Fibrous material and method of making the same
Assignee: Johnson and Johnson
•
Filing: 1976-10-20
•
Granted: 1978-03-28
•
Expires: 1996-10-20
Abstract
Abstract A high loft, low density, nonwoven fibrous material is provided comprising two layers of irregularly arranged, intersecting, overlapping, mechanically interengaged, loosely assembled fibers, one of the layers including thermoplastic synthetic wood pulp fibers at least in the portion thereof at the interface to the other layer, at least some of the thermoplastic synthetic wood pulp fibers in the one layer being in contact with and fused with segments of fibers of said other layer. The material is produced by air-laying the aforementioned layers successively so that some thermoplastic synthetic wood pulp fibers in one layer are in contact with some fibers in the other layer, and then applying heat without pressure to fuse and bond at least some of the thermoplastic synthetic wood pulp fibers in one layer to fibers in the other layer.
Inventors
- 👤 George A. M. Butterworth
- 👤 Robert T. Elias
- 👤 Wayne D. Miller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 18:13
CPC Classifications
D; D04; D04H; D04H1/00; D04H1/40; D04H1/42; D04H1/4391; D04H1/43918; B; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/26; A; A61; A61F; A61F13/00; A61F13/15; A61F13/53; A61F13/539; A61L; A61L15/00; A61L15/16; A61L15/22; A61L15/28; B32B38/00; B32B38/0036; B32B5/02; B32B5/08; D04H1/425; D04H1/4258; D04H1/4374; D04H1/4382; D04H1/43835; D04H1/58; D04H1/60; D21; D21H; D21H13/00; D21H27/00; D21H27/30; D21H5/00; D21H5/26; D21H5/2607; D21H5/2628; D21H5/2642; D21H5/2678; A61F13/534; A61F2013/15008; A61F2013/15048; A61F2013/15073; A61F13/15577; A61F2013/15821; A61F13/51; A61F2013/51002; A61F2013/51038; A61F2013/51042; A61F2013/530131; A61F2013/530182; A61F2013/530218; A61F2013/530481; A61F2013/530583; A61F2013/530635; A61F2013/53445; B32B2250/00; B32B2250/20; B32B2307/00; B32B2307/50; B32B2307/554; B32B2432/00; B32B2555/00; B32B2555/02; Y; Y10; Y10S; Y10S428/00; Y10S428/913; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31971; Y10T428/31975; Y10T428/31978; Y10T428/31982; Y10T428/31989; Y10T442/00; Y10T442/20; Y10T442/2861; Y10T442/60; Y10T442/659; Y10T442/666
Claims Analysis
Total Claims: 42
Claim 1
Independent Claim
434 words
A method of producing a high loft, low density, nonwoven fibrous material having thermoplastic synthetic wood pulp fibers in at least one region of said material parallel to or including its median plane which comprises: bringing together a first layer of irregularly arranged, intersecting, overlapping, mechanically interengaged, loosely assembled fibers defining interstices therebetween, said fibers including fibers other than thermoplastic synthetic wood pulp fibers, said layer of fibers having free fiber ends extending outwardly from at least one boundary surface of the layer, with a second layer of similarly disposed fibers, said second layer including at least thermoplastic synthetic wood pulp fibers and optionally, other fibers, said thermoplastic synthetic wood pulp fibers located at least in surface portions of said layer immediately adjacent said one boundary surface of the first layer and having free fiber ends extending outwardly therefrom, to bring at least some of the fiber segments of thermoplastic synthetic wood pulp fibers of said second layer into contact with said first layer of fibers of inserting free fiber ends from at least one of said layers into interstices between fibers in the other of said layers, thermoplastic synthetic wood pulp fibers that are mechanically interengaged with other fibers in the second layer being present at the boundary surface of said layer adjacent said first layer in a quantity sufficient to occupy at least about 10 percent of the area occupied by exposed fiber segments contained in the second layer at its said boundary surface, at least some of the interstices between fibers of said first layer being of a width at least twice as large as the mean diameter of said thermoplastic synthetic wood pulp fibers in said second layer, at least some of the interstices between fibers of said second layer being of a width at least twice as large as the mean diameter of the fibers in said first layer, said thermoplastic synthetic wood pulp fibers in the second layer having a melting point lower than the melting point or degradation temperature of every other type of fibers contained in said two layers; and applying heat in the absence of pressure at least to the portions of said two fibrous layers in which thermoplastic synthetic wood pulp fibers of said second layer that are in contact with fibers of said first layer are located, to fuse and bond at least some of said contacting thermoplastic synthetic wood pulp fibers to fibers of said first layer and thereby produce a fibrous material of good stability and mechanical integrity, which displays excellent resistance to delamination as well as good hand and softness.
