Flux-free photodetector bonding
Assignee: RCA Corp
•
Filing: 1983-11-28
•
Granted: 1985-09-10
•
Expires: 2003-11-28
Abstract
Abstract A method of bonding photodetector devices to heatsinks, which devices can be damaged above 250° C., using a gold-tin eutectic solder which has a melting point of 280° C., is disclosed. The process comprises heating the heatsink and solder past the solder melting point on a quick thermal response heating element, turning off the heating power, and introducing the chip into the liquid solder on the cool down cycle. By controlling the rate at which the heatsink solder and device cool down and the time span from introduction of the chip to solidification of the solder, the chip can be exposed to sufficient heat to provide a good thermal, electrical and physical bond while substantially enhancing the yield of electrically undamaged photodetector chips.
Inventors
- 👤 Frank Z. Hawrylo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 12:04
CPC Classifications
H; H10; H10F; H10F71/00; H10F71/127; H10F71/1272; H10F77/00; H10F77/60; H10W; H10W72/00; H10W72/071; H10W72/073; H10W72/07331; H10W72/07336; H10W72/30; H10W72/351; H10W72/352; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/544
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
123 words
A method of soldering a semiconductor device to a heatsink wherein said device has a critical temperature above which it is adversely affected and wherein the solder has a melting temperature above said critical temperature, which method comprises; heating the heatsink and the solder above the solder melting point; cooling the liquid solder situate on the heatsink; introducing the device into the liquid solder under a pressure sufficient to provide uniform heating and wetting of the device by the solder; and controlling the time span and cooling rate between the device introduction step and the point at which the solder solidifies whereby an acceptable electrical and thermal bond of the device to the heatsink is provided with minimal adverse effects to the device.
Claim 2
Independent Claim
123 words
A method of soldering a semiconductor device to a heatsink wherein said device has a critical temperature above which it is adversely affected and wherein the solder has a melting temperature above said critical temperature, which method comprises; heating the heatsink and the solder above the solder melting point; cooling the liquid solder situate on the heatsink; introducing the device into the liquid solder under a pressure sufficient to provide uniform heating and wetting of the device by the solder; and controlling the time span and cooling rate between the device introduction step and the point at which the solder solidifies whereby an acceptable electrical and thermal bond of the device to the heatsink is provided with minimal adverse effects to the device.
Claim 3
Dependent Claim
22 words
The method of claim 1 wherein the solder comprises 80 percent by weight of gold and 20 percent by weight of tin.
Claim 4
Dependent Claim
21 words
The method of claim 2 wherein the solder is heated to a temperature about 20°-30° C. greater than its melting point.
Claim 5
Dependent Claim
36 words
The method of claim 3 wherein the solder is heated to a temperature of about 20°-30° C. greater than its melting point by applying the solder to the heatsink and heating them to said temperature together.
Claim 6
Dependent Claim
29 words
The method of claim 1 wherein the pressure applied to the device upon introduction of the device into the solder is between 40 and 64 kilograms per square centimeter.
Claim 7
Dependent Claim
43 words
The method of claim 5 wherein the cooling rate between the device introduction step and the point at which the solder solidifies is greater than about 1° C./second and wherein the time span between those two points is less than about 20 seconds.
Claim 8
Dependent Claim
26 words
The method of claim 6 wherein the cooling rate is less than about 4° C./second and wherein the time span is greater than about 5 seconds.
Claim 9
Dependent Claim
22 words
The method of claim 7 wherein the cooling rate is about 2° C./second and wherein the time span is about 10 seconds.
Claim 10
Dependent Claim
23 words
The method of claim 8 wherein the semiconductor device is a photodetector including InGaAs having a mounting surface with a gold pad thereon.
References Cited (Backward Citations)
US3071854A
Cited
US3165818A
Cited
US3648357A
Cited
US3680196A
Cited
US3883946A
Cited
US4039116A
Cited
US4142662A
Cited
DD146153A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-09 | 1989-03-11 | 1989-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-09 | 1993-03-11 | 1993-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-09 | 1997-03-11 | 1997-09-10 | $7700.00 | Window Closed / Lapsed |