Filament-wound reinforced plastic articles and process of making and using same
Assignee: Evonik Operations GmbH
•
Filing: 1975-04-08
•
Granted: 1976-06-29
•
Expires: 1995-04-08
Abstract
Abstract Filament-wound reinforced plastic articles and parts thereof are obtained by wetting and impregnating filaments, rovings, webs, and the like fibrous materials consisting of glass, carbon, graphite, boron, steel, asbestos, temperature resistant organic fibers, and the like with a liquid or liquefied polymerizable organic compound of a high melting point which can be polymerized by addition polymerization, and converting the wetted fibrous material into the desired wound plastic article or part thereof by winding around a mandrel and then subjecting the wound article to addition polymerization. Wetting and winding with the polymerizable organic compound are effected under conditions under which substantially no polymerization takes place. Especially suitable polymerizable organic compounds are bisimides such as the bismaleimides of a melting point which is at least 20° C. below the temperature required for polymerization.
Inventors
- 👤 Horst Stenzenberger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 01:18
CPC Classifications
B; B29; B29C; B29C53/00; B29C53/56; B29C53/58; B29C53/60
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
180 words
In a process of producing a filament-wound reinforced substantially pore-free plastic article by wetting and impregnating fibrous material with a plastic material and winding the wetted and impregnated fibrous material around a mandrel of a shape corresponding to the inner structure of the desired plastic article, the improvement which consists in the steps of a. wetting and impregnating the filamentary fibrous material with a liquid molten polymerizable bisimide having a melting point below 200°C., which melting point is at least 20°C. below the temperature at which substantial polymerization sets in, said wetting and impregnating step being carried out at a temperature above the melting point of said bisimide and below that at which substantial polymerization takes place, at which temperature said bisimide has a viscosity substantially lower than 800 centistokes; b. winding the thus wetted and impregnated filamentary fibrous material around a winding mandrel of the desired shape to produce the respective wound article; and c. heating said wound article at a temperature sufficient to effect addition polymerization and to cause hardening and curing to the filament-wound, reinforced plastic article.
Claim 2
Dependent Claim
180 words
In a process of producing a filament-wound reinforced substantially pore-free plastic article by wetting and impregnating fibrous material with a plastic material and winding the wetted and impregnated fibrous material around a mandrel of a shape corresponding to the inner structure of the desired plastic article, the improvement which consists in the steps of a. wetting and impregnating the filamentary fibrous material with a liquid molten polymerizable bisimide having a melting point below 200°C., which melting point is at least 20°C. below the temperature at which substantial polymerization sets in, said wetting and impregnating step being carried out at a temperature above the melting point of said bisimide and below that at which substantial polymerization takes place, at which temperature said bisimide has a viscosity substantially lower than 800 centistokes; b. winding the thus wetted and impregnated filamentary fibrous material around a winding mandrel of the desired shape to produce the respective wound article; and c. heating said wound article at a temperature sufficient to effect addition polymerization and to cause hardening and curing to the filament-wound, reinforced plastic article.
Claim 3
Dependent Claim
43 words
The process of claim 1, in which the polymerizable organic compound is a bisimide, the polymerization speed of which is substantially slower than the time required for winding the filamentary fibrous material wetted and impregnated with the polymerizable bisimide around the winding mandrel.
Claim 4
Dependent Claim
108 words
The process of claim 1, in which the polymerizable compound is a bisimide of the formula ##EQU4## in which R 1 indicates a group which is capable of addition polymerization, while R 2 is a member selected from the group consisting of alkylene, cycloalkylene, arylene, at least two arylenes bonded to one another through a member selected from the group consisting of methylene --CH 2 --, sulfone --SO 2 --, and oxo --O--, at least two cycloalkylenes bonded to one another through a member selected from the group consisting of methylene --CH 2 --, sulfone --SO 2 --, and oxo --O--, and such substituted alkylene, cycloalkylene, and arylene.
Claim 5
Dependent Claim
13 words
The process of claim 3, in which the polymerizable compound is a bismaleimide.
Claim 6
Dependent Claim
33 words
The process of claim 4, in which the polymerizable compound is a bismaleimide selected from the group consisting of 1,12-bismaleimido dodecane, 2,4-bismaleimido toluene, 1,6-bismaleimido-2,2,4-(trimethyl) hexane, 4,4'-bismaleimido diphenylmethane, 4,4'-bismaleimido diphenyl ether, and mixtures thereof.
Claim 7
Dependent Claim
35 words
The process of claim 1, wherein said winding of the wetted and impregnated filamentary fibrous material around the mandrel is carried out at a temperature at which substantially no polymerization of said bisimide takes place.
Claim 8
Dependent Claim
34 words
The process of claim 1, wherein said winding of the wetted and impregnated filamentary fibrous material around the mandrel is carried out at a tension of said filamentary fibrous material of about 250 g.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-29 | 1979-12-29 | 1980-06-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-29 | 1983-12-29 | 1984-06-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-29 | 1987-12-29 | 1988-06-29 | $7700.00 | Window Closed / Lapsed |