Claim 2
Independent Claim
434 words
A method of producing a high loft, low density, nonwoven fibrous material having thermoplastic synthetic wood pulp fibers in at least one region of said material parallel to or including its median plane which comprises: bringing together a first layer of irregularly arranged, intersecting, overlapping, mechanically interengaged, loosely assembled fibers defining interstices therebetween, said fibers including fibers other than thermoplastic synthetic wood pulp fibers, said layer of fibers having free fiber ends extending outwardly from at least one boundary surface of the layer, with a second layer of similarly disposed fibers, said second layer including at least thermoplastic synthetic wood pulp fibers and optionally, other fibers, said thermoplastic synthetic wood pulp fibers located at least in surface portions of said layer immediately adjacent said one boundary surface of the first layer and having free fiber ends extending outwardly therefrom, to bring at least some of the fiber segments of thermoplastic synthetic wood pulp fibers of said second layer into contact with said first layer of fibers of inserting free fiber ends from at least one of said layers into interstices between fibers in the other of said layers, thermoplastic synthetic wood pulp fibers that are mechanically interengaged with other fibers in the second layer being present at the boundary surface of said layer adjacent said first layer in a quantity sufficient to occupy at least about 10 percent of the area occupied by exposed fiber segments contained in the second layer at its said boundary surface, at least some of the interstices between fibers of said first layer being of a width at least twice as large as the mean diameter of said thermoplastic synthetic wood pulp fibers in said second layer, at least some of the interstices between fibers of said second layer being of a width at least twice as large as the mean diameter of the fibers in said first layer, said thermoplastic synthetic wood pulp fibers in the second layer having a melting point lower than the melting point or degradation temperature of every other type of fibers contained in said two layers; and applying heat in the absence of pressure at least to the portions of said two fibrous layers in which thermoplastic synthetic wood pulp fibers of said second layer that are in contact with fibers of said first layer are located, to fuse and bond at least some of said contacting thermoplastic synthetic wood pulp fibers to fibers of said first layer and thereby produce a fibrous material of good stability and mechanical integrity, which displays excellent resistance to delamination as well as good hand and softness.
Claim 3
Dependent Claim
37 words
The method of claim 1 in which said second layer containing thermoplastic synthetic wood pulp fibers is a base layer supported to expose one boundary surface thereof for positioning of the fibers of said first layer thereon.
Claim 4
Dependent Claim
32 words
The method of claim 2 in which said first layer of fibers is simultaneously formed and positioned upon said base layer containing thermoplastic synthetic wood pulp fibers by an air deposition process.
Claim 5
Dependent Claim
69 words
The method of claim 2 in which said first layer of fibers is positioned upon said base layer containing thermoplastic synthetic wood pulp fibers in the form of a self-supporting web of fibers, and said two fibrous layers are vibrated as they are supported in contact with each other, to produce relative movement of the respective fibers of said two layers in the plane of the interface between them.
Claim 6
Dependent Claim
37 words
The method of claim 1 in which said first layer is a base layer supported to expose one boundary surface thereof for positioning of the fibers of said second layer containing thermoplastic synthetic wood pulp fibers thereon.
Claim 7
Dependent Claim
32 words
The method of claim 5 in which said second layer of fibers containing thermoplastic synthetic wood pulp fibers is simultaneously formed and positioned upon said base layer by an air deposition process.
Claim 8
Dependent Claim
68 words
The method of claim 5 in which said layer of fibers containing thermoplastic synthetic wood pulp fibers is positioned upon said base layer in the form of a self-supporting web of fibers, and said two fibrous layers are vibrated as they are supported in contact with each other, to produce relative movement of the respective fibers of said two layers in the plane of the interface between them.
Claim 9
Dependent Claim
106 words
The method of claim 1 in which fibers of thermoplastic synthetic wood pulp in said second layer that is brought together with said first layer in the first step of said method are arranged in overlapping contact engagement with other synthetic wood pulp fibers in said second layer to trace a multiplicity of continuous fiber paths extending from one edge of said second layer to the opposite edge in a generally transverse direction across said material, sas well as a multiplicity of continuous fiber paths extending from another edge of said layer to the edge opposite thereto in a direction generally normal to said first direction.
