Process for preparing multilayer fibrous structures and product
Assignee: Montedison SpA
•
Filing: 1984-03-12
•
Granted: 1985-02-19
•
Expires: 2004-03-12
Abstract
Abstract Composite sheets comprising a layer of cellulosic fibers and a layer adjacent thereto consisting in whole or in part of thermoplastic fibers are made to adhere by superimposing the sheets on the side of the cellulosic fibers layer and by inserting between such layers a film of a thermoplastic polymer having: (a) a melting temperature lower than the melting temperature of the polymer forming the thermoplastic synthetic fibres contained in the layer adjacent to the cellulosic layer, intended for the adhesion, of the composite sheet; (b) a viscosity in the molten state-measured in a capillary viscosimeter, at a velocity gradient equal to or lower than 10-1 seconds, and at a temperature comprised between a temperature higher by 10 DEG C. than the melting temperature of such polymer and a temperature higher by 20 DEG C. than the melting temperature of the abovesaid thermoplastic fibres-lower than 1x108 poises, and preferably lower than 1x105 poises; (c) a surface tension not exceeding by more than 5 dynes/cm the surface tension of the polymer forming such thermoplastic fibres, measured at the same temperature; (d) a solubility parameter, at a temperature of 25 DEG C., in a ratio of from 0.8 to 1.15, extremes included, to the solubility parameter of the polymer forming such thermoplastic fibres; and by heating the whole at a temperature ranging from a temperature exceeding by 10 DEG C. the melting temperature of the polymer forming such film to a temperature exceeding by 20 DEG C. the melting temperature of the polymer forming the synthetic fibres existing in the layer which is adjacent to the cellulosic fibre layer, intended for the adhesion, of the composite sheet.
Inventors
- 👤 Lino Credali
- 👤 Emilio Martini
- 👤 Domenico Lori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 18:18
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/26; B32B29/00; B32B29/02; B32B38/00; B32B38/0036; B32B7/00; B32B7/04; B32B7/12; D; D21; D21H; D21H11/00; D21H11/02; D21H11/04; D21H13/00; D21H13/10; D21H13/12; D21H13/14; D21H27/00; D21H27/30; D21H27/32; D21H27/34; D21H27/36; D21H27/38; B32B2262/00; B32B2262/02; B32B2262/06; B32B2262/062; B32B2439/00; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31855; Y10T428/3188; Y10T428/31895; Y10T428/31899; Y10T428/31902; Y10T428/31971; Y10T428/31975; Y10T428/31978; Y10T442/00; Y10T442/60; Y10T442/659; Y10T442/668
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
313 words
A process for bonding, by means of thermoadhesion, sheets or layers of cellulosic fibres, which comprises the following steps: (1) preparing composite waterlaid sheets consisting of at least two layers, one consisting essentially of cellulosic fibres and the other, adjacent to the first one, formed by fibres of a thermoplastic synthetic polymer, or of blends of such fibres with up to 95% by weight of cellulosic fibres; (2) superimposing two of such sheets on the side of the essentially cellulosic fibre layer, with inserted between them a film of at least a thermoplastic polymer having the following characteristics: (a) a melting temperature lower than the melting temperature of the polymer constituting the thermoplastic synthetic fibres contained in the layer adjacent to the one consisting of cellulosic fibres; (b) a viscosity in the molten state, measured in a capillary viscosimeter, at a velocity gradient lower than or equal to 10 -1 seconds and at a temperature comprised between a temperature higher by 10° C. than the melting temperature of such thermoplastic polymer and a temperature higher by 20° C. than the melting temperature of the polymer forming such thermoplastic synthetic fibres, lower than 1.10 8 poises; (c) a surface tension not exceeding by more than 5 dynes/cm the one of the polymer constituting such thermoplastic synthetic fibres, measured at the same temperature; (d) a solubility parameter which is in a ratio to the solubility parameter of the thermoplastic polymer constituting such synthetic fibres ranging from 0.85 to 1.15, extremes included, at a temperature of 25° C.; (3) heating the aggregate of the so superimposed sheets and film at a temperature ranging from a temperature exceeding by 10° C. the melting temperature of the polymer forming the film to a temperature exceeding by 20° C. the melting temperature of the polymer forming such thermoplastic fibres; (4) compressing the aggregate at a temperature within such range.
