US4442137A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Maskless coating of metallurgical features of a dielectric substrate
Assignee: International Business Machines Corp
•
Filing: 1982-03-18
•
Granted: 1984-04-10
•
Expires: 2002-03-18
Abstract
Abstract Maskless technique for plating a protective metal layer on existing metallurgical pattern supported on a dielectric substrate by blanket coating said metal layer over said substrate, heating to diffuse the metal into said pattern, cooling to spall the metal on the non-patterned portions of the substrate surfaces by the stresses induced from the differences in the thermal contraction differentials between the metal and the substrate, and mechanically removing the metal layer from the non-patterned substrate surfaces. Optionally, the metal layer can also be blanket coated with a passivating metal film with interdiffusion between them at their interface during the noted heating step. In application to support carriers for mounting of semiconductor devices, the substrate will comprise an alumina based ceramic, the pattern will comprise a molybdenum based metal, and the protective metal layer can comprise a nickel based metal. In this application, the second passivating metal film can comprise gold.
Inventors
- 👤 Ananda H. Kumar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 18:05
CPC Classifications
H; H10; H10W; H10W70/00; H10W70/60; H10W70/62; H10W70/66; H05; H05K; H05K3/00; H05K3/22; H05K3/24; H05K3/245; H05K3/246; H10W70/01; H10W70/05; H05K2203/00; H05K2203/11; H05K2203/1105; H05K3/02; H05K3/04; H05K3/10; H05K3/14; H05K3/143; H05K3/244
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
99 words
A method for selectively depositing a conductive solderable or brazeable metal layer over an existing diverse metallurgical pattern supported on a dielectric substrate comprising: blanket coating said metal over said substrate, said metal having a different thermal coefficient of contraction relative to said substrate; heating said substrate to diffusion bond said metal to said metallurgical pattern; cooling said substrate to spall said metal on the remaining metallurgically unpatterned portions of said substrate by the stresses induced from the differences in the thermal contraction differentials therebetween, and mechanically removing said spalled metal from said remaining unpatterned portions of said substrate.
Claim 2
Independent Claim
99 words
A method for selectively depositing a conductive solderable or brazeable metal layer over an existing diverse metallurgical pattern supported on a dielectric substrate comprising: blanket coating said metal over said substrate, said metal having a different thermal coefficient of contraction relative to said substrate; heating said substrate to diffusion bond said metal to said metallurgical pattern; cooling said substrate to spall said metal on the remaining metallurgically unpatterned portions of said substrate by the stresses induced from the differences in the thermal contraction differentials therebetween, and mechanically removing said spalled metal from said remaining unpatterned portions of said substrate.
Claim 3
Dependent Claim
14 words
The method of claim 1 wherein said metal is removed from said substrate ultrasonically.
Claim 4
Dependent Claim
14 words
The method of claim 1 wherein said substrate is formed of a ceramic material.
Claim 5
Dependent Claim
14 words
The method of claim 3 wherein said metal is removed from said substrate ultrasonically.
Claim 6
Dependent Claim
22 words
The method of claim 3 wherein said substrate comprises an alumina ceramic and said metallurgical pattern is comprised of a refractory metal.
Claim 7
Dependent Claim
14 words
The method of claim 5 wherein said metal is removed from said substrate ultrasonically.
Claim 8
Dependent Claim
13 words
The method of claim 5 wherein said metallurgical pattern is comprised of molybdenum.
Claim 9
Dependent Claim
14 words
The method of claim 7 wherein said metal is removed from said substrate ultrasonically.
Claim 10
Dependent Claim
10 words
The method of claim 7 wherein said metal is nickel.
Claim 11
Dependent Claim
14 words
The method of claim 9 wherein said metal is removed from said substrate ultrasonically.
Claim 12
Dependent Claim
36 words
The method of claim 1 including blanket depositing a conductive passivating diverse second metal layer prior to said heating over the first said metal, and interdiffusing both said metals at the interface therebetween during said heating.
Claim 13
Dependent Claim
14 words
The method of claim 11 wherein said substrate is formed of a ceramic material.
Claim 14
Dependent Claim
22 words
The method of claim 12 wherein said substrate comprises an alumina ceramic and said metallurgical pattern is comprised of a refractory metal.
Claim 15
Dependent Claim
13 words
The method of claim 13 wherein said metallurgical pattern is comprised of molybdenum.
Claim 16
Dependent Claim
12 words
The method of claim 14 wherein the first said metal is nickel.
Claim 17
Dependent Claim
12 words
The method of claim 15 wherein the said second metal is gold.
Claim 18
Dependent Claim
14 words
The method of claim 16 wherein said metal is removed from said substrate ultrasonically.
Claim 19
Independent Claim
134 words
A method for selectively coating an existant metallurgy patten supported by a dielectric substrate with a diverse metal which is non-wettable to said substrate but mechanically adhesive to said substrate and said metal layer with said diverse metal having a higher coefficient of thermal expansion than said substrate: blanket coating said substrate, inclusive of said existent metallurgical pattern, with said diverse metal, said diverse metal having a different thermal coefficient of contraction relative to said substrate; heating said substrate to interdiffuse said metal to said pattern at the interface therebetween, cooling said substrate to spall said metal coating on the remaining metallurgically unpatterned portions of said substrate by the stresses induced from the differences in the thermal contraction differentials therebetween, and ultrasonically removing said spalled metal from said remaining unpatterned portions of said substrate.
Claim 20
Independent Claim
134 words
A method for selectively coating an existant metallurgy patten supported by a dielectric substrate with a diverse metal which is non-wettable to said substrate but mechanically adhesive to said substrate and said metal layer with said diverse metal having a higher coefficient of thermal expansion than said substrate: blanket coating said substrate, inclusive of said existent metallurgical pattern, with said diverse metal, said diverse metal having a different thermal coefficient of contraction relative to said substrate; heating said substrate to interdiffuse said metal to said pattern at the interface therebetween, cooling said substrate to spall said metal coating on the remaining metallurgically unpatterned portions of said substrate by the stresses induced from the differences in the thermal contraction differentials therebetween, and ultrasonically removing said spalled metal from said remaining unpatterned portions of said substrate.
Claim 21
Dependent Claim
29 words
The method of claim 18 wherein said substrate is an alumina base ceramic, said pattern is a molybdenum based metal, and said metal layer is a nickel based metal.
Claim 22
Dependent Claim
41 words
The method of claim 18 including blanket coating said substrate prior to said heating, with a second diverse conductive passivating metal layer over the first said metal layer, and interdiffusing both said metal layers at the interface therebetween during said heating.
Claim 23
Dependent Claim
29 words
The method of claim 20 wherein said substrate is an alumina base ceramic, said pattern is a molybdenum based metal, and said metal layer is a nickel based metal.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-10 | 1987-10-10 | 1988-04-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-10 | 1991-10-10 | 1992-04-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-10 | 1995-10-10 | 1996-04-10 | $7700.00 | Window Closed / Lapsed |