US4525919A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Forming sub-micron electrodes by oblique deposition
Assignee: Raytheon Co
•
Filing: 1982-06-16
•
Granted: 1985-07-02
•
Expires: 2002-06-16
Abstract
Abstract A method for forming a field effect transistor having a submicron gate length. A gate electrode is formed by angularly depositing metal through an aperture formed in a thick masking layer. A substrate upon which the gate electrode is to be formed is placed in an apparatus for depositing a stream of evaporated metal through the aperture onto portions of the substrate surface exposed by the aperture. The stream is directed at a selective oblique angle θ with respect to a normal to the surface of such substrate. Portions of the exposed surface of the substrate are shadowed from the obliquely directed stream of evaporated metal by an edge of the aperture formed in the thick masking layer. Thus, only selected portions of such obliquely directed stream of evaporated metal are deposited onto unshadowed portions of the substrate to thereby provide the gate electrode. The width w' of the portion of the gate electrode in contact with the substrate, and hence the gate length of the field effect transistor, is related to the angle θ, the aperture width w, and aperture height h by w'=w (h)(tan θ). Such parameters are selected to provide a gate length which is less than a micron even though the aperture width is greater than or equal to a micron and hence one which can be formed using conventional optical photolithographic techniques. Edges of the masking layer are formed to overhang portions of the sidewall of the aperture to thereby shield such portions of the sidewall, thus providing separation between the evaporated metal deposited through the aperture onto the substrate and the evaporated metal deposited on the masking layer.
Inventors
- 👤 Walter Fabian
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 13:28
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/061; H10D30/0612; H10D64/00; H10D64/01; H10D64/012; H10D64/0124; H10D64/0125; H10D64/0126; Y; Y10; Y10S; Y10S148/00; Y10S148/143; Y10S438/00; Y10S438/942; Y10S438/948; Y10S438/951
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
240 words
A method of forming a conductor having a submicron dimension (w') on an exposed surface of a substrate including the steps of: providing a composite masking layer having a composite thickness (h) over such substrate, further comprising the steps of: depositing a first relatively thick layer of a first resist over the substrate to increase the surface flatness of the substrate, said first resist having a first resolution characteristic; depositing a second relatively thin layer of a second, different resist over the first layer of resist, said second resist having a second resolution characteristic higher than the first characteristic of said first resist; exposing selected portions of said first layer by patterning the second layer of resist to provide a relatively high resolution pattern in such second masking layer having a predetermined dimension (w); etching the underlying portion of said first layer of resist, using the second layer as a mask to provide the exposed portion of the substrate; and depositing selective portions of a stream of metal onto the exposed portion of the substrate at an oblique angle θ with respect to a normal to the surface of the substrate, using the composite mask to shield a portion of the exposed substrate from the obliquely angled stream of metal to form the conductor having the dimension w', where w' is substantially related to the dimension w in the high resolution pattern and the thickness h of the masking layer.
Claim 2
Independent Claim
240 words
A method of forming a conductor having a submicron dimension (w') on an exposed surface of a substrate including the steps of: providing a composite masking layer having a composite thickness (h) over such substrate, further comprising the steps of: depositing a first relatively thick layer of a first resist over the substrate to increase the surface flatness of the substrate, said first resist having a first resolution characteristic; depositing a second relatively thin layer of a second, different resist over the first layer of resist, said second resist having a second resolution characteristic higher than the first characteristic of said first resist; exposing selected portions of said first layer by patterning the second layer of resist to provide a relatively high resolution pattern in such second masking layer having a predetermined dimension (w); etching the underlying portion of said first layer of resist, using the second layer as a mask to provide the exposed portion of the substrate; and depositing selective portions of a stream of metal onto the exposed portion of the substrate at an oblique angle θ with respect to a normal to the surface of the substrate, using the composite mask to shield a portion of the exposed substrate from the obliquely angled stream of metal to form the conductor having the dimension w', where w' is substantially related to the dimension w in the high resolution pattern and the thickness h of the masking layer.
Claim 3
Independent Claim
130 words
A method of forming a field effect transistor on a substrate having source and drain electrodes disposed on source and drain contact regions and a gate electrode therebetween comprising the steps of: providing a composite mask on the substrate comprising first and second different masking layers; forming an aperture in the composite mask exposing a portion of the substrate between the source and drain contact regions and undercutting sidewall portions of said first masking layer to provide overhanging portions of said second masking layer; directing an obliquely angled stream of conductive material at the substrate; and depositing such directed stream of conductive material through the aperture onto the substrate to provide the gate electrode, with said overhanging portions isolating the material of the gate from material deposited on the mask.
