High performance fiber ribbon product, high strength hybrid composites and methods of producing and using same

Claim 3

Method of claim 1, wherein the contacting of the impregnated mat and the one or more continuous high performance reinforcing fibers is performed by filament winding, where the impregnated mat is placed on the mandrel having a polymeric film on its surface and continuous high performance fibers are wound onto the impregnated mat by the rotating mandrel until at least more than one length of the high performance fiber is disposed as a layer on the impregnated mat.

Claim 4

The method of claim 2, wherein the impregnated fiberous mat is prepared by placing an effective amount of the matrix compatible polymer of the polymeric film on the mandrel, applying the fiberous mat to be impregnated to the polymer and applying a second effective amount of the matrix compatible polymer to the mat.

Claim 5

The method of claim 2, wherein the preparation is performed by placing an impregnated mat on the mandrel having a polymeric film on its surface and simultaneously adding a small amount of matrix compatible polymer to the impregnated mat.

Claim 6

Method of claim 3, wherein the first effective amount of matrix compatible polymer, mat and second effective amount of matrix compatible polymer are added to a layer of continuous high performance reinforcing fibers present on the mandrel.

Claim 7

Method of claim 1, wherein the high performance reinforcing fibers are longitudinally aligned in the layers.

Claim 8

Method of claim 1, wherein the high performance reinforcing fibers are in near parallel alignment in the one or more layers.

Claim 9

Method of claim 1, wherein the high performance reinforcing fibers are in side-by-side near parallel alignment.

Claim 10

Method of claim 1, wherein the high performance reinforcing fibers have a controlled spacing between them in the one or more layers.

Claim 11

Method of claim 1, wherein the impregnated mat is contacted with the high performance continuous reinforcing fibers in a layer which extends across the mandrel.

Claim 12

Method of claim 4 or 5, wherein the second effective amount of polymer is rolled into the mat.

Claim 13

Method of claim 1, wherein the mat is selected from the group consisting of glass, organic or high performance fiberous continuous monofilament mat, continuous fine diameter fiberous mat, and chopped strand paper mat, and chopped short length strand mat.

Claim 14

Method of claim 1, wherein the high performance reinforcing fibers are selected from the group consisting of carbon fibers, graphite fibers, aramid fibers, and other fibers having a Young's modulus greater than about 14×10 6 psi.

Claim 15

Method of claim 1, wherein the contacting is performed by filament winding where the one or more layers of the high performance reinforcing fibers are wound onto the mandrel having a polymer film on its surface and the impregnated fiberous mat is placed on the wound fibers.

Claim 16

The method of claim 14, wherein the layers on the mandrel can be in the same direction or in different directions from layer to layer.

Claim 17

Method of claim 1, wherein the tape product is combined with molding compounds.

Claim 18

Method of claim 1, wherein the mat has a weight up to one ounce per square foot (0.03 gm (cm 2 ).

Claim 19

Method of claim 1, wherein the matrix compatible polymer is selected from the group consisting of: saturated and unsaturated polyesters, 1,2- and 1,3-epoxies, vinyl esters, with or without the addition of styrene or vinyl monomer, polybutylene terephthalate, polysulfone, polyester sulfone, nylon, polyphenylene sulfide and polyamide-imide.

Claim 20

Method of claim 1, wherein the coating on the one or more continuous high performance reinforcing fibers is applied by dye coating wherein the one or more dye orifices are set at about 0.014 to about 0.11 inch (0.036-0.28 cm).

Claim 21

Method of claim 1, wherein the matrix compatible polymer is the matrix molding compound.

Claim 22

Method of claim 1, wherein the matrix compatible polymer impregnating the fiberous mat and present on the one or more continuous high performance reinforcing fibers gives a total amount of matrix compatible polymer in the tape in the range of about 1 to about 20 weight percent of the tape.

Claim 23

Method of claim 1, wherein the matrix compatible polymer in the tape product is a curable thermosetting matrix compatible polymer or a softened thermoplastic matrix compatible polymer.

Claim 24

An improved high performance continuous reinforcing fiberous tape product, which maintains substantially the alignment of the high performance fiberous reinforcement in the tape during molding, comprising: a layer of fiberous mat having a thickness in the range of about 0.01 to about 0.05 inch, a matrix compatible polymer impregnating the fiberous mat, and more than one length of continuous high performance reinforcing fibers coated over a substantial portion of their surfaces with a matrix compatible polymer to thoroughly wet the fibers, where the fibers form one or more layers in which the fibers have a unidirectional orientation in each layer and where the fibers contact the fiberous mat.

