US4518457A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Raney alloy coated cathode for chlor-alkali cells
Assignee: Olin Corp
•
Filing: 1982-03-17
•
Granted: 1985-05-21
•
Expires: 2002-03-17
Abstract
Abstract An improved cathode with a conductive metal core and a Raney-type catalytic surface predominantly derived from an adherent Beta nickel (NiAl 3 ) crystalline precursory outer portion of the metal core is disclosed. The precursory outer portion preferably has molybdenum added to give a precursor alloy having the formula Ni x Mo 1-x Al 3 where x is within the range of from about 80 to about 95 weight percent. Also disclosed is a method of producing a low overvoltage cathode. The method includes the steps of taking a Ni-Mo core or substrate having about 5-20 weight percentage of Mo and coating it with aluminum then heat treating to form a Ni-Mo-Al alloy with mostly a Beta nickel structure and then leaching out the Al to produce a Raney surface.
Inventors
- 👤 Thomas J. Gray
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 22:40
CPC Classifications
C; C23; C23C; C23C10/00; C23C10/60; C25; C25B; C25B11/00; C25B11/04; C25B11/051; C25B11/073; C25B11/091
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
194 words
A method of producing a monolithic, non-pyrophoric, low overvoltage electrode for use as a hydrogen evolution cathode for the electrolysis of brine in an electrolytic cell which comprises the steps of: (a) coating with aluminum the surface of a clean, non-porous conductive metal substrate comprised of a nickel-molybdenum alloy having a weight percent molybdenum within the range of from about 5 to about 20 and a weight percent nickel within the range of from about 80 to about 95; (b) heat treating said coated surface by maintaining said surface at a temperature within the range of from about 660° C. to about 860° C. for a time about 1 to about 30 minutes to diffuse a portion of said aluminum into outer portions of said structure to produce an integral nickel-molybdenum-aluminum alloy larger in said outer portions predominantly of Beta phase grains but insufficient to create a predominance of Gamma phase grains in said outer portions; (c) leaching out residual aluminum and intermetallics from the alloy layer until a porous Raney nickel-molybdenum layer is formed integral with said structure; and (d) chemically treating said Raney nickel-molybdenum layer so that said layer is substantially non-pyrophoric.
Claim 2
Independent Claim
194 words
A method of producing a monolithic, non-pyrophoric, low overvoltage electrode for use as a hydrogen evolution cathode for the electrolysis of brine in an electrolytic cell which comprises the steps of: (a) coating with aluminum the surface of a clean, non-porous conductive metal substrate comprised of a nickel-molybdenum alloy having a weight percent molybdenum within the range of from about 5 to about 20 and a weight percent nickel within the range of from about 80 to about 95; (b) heat treating said coated surface by maintaining said surface at a temperature within the range of from about 660° C. to about 860° C. for a time about 1 to about 30 minutes to diffuse a portion of said aluminum into outer portions of said structure to produce an integral nickel-molybdenum-aluminum alloy larger in said outer portions predominantly of Beta phase grains but insufficient to create a predominance of Gamma phase grains in said outer portions; (c) leaching out residual aluminum and intermetallics from the alloy layer until a porous Raney nickel-molybdenum layer is formed integral with said structure; and (d) chemically treating said Raney nickel-molybdenum layer so that said layer is substantially non-pyrophoric.
Claim 3
Dependent Claim
17 words
The method of claim 1 wherein said heat treating time is no more than about 10 minutes.
Claim 4
Dependent Claim
25 words
The method of claim 1 wherein said temperature maintained during heat treating is within the range of from about 700° C. to about 750° C.
Claim 5
Dependent Claim
21 words
The method of claim 1 wherein said temperature is within the range of from about 715° C. to about 735° C.
Claim 6
Dependent Claim
35 words
The method of claim 1 wherein said coating step is applied by dipping said structure into molten aluminum at a temperature within the range of from about 650° to about 675° C. for 1-2 minutes.
Claim 7
Dependent Claim
29 words
The method of claim 1 wherein said conductive base metal structure contains from about 12 to about 18 percent molybdenum and from about 82 to about 88 percent nickel.
Claim 8
Dependent Claim
22 words
The method of claim 1 wherein said coated surface is maintained at said temperature for from about 5 to about 15 minutes.
Claim 9
Dependent Claim
16 words
The method of claim 1 wherein said heat treating is carried out in an inert atmosphere.
