Multilayer electrophotographic amorphous silicon element for electrophotographic copying processes
Assignee: Canon Production Printing Netherlands BV
•
Filing: 1983-10-17
•
Granted: 1985-07-02
•
Expires: 2003-10-17
Abstract
Abstract An amorphous silicon based photoconductive element for use in electrophotographic copying processes, which exhibits a suitably low dark discharge rate with other good photoelectric properties, is composed of an electrically conductive support having applied thereto, in sequence, a barrier layer consisting essentially of a doped hydrogen-containing amorphous silicon, an intermediate layer consisting essentially of substantially undoped hydrogen-containing amorphous silicon, an intermediate barrier layer consisting essentially of doped hydrogen-containing amorphous silicon and a main, charge receiving layer consisting essentially of substantially undoped hydrogen-containing amorphous silicon.
Inventors
- 👤 Gabriel N. M. M. van der Voort
- 👤 Marinus Groeneveld
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 04:53
CPC Classifications
G; G03; G03G; G03G5/00; G03G5/02; G03G5/04; G03G5/08; G03G5/082; G03G5/08214; G03G5/08235
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
154 words
An electrophotographic element for use in electrophotographic copying processes, comprising an electrically conductive support having applied thereto a barrier layer consisting essentially of a doped hydrogen-containing amorphous silicon, next to said barrier layer an intermediate layer consisting essentially of hydrogen-containing amorphous silicon, next to said intermediate layer an intermediate barrier layer consisting essentially of doped hydrogen-containing amorphous silicon, and on a said intermediate barrier layer a main layer consisting essentially of hydrogen-containing amorphous silicon, said barrier layer and said intermediate barrier layer being of the same conductivity type, and said intermediate layer and said main layer each being entirely undoped when said barrier layer and intermediate barrier layer are of p-type conductivity and, when said barrier layer and said intermediate barrier layer are of n-type conductivity, being either entirely undoped or doped with up to about 30 pm of a dopant sufficient to cause said main and intermediate layers to be preferentially p-type conductive.
Claim 2
Dependent Claim
154 words
An electrophotographic element for use in electrophotographic copying processes, comprising an electrically conductive support having applied thereto a barrier layer consisting essentially of a doped hydrogen-containing amorphous silicon, next to said barrier layer an intermediate layer consisting essentially of hydrogen-containing amorphous silicon, next to said intermediate layer an intermediate barrier layer consisting essentially of doped hydrogen-containing amorphous silicon, and on a said intermediate barrier layer a main layer consisting essentially of hydrogen-containing amorphous silicon, said barrier layer and said intermediate barrier layer being of the same conductivity type, and said intermediate layer and said main layer each being entirely undoped when said barrier layer and intermediate barrier layer are of p-type conductivity and, when said barrier layer and said intermediate barrier layer are of n-type conductivity, being either entirely undoped or doped with up to about 30 pm of a dopant sufficient to cause said main and intermediate layers to be preferentially p-type conductive.
Claim 3
Dependent Claim
18 words
An electrophotographic element according to claim 1, said intermediate layer having a thickness of at least 3 μm.
Claim 4
Dependent Claim
38 words
An electrophotographic element according to claim 1, said main layer and said intermediate layer each consisting essentially of intrinsic amorphous silicon, said barrier layer and said intermediate barrier layer each consisting essentially of boron-doped p-type conductive amorphous silicon.
Claim 5
Dependent Claim
66 words
An electrophotographic element according to claim 1, said layers respectively being layers of the silicon produced by precipitation thereof from silane gas, and in the case of each doped layer by precipitation thereof from silane gas containing a small proportion of diborane or phosphine, under the influence of a glow-discharge plasma onto a said support being held at a temperature of between 150° and 200° C.
Claim 6
Dependent Claim
36 words
An electrophotographic element according to claim 1, 2, 3, or 4, comprising between said barrier layer and said main layer a plurality of said intermediate layers each having a said intermediate barrier layer applied onto it.
Claim 7
Dependent Claim
32 words
An electrophotographic element according to claim 1, 2, 3, or 4, comprising between said barrier layer and said main layer only one said intermediate layer and only one said intermediate barrier layer.
Claim 8
Dependent Claim
49 words
An electrophotographic element according to claim 6, said barrier layer and said intermediate barrier layer each having a thickness of about 0.1 to 0.3 μm, said intermediate layer having a thickness of at least 3 μm, and said main layer having a thickness of about 2 to 10 μm.
Claim 9
Dependent Claim
59 words
An electrophotographic element according to claim 1, said main layer and said intermediate layer each consisting essentially of hydrogen-containing amorphous silicon doped with up to about 30 ppm of a dopant sufficient to cause said layers to be preferentially p-type conductive, said barrier layer and said intermediate barrier layer each consisting essentially of phosphorous-doped, n-type conductive hydrogen-containing amorphous silicon.
References Cited (Backward Citations)
US4330182B1
Cited
US4330182A
Cited
GB2018446A
Cited
US4342044A
Cited
US4226898A
Cited
US4271328A
Cited
US4378417A
Cited
GB2077451A
Cited
US4443529A
Cited
US4379943A
Cited
US4452874A
Cited
US4452875A
Cited
US4453173A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-01 | 1988-12-31 | 1989-07-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-01 | 1992-12-31 | 1993-07-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-01 | 1996-12-31 | 1997-07-02 | $7700.00 | Window Closed / Lapsed |