Process for preparing printing ink binders, and their use in printing inks
Assignee: Hoechst AG
•
Filing: 1984-03-29
•
Granted: 1985-07-09
•
Expires: 2004-03-29
Abstract
Abstract Process for preparing printing ink binders based on reaction products of (a) natural resins, a copolymer (b+c) of (b) polymerizable hydrocarbons having isolated C 5 rings and (c) α,β-olefinically unsaturated carboxylic acid units and (d) calcium compounds and, if appropriate, other compounds of metals of group II of the periodic system. The compounds (a) to (c) are reacted to give a product having an acid number of 75 to 150, which is then reacted with metal compounds in such a way that the acid number is reduced by at least one third. Unreacted metal compounds present in the resulting reaction product are then converted by means of acetic acid, via acetates, into salts of the resins. The resulting binders are used for preparing printing inks.
Inventors
- 👤 Albert Rudolphy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 20:51
CPC Classifications
C; C09; C09D; C09D11/00; C09D11/02; C09D11/10
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
188 words
A process for preparing printing ink binders which consists essentially of (A) reacting a natural resin acid (a) with (B) a copolymer (b+c) which has an acid number of 35 to 100 and is derived from (b) polymerizable hydrocarbons having isolated C 5 rings and (c) an α,β-olefinically unsaturated carboxylic acid component, the natural resin acid (a) and the copolymer (b+c) being in a weight ratio of (1 to 5):1, to yield a product having an acid number of 75 to 150, which is then (C) reacted with a metal compound (d) selected from the group consisting of at least one calcium compound, and a combination thereof with a compound at least one other metal of group II of the periodic system, in an amount of 1.5 to 6% by weight of metal content, relative to the total amount of components (a) to (c), in such a way that the acid number is reduced by at least one third of its value and, after the reaction of the metal compounds, converting not yet converted metal compounds via acetates, into salts of the resin by treatment with acetic acid.
Claim 2
Dependent Claim
188 words
A process for preparing printing ink binders which consists essentially of (A) reacting a natural resin acid (a) with (B) a copolymer (b+c) which has an acid number of 35 to 100 and is derived from (b) polymerizable hydrocarbons having isolated C 5 rings and (c) an α,β-olefinically unsaturated carboxylic acid component, the natural resin acid (a) and the copolymer (b+c) being in a weight ratio of (1 to 5):1, to yield a product having an acid number of 75 to 150, which is then (C) reacted with a metal compound (d) selected from the group consisting of at least one calcium compound, and a combination thereof with a compound at least one other metal of group II of the periodic system, in an amount of 1.5 to 6% by weight of metal content, relative to the total amount of components (a) to (c), in such a way that the acid number is reduced by at least one third of its value and, after the reaction of the metal compounds, converting not yet converted metal compounds via acetates, into salts of the resin by treatment with acetic acid.
Claim 3
Dependent Claim
24 words
Process as claimed in claim 1, wherein up to 30 mole % of the calcium compounds are reacted in the form of calcium acetate.
Claim 4
Dependent Claim
36 words
Process as claimed in claim 1, wherein the calcium compound is used in a mixture with at least one zinc compound and/or magnesium compound, the proportion of calcium being above 70% of the total metal content.
Claim 5
Dependent Claim
25 words
Process as claimed in claim 1 wherein the metal compound (d) is used in an amount of 1.8 to 4.5% by weight of metal content.
Claim 6
Dependent Claim
56 words
Process as claimed in claim 1, wherein the reaction mixture, during or after the reaction, or the natural resin acids is modified with (a1) maleic anhydride and/or (a2) phenolic resin or its components and/or (a3) olefinically unsaturated aromatic hydrocarbons or (a4) formaldehyde or (a5) phenol or the natural resin acids is previously modified with (a6) dicyclopentadiene.
Claim 7
Dependent Claim
22 words
Process as claimed in claim 1, wherein at most 70% of the COOH groups of the reaction product are converted into salts.
Claim 8
Dependent Claim
23 words
Process as claimed in claim 1, wherein the starting copolymer (b+c) is a polymer having an average molecular weight of 300 to 800.
Claim 9
Dependent Claim
27 words
Process as claimed in claim 1, wherein the component (c) is used in amounts of 10 to 18% by weight, relative to the amounts of polymerizable hydrocarbons.
Claim 10
Dependent Claim
17 words
An intaglio printing ink containing a binder prepared according to the process as claimed in claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-08 | 1989-01-07 | 1989-07-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-08 | 1993-01-07 | 1993-07-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-08 | 1997-01-07 | 1997-07-09 | $7700.00 | Window Closed / Lapsed |