Claim 10
Dependent Claim
75 words
The method of claim 8 in which said thermoplastic synthetic wood pulp fibers in said second layer that is brought together with said first layer in the first step of said method include a multiplicity of configurations of fiber segments in in which said segments lie in intersecting, overlapping relationship with one another, each of said configurations being at least three fiber segments in thickness measured perpendicularly to the median plane of said second layer.
Claim 11
Dependent Claim
40 words
The fibrous material of claim 9 in which the thickness of said second layer that is brought together with said first layer in the first step of said method is a minor fraction of the thickness of said first layer.
Claim 12
Dependent Claim
77 words
The method of claim 1 in which substantially all the fibers in said second layer that is brought together with said first layer in the first step of said method are thermoplastic synthetic wood pulp fibers, and said thermoplastic synthetic wood pulp fibers are substantially free of configurations of fiber segments in which said segments lie in intersecting, overlapping relationship more than two fiber segments in thickness measured perpendicularly to the median plane of said second layer.
Claim 13
Dependent Claim
83 words
The method of claim 1 in which thermoplastic synthetic wood pulp fibers that are mechanically interengaged with other fibers in said second fibrous layer are present at the boundary surface of said layer that is adjacent said first layer, when the second layer is brought together with it in the first step of said method, in a quantity sufficient to constitute at least about 15 percent of the area occupied by exposed fiber segments contained in said second layer at said boundary surface.
Claim 14
Dependent Claim
83 words
The method of claim 1 in which thermoplastic synthetic wood pulp fibers that are mechanically interengaged with other fibers in said second fibrous layer are present at the boundary surface of said layer that is adjacent said first layer, when the second layer is brought together with it in the first step of said method, in a quantity sufficient to constitute at least about 20 percent of the area occupied by exposed fiber segments contained in said second layer at said boundary surface.
Claim 15
Dependent Claim
81 words
The method of claim 1 in which thermoplastic synthetic wood pulp fibers are present in the portions of said second layer at its boundary surface remote from said first layer, when said two layers are brought together in the first step of said method, in a quantity sufficient to constitute at least about 10 percent by weight of the fibers in said remote boundary surface portions, whereby said fibrous material is provided good resistance to abrasion at its said remote surface.
Claim 16
Dependent Claim
81 words
The method of claim 1 in which thermoplastic synthetic wood pulp fibers are present in the portions of said second layer at its boundary surface remote from said first layer, when said two layers are brought together in the first step of said method, in a quantity sufficient to constitute at least about 15 percent by weight of the fibers in said remote boundary surface portions, whereby said fibrous material is provided good resistance to abrasion at its said remote surface.
Claim 17
Dependent Claim
81 words
The method of claim 1 in which thermoplastic synthetic wood pulp fibers are present in the portions of said second layer at its boundary surface remote from said first layer, when said two layers are brought together in the first step of said method, in a quantity sufficient to constitute at least about 20 percent by weight of the fibers in said remote boundary surface portions, whereby said fibrous material is provided good resistance to abrasion at its said remote surface.
Claim 18
Dependent Claim
95 words
The method of claim 1 in which the external boundary surface portions of said first layer that are adjacent said second layer when said two layers are brought together in the first step of said method also contain thermoplastic synthetic wood pulp fibers, at least some of which are mechanically interengaged with other fibers of the first layer, in a quantity equal to at least about 5 percent by weight of the portion of the first layer extending from the innermost thermoplastic synthetic wood pulp fibers to said external boundary surface of the first layer.
Claim 19
Dependent Claim
34 words
The method of claim 1 in which nonwettable thermoplastic synthetic wood pulp fibers are included in said second layer that is brought together with said first layer in the first step of said method.
Claim 20
Dependent Claim
36 words
The method of claim 1 in which the only thermoplastic synthetic wood pulp fibers included in said second layer that is brought together with said first layer in the first step of said method are nonwettable.
Claim 21
Dependent Claim
45 words
The method of claim 1 in which the heating step described therein is carried out by applying radiant heat in the absence of pressure at least to the portions of said first and second layers that lie immediately adjacent the interface between said two layers.