Claim 10
Dependent Claim
73 words
The method of claim 1 wherein said chemical treatment comprises immersing said cathode for a time between about 1 hour and about 4 hours in a dilute aqueous solution selected from the group consisting of: (a) about 3 percent by weight NaNO 3 ; (b) about 3 percent by weight K 2 Cr 2 O 7 ; or (c) about 3 percent by weight NaClO 3 with about 10 percent by weight NaOH.
Claim 11
Dependent Claim
23 words
The method of claim 1 further comprising the step of coating a thin layer of nickel onto the porous surface of said cathode.
Claim 12
Dependent Claim
18 words
The method of claim 10 wherein said nickel layer is between about 5 to about 10 microns thick.
Claim 13
Independent Claim
148 words
A method of substantially eliminating iron fouling of the surface of a cathode used for the electrolysis of brine in a chlor-alkali cell which comprises employing as said cathode a monolithic cathode comprised of a non-porous conductive metal substrate having as an exterior surface an ordered orthorhombic Beta phase crystal structure which is integral with and derived from said substrate and is represented by the formula Ni x Mo 1-x Al 3 , where x is the weight percent of nickel in the combined weight of nickel and molybdenum, and x ranges from about 80 to about 95 percent by weight, and leaching from about 75 to about 95 percent of aluminum from said surface with a strong aqueous base to form an active porous Raney nickel-molybdenum surface layer, whereby the hydrogen overvoltage of said surface is reduced to a non-fouling level of less than about 140 millivolts.
Claim 14
Independent Claim
148 words
A method of substantially eliminating iron fouling of the surface of a cathode used for the electrolysis of brine in a chlor-alkali cell which comprises employing as said cathode a monolithic cathode comprised of a non-porous conductive metal substrate having as an exterior surface an ordered orthorhombic Beta phase crystal structure which is integral with and derived from said substrate and is represented by the formula Ni x Mo 1-x Al 3 , where x is the weight percent of nickel in the combined weight of nickel and molybdenum, and x ranges from about 80 to about 95 percent by weight, and leaching from about 75 to about 95 percent of aluminum from said surface with a strong aqueous base to form an active porous Raney nickel-molybdenum surface layer, whereby the hydrogen overvoltage of said surface is reduced to a non-fouling level of less than about 140 millivolts.
Claim 15
Dependent Claim
147 words
The method of claim 12 wherein said generating step comprises the steps of: (a) coating the surface of a clean, non-porous conductive base metal structure of an alloy of from about 5 to about 20 percent molybdenum and from about 80 to about 95 percent nickel with aluminum; (b) heat treating said coated surface by maintaining said surface at a temperature within the range of from about 660° C. to about 860° C. for a time of about 1 to about 30 minutes to diffuse said aluminum into outer portions of said structure to produce an integral nickel-molybdenum-aluminum alloy layer in said outer portions predominantly of Beta phase grains but insufficient to create a predominance of Gamma phase grains in said outer portions; and (c) leaching out residual aluminum and intermetallics from the alloy layer until a porous Raney nickel-molybdenum layer is formed integral with said structure.
Claim 16
Dependent Claim
17 words
The method of claim 13 wherein said heat treating time is no more than about 10 minutes.
Claim 17
Dependent Claim
25 words
The method of claim 14 wherein said temperature maintained during heat treating is within the range of from about 700° C. to about 750° C.
Claim 18
Dependent Claim
25 words
The method of claim 15 wherein said temperature maintained during heat treating is within the range of from about 715° C. to about 735° C.
Claim 19
Dependent Claim
13 words
The method of claim 12 wherein said overvoltage is reduced below 80 millivolts.
Claim 20
Dependent Claim
13 words
The method of claim 17 wherein said overvoltage is reduced below 60 millivolts.
Claim 21
Dependent Claim
14 words
The method of claim 12 wherein x ranges from about 82 to about 88.
References Cited (Backward Citations)
US2948687A
Cited
US3674710A
Cited
US3627790A
Cited
US4154705A
Cited
US4049580A
Cited
US4043946A
Cited
US4116804A
Cited
US4224248A
Cited
US4162204A
Cited
US4248679A
Cited
US4248680A
Cited
US4323595A
Cited
US4251478A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-05-20 | 1988-11-19 | 1989-05-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-05-20 | 1992-11-19 | 1993-05-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-05-20 | 1996-11-19 | 1997-05-21 | $7700.00 | Window Closed / Lapsed |