Claim 4
Independent Claim
130 words
A method of forming a field effect transistor on a substrate having source and drain electrodes disposed on source and drain contact regions and a gate electrode therebetween comprising the steps of: providing a composite mask on the substrate comprising first and second different masking layers; forming an aperture in the composite mask exposing a portion of the substrate between the source and drain contact regions and undercutting sidewall portions of said first masking layer to provide overhanging portions of said second masking layer; directing an obliquely angled stream of conductive material at the substrate; and depositing such directed stream of conductive material through the aperture onto the substrate to provide the gate electrode, with said overhanging portions isolating the material of the gate from material deposited on the mask.
Claim 5
Independent Claim
130 words
A method of forming a gate electrode for a field effect transistor comprising the steps of: forming a masking layer of resist having a thickness (h) over a substrate; forming an aperture in said masking layer having overhanging portions, with an opening width (w) between said overhanging portions, to expose an underlying portion of the substrate; directing a stream of conductive material toward the substrate at an oblique angle θ with respect to the substrate; depositing the conductive material through the aperture forming the gate electrode having a portion thereof disposed on the substrate, said portion having a dimension (w') substantially equal to w-(h) tan θ, with the overhanging portion shadowing the stream to isolate the conductive material of the gate electrode from conductive material deposited on the masking layer.
Claim 6
Independent Claim
130 words
A method of forming a gate electrode for a field effect transistor comprising the steps of: forming a masking layer of resist having a thickness (h) over a substrate; forming an aperture in said masking layer having overhanging portions, with an opening width (w) between said overhanging portions, to expose an underlying portion of the substrate; directing a stream of conductive material toward the substrate at an oblique angle θ with respect to the substrate; depositing the conductive material through the aperture forming the gate electrode having a portion thereof disposed on the substrate, said portion having a dimension (w') substantially equal to w-(h) tan θ, with the overhanging portion shadowing the stream to isolate the conductive material of the gate electrode from conductive material deposited on the masking layer.
Claim 7
Independent Claim
128 words
A method of forming a gate electrode for a field effect transistor having source and drain electrodes comprising the steps of: providing a masking layer over a substrate; forming an aperture in the masking layer exposing a portion of the substrate between the source and drain regions; directing an obliquely angled stream of conductive material toward the substrate; depositing such directed stream of conductive material onto the masking layer and through the aperture, onto portions of the substrate using the mask to isolate the conductive material deposited on the masking layer from the conductive material deposited within the aperture on the substrate; and then lifting off the masking layer and the conductive material deposited thereon, while leaving the conductive material on the substrate to provide the gate electrode.
Claim 8
Independent Claim
128 words
A method of forming a gate electrode for a field effect transistor having source and drain electrodes comprising the steps of: providing a masking layer over a substrate; forming an aperture in the masking layer exposing a portion of the substrate between the source and drain regions; directing an obliquely angled stream of conductive material toward the substrate; depositing such directed stream of conductive material onto the masking layer and through the aperture, onto portions of the substrate using the mask to isolate the conductive material deposited on the masking layer from the conductive material deposited within the aperture on the substrate; and then lifting off the masking layer and the conductive material deposited thereon, while leaving the conductive material on the substrate to provide the gate electrode.
Claim 9
Dependent Claim
106 words
The method recited in claim 4 wherein the mask forming step further comprises the steps of: depositing a first relatively thick layer of a first resist over the substrate to increase the surface flatness of the substrate; depositing a second relatively thin layer of a second, different resist over the first layer of resist; and wherin the aperture forming step comprises the step of: (i) forming such aperture with portions of the second masking layer overhanging portions of the first masking layer, such overhanging portions of the second masking layer shielding portions of a sidewall of the aperture from the conductive material to provide the isolation.
Claim 10
Dependent Claim
15 words
The method of claim 1 wherein the dimension w' is related to w-(h) tan θ.
Claim 11
Dependent Claim
55 words
The method as recited in claim 1 wherein during the etching step the first layer of resist is etched away to provide overhanging portions of the second masking layer; and wherein during the depositing step the overhanging portions are provided to isolate the metal providing the gate electrode from metal deposited on the composite mask.
References Cited (Backward Citations)
US3920861A
Cited
US3851379A
Cited
US3908262A
Cited
US3846822A
Cited
US3951708A
Cited
US4337115A
Cited
JPS548972A
Cited
US4145459A
Cited
US4194285A
Cited
US4377899A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-01 | 1988-12-31 | 1989-07-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-01 | 1992-12-31 | 1993-07-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-01 | 1996-12-31 | 1997-07-02 | $7700.00 | Window Closed / Lapsed |