Claim 22
Dependent Claim
20 words
The method of claim 20 in which radiant heat is applied in the absence of pressure throughout said two layers.
Claim 23
Dependent Claim
36 words
The method of claim 1 in which following said heating step a binder is introduced into said two layers, and is thereafter activated to bond individual fiber segments to each other in both of said layers.
Claim 24
Dependent Claim
15 words
The method of claim 22 in which said binder is distributed throughout both said layers.
Claim 25
Dependent Claim
331 words
A high loft, low density, non-woven fibrous material of good stability and mechanical integrity, excellent resistance to delamination, and good hand and softness, which comprises a first layer of irregularly arranged, intersecting, overlapping, mechanically interengaged, loosely assembled fibers defining interstices therebetween, said fibers including fibers other than thermoplastic synthetic wood pulp fibers, and a second layer of similarly disposed fibers in firm engagement with said first layer at an interface therebetween, said second layer including, at least thermoplastic synthetic wood pulp fibers and optionally, other fibers, said thermoplastic synthetic wood pulp fibers located at least in portions of said second layer adjacent said interface between said two layers, thermoplastic synthetic wood pulp fibers that are mechanically interengaged with other fibers in said second layer being present in the portions of said layer at said interface between the two layers in a quantity sufficient to occupy at least about 10 percent of the area occupied by fiber segments contained in said second layer at said interface, fibers of at least one of said two layers extending across the interface between the two layers with free end portions of said fibers positioned within interstices between fibers in the other of said layers, at least some of the interstices between fibers of said first layer being of a width at least twice as large as the mean diameter of said synthetic wood pulp fibers in said second layer, at least some of the interstices between fibers of said second layer being of a width at least twice as large as the mean diameter of the fibers in said fiber layer, segments of at least some of the thermoplastic synthetic wood pulp fibers in said second layer being in contact with and heat fused with segments of fibers of said first layer, said thermoplastic synthetic wood pulp fibers in the second layer having a melting point lower than the melting point or degradation temperature of every other type of fibers contained in said two layers.
Claim 26
Dependent Claim
331 words
A high loft, low density, non-woven fibrous material of good stability and mechanical integrity, excellent resistance to delamination, and good hand and softness, which comprises a first layer of irregularly arranged, intersecting, overlapping, mechanically interengaged, loosely assembled fibers defining interstices therebetween, said fibers including fibers other than thermoplastic synthetic wood pulp fibers, and a second layer of similarly disposed fibers in firm engagement with said first layer at an interface therebetween, said second layer including, at least thermoplastic synthetic wood pulp fibers and optionally, other fibers, said thermoplastic synthetic wood pulp fibers located at least in portions of said second layer adjacent said interface between said two layers, thermoplastic synthetic wood pulp fibers that are mechanically interengaged with other fibers in said second layer being present in the portions of said layer at said interface between the two layers in a quantity sufficient to occupy at least about 10 percent of the area occupied by fiber segments contained in said second layer at said interface, fibers of at least one of said two layers extending across the interface between the two layers with free end portions of said fibers positioned within interstices between fibers in the other of said layers, at least some of the interstices between fibers of said first layer being of a width at least twice as large as the mean diameter of said synthetic wood pulp fibers in said second layer, at least some of the interstices between fibers of said second layer being of a width at least twice as large as the mean diameter of the fibers in said fiber layer, segments of at least some of the thermoplastic synthetic wood pulp fibers in said second layer being in contact with and heat fused with segments of fibers of said first layer, said thermoplastic synthetic wood pulp fibers in the second layer having a melting point lower than the melting point or degradation temperature of every other type of fibers contained in said two layers.
Claim 27
Dependent Claim
57 words
The fibrous material of claim 24 in which thermoplastic synthetic wood pulp fibers of said second fibrous layer extend across the interface between said two layers, with free end portions of said fibers positioned within interstices between fibers in said first layer, where they are in contact with and heat fused with fibers of said first layer.
Claim 28
Dependent Claim
57 words
The fibrous material of claim 24 in which fibers of said first fibrous layer extend across the interface between said two layers, with free end portions of said fibers positioned within interstices between fibers in said second layer, where they are in contact with and heat fused with thermoplastic synthetic wood pulp fibers of said second layer.
