Plated metallic cathode
Assignee: Olin Corp
•
Filing: 1978-04-03
•
Granted: 1979-07-24
•
Expires: 1998-04-03
Abstract
Abstract A highly conductive and corrosion resistant low hydrogen overvoltage cathode. The cathode comprises a copper substrate plated with an alloy of nickel and molybdenum.
Inventors
- 👤 Han C. Kuo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 16:30
CPC Classifications
C; C25; C25D; C25D3/00; C25D3/02; C25D3/56; C25B; C25B11/00; C25B11/04; C25B11/051; C25B11/073; C25B11/091; C25D5/00; C25D5/10; C25D5/34; C25D5/60; C25D5/605; C25D5/615; C25D5/617; C25D5/623; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12806; Y10T428/12826; Y10T428/12861; Y10T428/12903
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
162 words
Electrolytic method for producing a catalytically coated cathode for an electrolytic cell for the production of an alkali metal hydroxide and halogen gas from an alkali metal halide, said method comprising the steps of: (a) forming an aqueous solution of alkali metal molybdate at a concentration of 1-40 grams/liter, nickel salts and a complexing agent selected from the group consisting of alkali metal citrates and alkali metal pyrophosphates with proportions adjusted so that the resultant coating contains more than 50 percent by weight of molybdenum, (b) adjusting the pH between 9 and 11, (c) locating a clean support formed of a metal selected from the group consisting of copper and copper base alloys at the cathode in an electrolytic bath of said aqueous solution, and (d) passing current in said bath with a cathodic current density of 0.4 A/dm 2 to 50 A/dm 2 for a duration sufficient to make said resultant coating from about 1 μm to about 5 μm thick.
Claim 2
Dependent Claim
162 words
Electrolytic method for producing a catalytically coated cathode for an electrolytic cell for the production of an alkali metal hydroxide and halogen gas from an alkali metal halide, said method comprising the steps of: (a) forming an aqueous solution of alkali metal molybdate at a concentration of 1-40 grams/liter, nickel salts and a complexing agent selected from the group consisting of alkali metal citrates and alkali metal pyrophosphates with proportions adjusted so that the resultant coating contains more than 50 percent by weight of molybdenum, (b) adjusting the pH between 9 and 11, (c) locating a clean support formed of a metal selected from the group consisting of copper and copper base alloys at the cathode in an electrolytic bath of said aqueous solution, and (d) passing current in said bath with a cathodic current density of 0.4 A/dm 2 to 50 A/dm 2 for a duration sufficient to make said resultant coating from about 1 μm to about 5 μm thick.
Claim 3
Dependent Claim
19 words
The method of claim 1 wherein said aqueous solution also contains ferrous salts in the amount of 5-15 grams/liter.
Claim 4
Dependent Claim
19 words
The method of claim 1 wherein said current is passed in said bath for from 10 to 90 minutes.
Claim 5
Dependent Claim
23 words
The method of claim 1, 2 or 3 wherein said cathodic current density is from 3 A/dm 2 to 5 A/dm 2 .
Claim 6
Dependent Claim
19 words
The method of claim 4 wherein said current is passed in said bath for from 50 to 70 minutes.
Claim 7
Dependent Claim
27 words
The method of claim 1, wherein said concentration of said alkali metal molybdate is 2-20 grams/liter so that the resultant coating contains 60-75 percent by weight molybdenum.
References Cited (Backward Citations)
US3947331A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-07-23 | 1983-01-22 | 1983-07-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-07-23 | 1987-01-22 | 1987-07-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-07-23 | 1991-01-22 | 1991-07-24 | $7700.00 | Window Closed / Lapsed |