Claim 25

An improved high performance continuous reinforcing fiberous tape product, which maintains substantially the alignment of the high performance fiberous reinforcement in the tape during molding, comprising: a layer of fiberous mat having a thickness in the range of about 0.01 to about 0.05 inch, a matrix compatible polymer impregnating the fiberous mat, and more than one length of continuous high performance reinforcing fibers coated over a substantial portion of their surfaces with a matrix compatible polymer to thoroughly wet the fibers, where the fibers form one or more layers in which the fibers have a unidirectional orientation in each layer and where the fibers contact the fiberous mat.

Claim 26

Article of claim 23, wherein the mat is selected from the group consisting of glass fiberous, organic fiberous, or high performance fiberous continuous monofilament mat; chopped strand paper mat, and fine diameter continuous multifilament mat, and chopped short length strand mat.

Claim 27

Article of claim 23, wherein the matrix compatible polymer is selected from the group consisting of: saturated and unsaturated polyesters, 1,2- and 1,3-epoxies, vinyl esters, with or without the addition of styrene or vinyl monomer, polybutylene terephthalate, polysulfone, polyether sulfone, nylon, polyphenylene sulfide and polyamide-imide.

Claim 28

Article of claim 23, wherein the high performance reinforcing fiberous strand is selected from the group consisting of carbon, graphite, aramid, boron, and silicon carbide strands and other strands having a Young's modulus greater than about 14×10 6 psi.

Claim 29

Article of claim 24, wherein the mat is present in an amount of about 1 to about 35 weight percent of the article.

Claim 30

Article of claim 25, wherein the amount of resin is present in an amount of about 1 to about 20 weight percent of the article.

Claim 31

Article of claim 26, wherein the amount of high performance reinforcing fiber is present in an amount of about 5 to about 85 weight percent of the article.

Claim 32

Article of claim 23 contacting molding compounds selected from the group consisting of sheet molding compounds, high reinforcement content molding compounds, filament wound molding compounds, thick molding compounds and bulk molding compounds.

Claim 33

Article of claim 23, wherein the high performance reinforcing fiber strands are in side-by-side near parallel alignment.

Claim 34

Article of claim 23, wherein the high performance reinforcing strands have controlled spacing between the strands in the layers.

Claim 35

Tape product of claim 23, wherein the matrix compatible polymer is the matrix molding polymeric compound.

Claim 36

Tape product of claim 23, wherein the total amount of the matrix compatible polymer present in the impregnated fiberous mat and with the one or more continuous high performance reinforcing fibers is an amount in the range of about 1 to about 20 weight percent of the tape product.

Claim 37

Tape product of claim 23 having cured thermosetting matrix compatible polymer or a hardened thermoplastic matrix compatible polymer.

Claim 38

Method of preparing a molding compound with high performance reinforcing fibers by filament winding, comprising: (a) placing a polymeric film on the mandrel of a filament winding apparatus to assure release of the material from the mandrel, (b) applying to the mandrel an effective amount of a matrix compatible polymer, (c) applying to the polymer on the mandrel a fiberous mat having a thickness in the range of about 0.01 inch to about 0.05 inch (0.025-0.13 cm), (d) rolling the mat in the polymer to impregnate the mat with the polymer, (e) rotating the mandrel to wind one or more layers of one or more high performance reinforcing fibers, (f) rotating the mandrel to wind on top of the layer of high performance fiber one or more layers of reinforcing fiberous strand, coated with matrix compatible polymer, and (g) removing the polymer impregnated mat, high performance fiber layer or layers and reinforcing fiberous strand layer or layers as a molding compound with a polymeric film covering.

Claim 39

Method of preparing a molding compound with high performance reinforcing fibers by filament winding, comprising: (a) placing a polymeric film on the mandrel of a filament winding apparatus to assure release of the material from the mandrel, (b) applying to the mandrel an effective amount of a matrix compatible polymer, (c) applying to the polymer on the mandrel a fiberous mat having a thickness in the range of about 0.01 inch to about 0.05 inch (0.025-0.13 cm), (d) rolling the mat in the polymer to impregnate the mat with the polymer, (e) rotating the mandrel to wind one or more layers of one or more high performance reinforcing fibers, (f) rotating the mandrel to wind on top of the layer of high performance fiber one or more layers of reinforcing fiberous strand, coated with matrix compatible polymer, and (g) removing the polymer impregnated mat, high performance fiber layer or layers and reinforcing fiberous strand layer or layers as a molding compound with a polymeric film covering.

