Ag/Pd electroding powder and method for making
Assignee: MRA Laboratories Inc
•
Filing: 1983-05-12
•
Granted: 1985-02-19
•
Expires: 2003-05-12
Abstract
Abstract Pure silver and palladium powders are thoroughly mixed and dispersed by ball milling in a solution of a surfactant in a liquid vehicle. After drying and granulating, the resulting powder was heated to 500 DEG C., first to form an Ag/Pd alloy powder and then to cause palladium to precipitate from the interior of the alloy particles, to form a protective barrier of PdO on the alloy particle surfaces and to alter the alloy to 90Ag/10Pd. This powder, when used to make a buried electrode in a ceramic capacitor changes dimensions very little up to 500 DEG C. in the early stage of sintering the ceramic below which temperature the ceramic is weakest and most subject to cleaving.
Inventors
- 👤 Galeb H. Maher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 12:17
CPC Classifications
H; H01; H01G; H01G4/00; H01G4/002; H01G4/005; H01G4/008; H01G4/0085; C; C22; C22C; C22C32/00; C22C32/001; C22C32/0015; C22C32/0021; Y; Y10; Y10S; Y10S75/00; Y10S75/95; Y10S75/951; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
66 words
A metal electroding powder for use in making monolithic ceramic capacitors comprised of a silver-palladium alloy powder having a composition by weight of 90Ag/10Pd and a fine palladium oxide formed at the surfaces of the particles of said alloy powder to elevate the temperature at which said alloy will sinter, the presence of said alloy and said palladium oxide being detectable by X-ray defraction angle analysis.
Claim 2
Dependent Claim
66 words
A metal electroding powder for use in making monolithic ceramic capacitors comprised of a silver-palladium alloy powder having a composition by weight of 90Ag/10Pd and a fine palladium oxide formed at the surfaces of the particles of said alloy powder to elevate the temperature at which said alloy will sinter, the presence of said alloy and said palladium oxide being detectable by X-ray defraction angle analysis.
Claim 3
Dependent Claim
31 words
The powder of claim 1 wherein upon being pressed into pellets of about 50 percent theoretical density has a characteristic change of dimensions of less than 1% up to 500° C.
Claim 4
Dependent Claim
23 words
The powder of claim 2 wherein said characteristic change of dimensions goes negative at temperatures beyond 500° C. at which said powder sinters.
Claim 5
Dependent Claim
26 words
The powder of claim 1 wherein the ratio by weight of all the silver to all the palladium metal lies within the ratios 30Ag/70Pd and 90Ag/10Pd.
Claim 6
Dependent Claim
20 words
The powder of claim 1 wherein the surface area of said powder is from 0.5 to 2.0 M 2 /gm.
Claim 7
Dependent Claim
19 words
The powder of claim 1 wherein the average size of said particles ranges from about 0.1 to 2 microns.
References Cited (Backward Citations)
US3337365A
Cited
US3554796A
Cited
US3988498A
Cited
US3815187A
Cited
US4082906A
Cited
US4192698A
Cited
US4266265A
Cited
US4426356A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-02-19 | 1988-08-20 | 1989-02-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-02-19 | 1992-08-20 | 1993-02-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-02-19 | 1996-08-20 | 1997-02-19 | $7700.00 | Window Closed / Lapsed |