claim
61 words
The process of claim 1 wherein said green ceramic substrate is a laminated multi-layer substrate including an internal metallurgy system that includes metal filled vias that extend through at least the upper laminated sheet of the substrate, and said indented lines that define the desired surface metallurgy pattern being in alignment with and selectively overlying in part said metal filled vias.
Claim 4
Dependent Claim
35 words
The process of claim 2 wherein said indented lines that least define a fan-out metallurgy pattern for an I/O solder pad configuration for interconnecting a semiconductor device to the internal metallurgy system of said substrate.
Claim 5
Dependent Claim
20 words
The process of claim 3 wherein said fan-out metallurgy pattern of indented lines include enlarged areas defining engineering change pads.
Claim 6
Dependent Claim
51 words
The process of claim 2 wherein said internal metallurgy system is formed of a refractory metal selected from the group consisting of Mo, Ta and W, and mixtures thereof, and said surface metal layer is a high conductivity metal selected from the group consisting of Cu, Ag, Au, and alloys thereof.
Claim 7
Dependent Claim
34 words
The process of claim 3 wherein said indented lines include small unconnected areas overlying a single metal filled via, which unconnected area defines a power pad for powering the device to be connected thereto.
Claim 8
Dependent Claim
54 words
The process of claim 1 wherein said indented lines defining the surface metallurgy pattern is formed by heating the substrate to a temperature that softens the resin in the green ceramic material of the substrate, and an embossed die defining the desired surface metallurgy pattern is pressed against the top surface of the substrate.
Claim 9
Dependent Claim
26 words
The process of claim 1 wherein said temperature is at least the softening temperature of the resin used in the green ceramic material of the substrate.
Claim 10
Dependent Claim
30 words
The process of claim 8 wherein the green ceramic material of said substrate includes polyvinyl butyral resin material and said temperature is in the range of 75° to 95° C.
Claim 11
Dependent Claim
46 words
The process of claim 1 wherein the green ceramic material of said substrate includes alumina with an average particle diameter size in the range of 2 μm to 8 μm, and the width of said indented lines is approximately three times the diameter of the particles.
Claim 12
Dependent Claim
26 words
The process of claim 10 wherein the depth of said indented lines of said surface metallurgy pattern is in the range of 0.5 to 2 mils.
Claim 13
Dependent Claim
18 words
The process of claim 1 wherein said uniform metal layer is comprised of a plurality of metal layers.
Claim 14
Dependent Claim
32 words
The process of claim 12 wherein said metal layer is comprised of a first layer of Cr, a second intermediate relatively thick layer of Cu, and a thin overlying layer of Au.
Claim 15
Dependent Claim
31 words
The process of claim 1 wherein said metal layer is deposited by vapor deposition techniques, which leave a relatively thin layer of metal on the side walls of the indented pattern.
Claim 16
Dependent Claim
31 words
The process of claim 1 wherein said metal layer is deposited by gravity settling techniques, which leave a relatively thin layer of metal on the side walls of the indented pattern.
Claim 17
Dependent Claim
60 words
The process of claim 3 which further includes placing a block-out mask on the surface of said substrate having openings that expose the areas designated as I/O solder pads, depositing a relatively thick layer of solder on the block-out mask and through the openings on the substrate, and heating the substrate to re-form the deposited solder into I/O solder mounds.
Claim 18
Dependent Claim
46 words
The process of claim 4 which further includes placing a block-out mask on the surface of said substrate having openings that expose the areas designated as engineering change pads, and depositing a layer of Au on the block-out mask and through the openings on the substrate.
Claim 19
Dependent Claim
48 words
The process of claim 1 wherein the green ceramic material of said substrate is a glass-ceramic mixture having a coefficient of expansion that substantially matches the coefficient of expansion of Si, and a low sintering temperature that permits the use of non-refractory metals for the internal metallurgy system.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-11 | 1989-05-13 | 1989-11-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-11 | 1993-05-13 | 1993-11-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-11 | 1997-05-13 | 1997-11-12 | $7700.00 | Window Closed / Lapsed |