Claim 40

Method of claim 36 which includes placing a second application of matrix compatible polymer on the last layer of reinforcing fiberous strand, and placing a second mat on the second application of polymer, and rolling the mat into the polymer to saturate the fiberous mat.

Claim 41

Method of claim 36 or 37 which includes: rotating the mandrel to wind a second application of one or more layers of high performance fibers onto one or more layers of general reinforcing fiberous strand, applying to the last layer of high performance fiber another application of an effective amount of matrix compatible polymer, and rolling into the effective amount of polymer another fiberous mat to saturate the mat with the polymer.

Claim 42

Method of claim 36 or 38, wherein a polymeric film is applied to the top layer of the molding compound.

Claim 43

Method of claim 36 or 38, wherein the high performance reinforcing fiber or fibers are coated with matrix compatible polymer before being wound on the mandrel.

Claim 44

Method of claim 36 or 38, wherein the general reinforcing fiberous strand is wound in a helical pattern on the mandrel.

Claim 45

Method of claims 36 or 38, wherein the general reinforcing fiberous strands are glass fiber strands.

Claim 46

A molding compound, comprising: (a) a fiberous mat, (b) an effective amount of matrix compatible polymer impregnating the mat, where the mat impregnated with the matrix compatible polymer is suitable for contacting with high performance reinforcing fibers, (c) one or more high performance continuous reinforcing fibers in the form of one or more layers with a layer in contact with the impregnated mat, whereby the high performance reinforcing fibers have improved alignment, (d) one or more layers of general reinforcing mat selected from filament wound reinforcing fiberous strand, continuous strand mat chopped strand mat high glass reinforcement and woven strand mat, contacting the last layer of high performance continuous reinforcing fibers, and (e) matrix polymer for the one or more layers of general reinforcing mats selected from saturated and unsaturated polyesters, 1,2- and 1,3-epoxy polymers and vinyl esterpolymers, polybutylene terephthalate, polysulfone, polyether sulfone, nylon, polyphenylene sulfide and polyamide-imide forming molding compounds with the general reinforcing mat selected from the group consisting of bulk molding compounds, sheet molding compounds, high glass reinforcing molding compounds and thick molding compounds.

Claim 47

A molding compound, comprising: (a) a fiberous mat, (b) an effective amount of matrix compatible polymer impregnating the mat, where the mat impregnated with the matrix compatible polymer is suitable for contacting with high performance reinforcing fibers, (c) one or more high performance continuous reinforcing fibers in the form of one or more layers with a layer in contact with the impregnated mat, whereby the high performance reinforcing fibers have improved alignment, (d) one or more layers of general reinforcing mat selected from filament wound reinforcing fiberous strand, continuous strand mat chopped strand mat high glass reinforcement and woven strand mat, contacting the last layer of high performance continuous reinforcing fibers, and (e) matrix polymer for the one or more layers of general reinforcing mats selected from saturated and unsaturated polyesters, 1,2- and 1,3-epoxy polymers and vinyl esterpolymers, polybutylene terephthalate, polysulfone, polyether sulfone, nylon, polyphenylene sulfide and polyamide-imide forming molding compounds with the general reinforcing mat selected from the group consisting of bulk molding compounds, sheet molding compounds, high glass reinforcing molding compounds and thick molding compounds.

Claim 48

Molding compound of claim 43, wherein the fiberous mat is selected from the group consisting of a glass fiberous, organic fiberous or high performance fiberous continuous monofilament mat; or chopped glass fiber strand mat or chopped strand paper mat; or fine diameter continuous multifilament mat; or chopped short length strand mat.

Claim 49

Molding compound of claim 43 or 44, wherein the fiberous mat has a thickness in the range of about 0.01 inch to about 0.05 inch (0.025-0.13 cm).

Claim 50

Molding compound of claim 43, wherein the mattrix compatible polymer is selected from general polyester polymers, 1,2- and 1,3-epoxy polymers and vinyl ester polymers.

Claim 51

Molding compound of claim 43, wherein the high performance reinforcing fiber is carbon, or graphite fibers or mixture thereof.

