Abstract
Abstract A process for preparing a synthetic wood comprises fusion mixing a thermoplastic resin and a particulate filler, molding the resulting mixture into sheets, monoaxially drawing the sheets, arranging the drawn sheets one upon another and then rapidly heating the thus-arranged drawn sheets to fusion bond them together thereby obtaining the synthetic wood. In one embodiment the sheets may allow a thermoplastic resin film to be inserted between any adjacent two sheets before the heating step, and in another embodiment the sheets may be coated with a thermoplastic resin before or after the drawing step.
Inventors
- 👤 Toshihiko Shinomura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 06:13
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/08; B32B27/18; B32B27/20; B32B27/30; B32B27/302; B32B27/304; B32B27/32; C; C08; C08K; C08K3/00; C08K3/01; C08K3/013; C08K3/02; C08K3/04; C08K3/18; C08K3/20; C08K3/22; C08K3/24; C08K3/26; C08K3/30; C08K3/34; C08L; C08L57/00; C08L97/00; C08L97/02; B32B2270/00; B32B2307/00; B32B2307/50; B32B2307/514; B32B2307/516; B32B2307/70; B32B2307/718
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
192 words
A process for the preparation of a synthetic wood comprising the steps of: fusion mixing a composition consisting essentially of 100 parts by weight of a thermoplastic resin and 5 - 400 parts by weight of an inorganic particulate filler to form a mixture thereof, the thermoplastic resin being selected from the group consisting of homopolymers of the monomers ethylene, propylene, styrene, vinyl chloride and vinylidene chloride, copolymers of at least two of said monomers, blends of said homopolymers and said copolymers, and mixtures of rubber with said homopolymers and said copolymers molding the mixture into sheets, having a thickness of at least 0.5 mm, drawing the sheets only monoaxially and to an extent that a drawing ratio of 50 - 1500% is attained, heating the drawn sheets for a time sufficient to permit their surfaces to be heated to temperatures not lower than the melting point of the sheets while their interior remains at a temperature lower than said melting point, superposing the thus heated drawn sheets one upon another, fusion bonding the thus heated, superposed sheets together, and allowing the fusion bonded mass to cool thereby obtaining the synthetic wood.
Claim 2
Dependent Claim
192 words
A process for the preparation of a synthetic wood comprising the steps of: fusion mixing a composition consisting essentially of 100 parts by weight of a thermoplastic resin and 5 - 400 parts by weight of an inorganic particulate filler to form a mixture thereof, the thermoplastic resin being selected from the group consisting of homopolymers of the monomers ethylene, propylene, styrene, vinyl chloride and vinylidene chloride, copolymers of at least two of said monomers, blends of said homopolymers and said copolymers, and mixtures of rubber with said homopolymers and said copolymers molding the mixture into sheets, having a thickness of at least 0.5 mm, drawing the sheets only monoaxially and to an extent that a drawing ratio of 50 - 1500% is attained, heating the drawn sheets for a time sufficient to permit their surfaces to be heated to temperatures not lower than the melting point of the sheets while their interior remains at a temperature lower than said melting point, superposing the thus heated drawn sheets one upon another, fusion bonding the thus heated, superposed sheets together, and allowing the fusion bonded mass to cool thereby obtaining the synthetic wood.
Claim 3
Dependent Claim
41 words
A process according to claim 1, wherein the particulate filler is a member selected from the group consisting of calcium carbonate, magnesium carbonate, calcium sulphate, calcium sulphite, silicon dioxide, titanium dioxide, barium sulphate, diatomaceous earth, talc, clay, Hedoro and carbon black.
Claim 4
Dependent Claim
85 words
A process according to claim 1, further comprising interposing a thermoplastic resin film between all of the sheets before the heating step, the thermoplastic resin films having a lower melting point than the sheets and being capable of being satisfactorily bonded thereto, and wherein the heating is affected for a time sufficient to heat the resin films to a temperature not lower than the melting point thereof while allowing the interior of the sheets to remain at a temperature lower than the melting point thereof.
Claim 5
Dependent Claim
52 words
A process according to claim 3, wherein the thermoplastic resin of the films is a member selected from low-density polyethylene, ethylene-vinyl acetate copolymers, ethylene-acrylic acid copolymers, chlorinated polypropylene, maleic-modified polypropylene and soft polyvinyl chloride, the thermoplastic resin of the films having a lower melting point than the thermoplastic resin of the sheets.
Claim 6
Dependent Claim
41 words
A process according to claim 3, wherein the particulate filler is a member selected from the group consisting of calcium carbonate, magnesium carbonate, calcium sulphate, calcium sulphite, silicon dioxide, titanium dioxide, barium sulphate, diatomaceous earth, talc, clay, Hedoro and carbon black.
Claim 7
Dependent Claim
90 words
A process according to claim 1 further comprising coating the sheets on at least one side with a thermoplastic resin immediately before or after the drawing step, the thermoplastic resin coating having a lower melting point than the sheets and being capable of being satisfactorily bonded thereto, and wherein the heating is effected for a time sufficient to heat the resin coating to a temperature not lower than the melting point thereof while allowing the interior of said sheets to remain at a temperature lower than the melting point thereof.
Claim 8
Dependent Claim
60 words
A process according to claim 6, wherein the thermoplastic resin of the resin coating is a member selected from the group consisting of low-density polyethylene, ethylene-vinyl acetate copolymers, ethylene-acrylic acid copolymers, chlorinated polypropylene, maleic-modified polypropylene, low-density polyethylene and soft polyvinyl chloride, the thermoplastic resin of the resin coating having a lower melting point than the thermoplastic resin of the sheets.
Claim 9
Dependent Claim
39 words
A process according to claim 6, wherein the particulate filler is selected from the group consisting of calcium carbonate, magnesium carbonate, calcium sulphate, calcium sulphite, silicon dioxide, titanium dioxide, barium sulphate, diatomaceous earth, talc, clay, Hedoro and carbon black.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-26 | 1979-07-28 | 1980-01-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-26 | 1983-07-28 | 1984-01-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-26 | 1987-07-28 | 1988-01-27 | $7700.00 | Window Closed / Lapsed |