Claim 2
Dependent Claim
313 words
A process for bonding, by means of thermoadhesion, sheets or layers of cellulosic fibres, which comprises the following steps: (1) preparing composite waterlaid sheets consisting of at least two layers, one consisting essentially of cellulosic fibres and the other, adjacent to the first one, formed by fibres of a thermoplastic synthetic polymer, or of blends of such fibres with up to 95% by weight of cellulosic fibres; (2) superimposing two of such sheets on the side of the essentially cellulosic fibre layer, with inserted between them a film of at least a thermoplastic polymer having the following characteristics: (a) a melting temperature lower than the melting temperature of the polymer constituting the thermoplastic synthetic fibres contained in the layer adjacent to the one consisting of cellulosic fibres; (b) a viscosity in the molten state, measured in a capillary viscosimeter, at a velocity gradient lower than or equal to 10 -1 seconds and at a temperature comprised between a temperature higher by 10° C. than the melting temperature of such thermoplastic polymer and a temperature higher by 20° C. than the melting temperature of the polymer forming such thermoplastic synthetic fibres, lower than 1.10 8 poises; (c) a surface tension not exceeding by more than 5 dynes/cm the one of the polymer constituting such thermoplastic synthetic fibres, measured at the same temperature; (d) a solubility parameter which is in a ratio to the solubility parameter of the thermoplastic polymer constituting such synthetic fibres ranging from 0.85 to 1.15, extremes included, at a temperature of 25° C.; (3) heating the aggregate of the so superimposed sheets and film at a temperature ranging from a temperature exceeding by 10° C. the melting temperature of the polymer forming the film to a temperature exceeding by 20° C. the melting temperature of the polymer forming such thermoplastic fibres; (4) compressing the aggregate at a temperature within such range.
Claim 3
Dependent Claim
76 words
The process according to claim 1, in which the heating and/or compression operation of the aggregate is accomplished at a temperature ranging from a temperature higher by 10° C. than the melting temperature of the polymer forming the film to the melting temperature of the polymer forming such thermoplastic synthetic fibres when the melting temperature of the film polymer is lower by at least 10° C. than the melting temperature of the polymer of such fibres.
Claim 4
Dependent Claim
35 words
The process according to claims 1 and 2, in which such thermoplastic synthetic fibres are at least in part in the form of fibrils having a surface area of at least 1 m 2 /g.
Claim 5
Dependent Claim
24 words
The process according to claim 1, in which the viscosity in the molten state of the thermoplastic polymer is lower than 1.10 5 poises.
Claim 6
Dependent Claim
16 words
The process according to claim 1, in which the thermoplastic polymer constituting the film is polyethylene.
Claim 7
Dependent Claim
52 words
The process according to claim 1, in which the thermoplastic polymer constituting the film is low-density polyethylene, and the thermoplastic synthetic fibres contained in the layer adjacent to the cellulose fibre layer to be made to adhere are high-density polyethylene fibrils having a surface area of at least 1 m 2 /g.
Claim 8
Dependent Claim
29 words
The process according to claim 6, in which heating operation (3) and/or compressione operation (4) are carried out at a temperature ranging from about 120° to about 135° C.
Claim 9
Dependent Claim
51 words
The process according to claim 1, in which the thermoplastic polymer constituting the film is high-density polyethylene, and the thermoplastic synthetic fibres contained in the layer adjacent to the cellulosic fibre layer to be made to adhere are polypropylene fibrils having a surface area of at least 1 m 2 /g.
Claim 10
Dependent Claim
27 words
The process according to claim 8, in which heating operation (3) and/or compression operation (4) are conducted at a temperature ranging from 145° C. to 165° C.
Claim 11
Dependent Claim
35 words
The process according to claim 1, in which the sheets utilized for superimposition operation (2) have been previously subjected to heating, and optionally to compression, with melting of the thermoplastic synthetic fibres present the rein.
Claim 12
Dependent Claim
36 words
The process according to claim 1, in which the cellulosic fibre layer present in the composite sheets has a weight of from 40 to 120 g/m 2 and a density of from 0.6 to 0.8 g/cc.
Claim 13
Dependent Claim
44 words
The process according to claim 1, in which the layer containing the thermoplastic synthetic fibres, which is present in the composite sheets and is adjacent to the cellulosic fibre layer intended for adhesion, has a weight comprised between 40 and 120 g/m 2 .
Claim 14
Dependent Claim
10 words
Bonded articles obtained by the process according to claim 1.
References Cited (Backward Citations)
US2077016A
Cited
US2500282A
Cited
US3256138A
Cited
US3501369A
Cited
US3560324A
Cited
US3684643A
Cited
US3790417A
Cited
US3935047A
Cited
US4212703A
Cited
US4081582A
Cited
US4318774A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-02-19 | 1988-08-20 | 1989-02-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-02-19 | 1992-08-20 | 1993-02-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-02-19 | 1996-08-20 | 1997-02-19 | $7700.00 | Window Closed / Lapsed |