Claim 52

A molding compound, comprising: (a) a fiberous mat having a thickness in the range of about 0.01 to about 0.05 inch and a weight up to one ounce per square foot (0.03 grams/cm 2 ) wherein the fiberous material in the mat is one or more continuous monofilaments selected from the group consisting of glass fibers, organic fibers, or high performance fibers, (b) an effective amount of matrix compatible polymer impregnating the mat, wherein the mat impregnated with the matrix compatible polymer is suitable for contacting with high performance reinforcing fibers, (c) one or more high performance continuous reinforcing fibers in the form of one or more layers with a layer in contact with the impregnated mat, wherein the one or more high performance continuous reinforcing fibers have a coating of the matrix compatible polymer on a substantial portion of their surfaces to thoroughly wet the fibers, and where the fibers are present in a unidirectional orientation in each layer, and wherein the amount of the continuous monofilament fiberous mat that is present is in the range of about 1 to about 35 weight percent of the fiberous mat plus the matrix compatible polymer of (b), and plus the high performance continuous reinforcing fibers of (c), and where the amount of the high performance reinforcing continuous fibers is about 5 to about 85 weight percent of the monofilament fiberous mat plus matrix compatible polymer of (b), and high performance fibers of (c), and where the matrix compatible polymer is present in an amount of about 1 to about 20 weight percent of the monofilament mat of (a), plus the matrix compatible polymer of (b) and the high performance continuous fibers of (c), (d) one or more layers of molding compound selected from the group consisting of bulk molding compounds, sheet molding compounds and high glass reinforcement molding compounds and filament wound molding materials formed from one or more layers of general reinforcing mat selected from filament wound reinforcing fiberous strand, continuous strand mat, chopped strand mat, high glass reinforcement, and woven strand mat and a matrix polymer for the one or more layers of general reinforcing mats selected from saturated polyesters, unsaturated polyesters, 1,2- and 1,3-epoxy polymers, vinyl ester polymers, polybutylene terephthalate, polysulfone, polyether sulfone, nylon, polyphenylene sulfide and polyamideimide, wherein the molding compound contacts the last layer of high performance continuous reinforcing fibers, (e) a fiberous mat having a thickness in the range of about 0.01 to about 0.05 inch and a weight up to one ounce per square foot (0.03 grams/cm 2 ) wherein the fiberous material in the mat is one or more continuous monofilaments of glass fibers, organic fibers, or high performance fibers that is in contact with the last layer of molding compound, (f) an effective amount of matrix compatible polymer impregnating the mat of (e), wherein the mat impregnated with the matrix compatible polymer is suitable for contacting with high performance reinforcing fibers, and (g) one or more high performance continuous reinforcing fibers in the form of one or more layers in contact with the impregnated mat, wherein the one or more high performance continuous reinforcing fibers have a coating of the matrix compatible polymer on a substantial portion of their surfaces to thoroughly wet the fibers, and where the fibers are present in a unidirectional orientation in each layer, and wherein the amount of continuous monofilament mat that is present is about 1 to about 35 weight percent of the mat of (e), the matrix compatible polymer of (f), and the high performance continuous reinforcing fibers of (g), and where the amount of the high performance reinforcing continuous fibers in the monofilament mat is about 5 to about 85 weight percent of the monofilament mat of (e), matrix compatible polymer of (f), and high performance fibers of (g) and where the matrix compatible polymer is present in an amount of about 1 to about 20 weight percent of the monofilament mat of (e), the matrix compatible polymer of (f) and the high performance continous fibers of (g).