Claim 29
Dependent Claim
90 words
The fibrous material of claim 24 in which thermoplastic synthetic wood pulp fibers in said second layer are arranged in overlapping contact engagement with other thermoplastic synthetic wood pulp fibers in said layer to trace a multiplicity of continuous fiber paths extending from one edge of said material to the opposite edge in a generally transverse direction across said material, as well as a multiplicity of continuous fiber paths extending from another edge of said material to the edge opposite thereto in a direction generally normal to said first direction.
Claim 30
Dependent Claim
60 words
The fibrous material of claim 27 in which the thermoplastic synthetic wood pulp fibers in said second layer include a multiplicity of configurations of fiber segments in which said segments lie in intersecting, overlapping relationship with one another, each of said configurations being at least three fiber segments in thickness measured perpendicularly to the median plane of said second layer.
Claim 31
Dependent Claim
27 words
The fibrous material of claim 28 in which the thickness of said second fibrous layer is a minor fraction of the thickness of said first fibrous layer.
Claim 32
Dependent Claim
63 words
The fibrous material of claim 24 in which substantailly all the fibers in said second layer are thermoplastic synthetic wood pulp fibers, and said thermoplastic synthetic wood pulp fibers are substantially free of configurations of fiber segments in which said segments lie in intersecting, overlapping relationship more than two fiber segments in thickness measured perpendiculary to the median plane of said second layer.
Claim 33
Dependent Claim
66 words
The fibrous material of claim 24 in which thermoplastic synthetic wood pulp fibers that are mechanically interengaged with other fibers in said second fibrous layer are present in the portions of said layer at the interface between said two layers in a quantity sufficient to constitute at least about 15 percent of the area occupied by fiber segments contained in said second layer at said interface.
Claim 34
Dependent Claim
66 words
The fibrous material of claim 24 in which thermoplastic synthetic wood pulp fibers that are mechanically interengaged with other fibers in said second fibrous layer are present in the portions of said layer at the interface between said two layers in a quantity sufficient to constitute at least about 20 percent of the area occupied by fiber segments contained in said second layer at said interface.
Claim 35
Dependent Claim
69 words
The fibrous material of claim 24 in which thermoplastic synthetic wood pulp fibers are present in the portions of said second layer at its external boundary surface remote from the interface between said two layers in a quantity sufficient to constitute at least about 10 percent by weight of said remote boundary surface portions, whereby said fibrous material is provided good resistance to abrasion at its said remote surface.
Claim 36
Dependent Claim
69 words
The fibrous material of claim 24 in which thermoplastic synthetic wood pulp fibers are present in the portions of said second layer at its external boundary surface remote from the interface between said two layers in a quantity sufficient to constitute at least about 15 percent by weight of said remote boundary surface portions, whereby said fibrous material is provided good resistance to abrasion at its said remote surface.
Claim 37
Dependent Claim
69 words
The fibrous material of claim 24 in which thermoplastic synthetic wood pulp fibers are present in the portions of said second layer at its external boundary surface remote from the interface between said two layers in a quantity sufficient to constitute at least about 20 percent by weight of said remote boundary surface portions, whereby said fibrous material is provided good resistance to abrasion at its said remote surface.
Claim 38
Dependent Claim
80 words
The fibrous material of claim 24 in which the portions of said first layer adjacent the interface between said two fibrous layers also contain thermoplastic synthetic wood pulp fibers, at least some of which are mechanically interengaged with other fibers in the first layer, in a quantity equal to at least about 5 percent by weight of the portion of the first layer extending from the thermoplastic synthetic wood pulp fibers located most distant from said interface to said interface.
Claim 39
Dependent Claim
22 words
The fibrous material of claim 24 in which both wettable and nonwettable synthetic wood pulp fibers are included in said second layer.
Claim 40
Dependent Claim
22 words
The fibrous material of claim 24 in which the only thermoplastic synthetic wood pulp fibers included in said second layer are nonwettable.
Claim 41
Dependent Claim
33 words
The fibrous material of claim 24 in which a binder is present in both said first and second layers, said binder bonding individual fiber segments to each other in both of said layers.
Claim 42
Dependent Claim
16 words
The fibrous material of claim 39 in which said binder is distributed throughout both said layers.
References Cited (Backward Citations)
US3973067A
Cited
US4012281A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-27 | 1981-09-26 | 1982-03-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-27 | 1985-09-26 | 1986-03-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-27 | 1989-09-26 | 1990-03-28 | $7700.00 | Window Closed / Lapsed |