Claim 53

A molding compound, comprising: (a) a fiberous mat having a thickness in the range of about 0.01 to about 0.05 inch and a weight up to one ounce per square foot (0.03 grams/cm 2 ) wherein the fiberous material in the mat is one or more continuous monofilaments selected from the group consisting of glass fibers, organic fibers, or high performance fibers, (b) an effective amount of matrix compatible polymer impregnating the mat, wherein the mat impregnated with the matrix compatible polymer is suitable for contacting with high performance reinforcing fibers, (c) one or more high performance continuous reinforcing fibers in the form of one or more layers with a layer in contact with the impregnated mat, wherein the one or more high performance continuous reinforcing fibers have a coating of the matrix compatible polymer on a substantial portion of their surfaces to thoroughly wet the fibers, and where the fibers are present in a unidirectional orientation in each layer, and wherein the amount of the continuous monofilament fiberous mat that is present is in the range of about 1 to about 35 weight percent of the fiberous mat plus the matrix compatible polymer of (b), and plus the high performance continuous reinforcing fibers of (c), and where the amount of the high performance reinforcing continuous fibers is about 5 to about 85 weight percent of the monofilament fiberous mat plus matrix compatible polymer of (b), and high performance fibers of (c), and where the matrix compatible polymer is present in an amount of about 1 to about 20 weight percent of the monofilament mat of (a), plus the matrix compatible polymer of (b) and the high performance continuous fibers of (c), (d) one or more layers of molding compound selected from the group consisting of bulk molding compounds, sheet molding compounds and high glass reinforcement molding compounds and filament wound molding materials formed from one or more layers of general reinforcing mat selected from filament wound reinforcing fiberous strand, continuous strand mat, chopped strand mat, high glass reinforcement, and woven strand mat and a matrix polymer for the one or more layers of general reinforcing mats selected from saturated polyesters, unsaturated polyesters, 1,2- and 1,3-epoxy polymers, vinyl ester polymers, polybutylene terephthalate, polysulfone, polyether sulfone, nylon, polyphenylene sulfide and polyamideimide, wherein the molding compound contacts the last layer of high performance continuous reinforcing fibers, (e) a fiberous mat having a thickness in the range of about 0.01 to about 0.05 inch and a weight up to one ounce per square foot (0.03 grams/cm 2 ) wherein the fiberous material in the mat is one or more continuous monofilaments of glass fibers, organic fibers, or high performance fibers that is in contact with the last layer of molding compound, (f) an effective amount of matrix compatible polymer impregnating the mat of (e), wherein the mat impregnated with the matrix compatible polymer is suitable for contacting with high performance reinforcing fibers, and (g) one or more high performance continuous reinforcing fibers in the form of one or more layers in contact with the impregnated mat, wherein the one or more high performance continuous reinforcing fibers have a coating of the matrix compatible polymer on a substantial portion of their surfaces to thoroughly wet the fibers, and where the fibers are present in a unidirectional orientation in each layer, and wherein the amount of continuous monofilament mat that is present is about 1 to about 35 weight percent of the mat of (e), the matrix compatible polymer of (f), and the high performance continuous reinforcing fibers of (g), and where the amount of the high performance reinforcing continuous fibers in the monofilament mat is about 5 to about 85 weight percent of the monofilament mat of (e), matrix compatible polymer of (f), and high performance fibers of (g) and where the matrix compatible polymer is present in an amount of about 1 to about 20 weight percent of the monofilament mat of (e), the matrix compatible polymer of (f) and the high performance continous fibers of (g).

Claim 54

Molding compound of claim 48, wherein the matrix compatible polymer is selected from general polyester polymers, 1,2- and 1,3-epoxy polymers and vinyl ester polymers.

Claim 55

Molding compound of claim 48, wherein the high performance reinforcing fiber is carbon, or graphite fibers or mixture thereof.

Claim 56

Method of producing a molded article with increased physical properties at desired locations in the article, comprising: (a) placing in a compression mold a molding compound selected from sheet molding compound, high reinforcement content sheet molding compound, bulk molding compound, thick molding compound, filament wound molding compound or mixture thereof, or heated thermoplastic molding compounds, (b) placing in the mold with the molding compound one or more segments of a tape of aligned high performance reinforcing fibers having attached to the fibers a fiberous mat which is impregnated with a matrix compatible polymer, (c) arranging the segments of tape to be at the locations in the molding article, where the higher physical properties are desired, and (d) activating the compression molding device to close to mold the article, (e) activating the compression molding device to open, and (f) recovering the molded article having high performance fiber reinforcement that is substantially aligned as the tape was placed in the mold at the desired location.

Claim 57

Method of producing a molded article with increased physical properties at desired locations in the article, comprising: (a) placing in a compression mold a molding compound selected from sheet molding compound, high reinforcement content sheet molding compound, bulk molding compound, thick molding compound, filament wound molding compound or mixture thereof, or heated thermoplastic molding compounds, (b) placing in the mold with the molding compound one or more segments of a tape of aligned high performance reinforcing fibers having attached to the fibers a fiberous mat which is impregnated with a matrix compatible polymer, (c) arranging the segments of tape to be at the locations in the molding article, where the higher physical properties are desired, and (d) activating the compression molding device to close to mold the article, (e) activating the compression molding device to open, and (f) recovering the molded article having high performance fiber reinforcement that is substantially aligned as the tape was placed in the mold at the desired location.

Claim 58

Method of claim 51, wherein the tape is a high performance continuous reinforcing fiberous tape product, which maintains substantially the alignment of the high performance fiberous reinforcement in the tape during molding, comprising: a layer of fiberous mat having a thickness in the range of about 0.01 to about 0.05 inch, a matrix compatible polymer impregnating the fiberous mat, and more than one length of continuous high performance reinforcing fibers coated over a substantial portion of their surface with a matrix compatible polymer to thoroughly wet the fibers where the fibers from one or more layers having the fibers in a unidirectional orientation in each layer, where a layer is in contact with the fiberous mat and matrix compatible polymer.