Low temperature fired ceramic capacitors
Assignee: San Fernando Electric Manufacturing Co
•
Filing: 1977-02-14
•
Granted: 1978-04-04
•
Expires: 1997-02-14
Abstract
Abstract A multi-layer ceramic capacitor is characterized by a ceramic composition including barium titanate and lithium fluoride as essential ingredients resulting in the capability of sintering the composition at temperatures below 1100° C. As a consequence, the electrodes for the capacitor can be formulated from pure silver or a silver palladium composition in which the major component is silver thereby decreasing the expense of such capacitors as compared to those requiring platinum, gold, or mixtures of these precious metals and/or similar precious metals in making up the electrodes.
Inventors
- 👤 Rajnikant B. Amin
- 👤 Harlan Urie Anderson
- 👤 Charles E. Hodgkins
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 06:51
CPC Classifications
H; H01; H01G; H01G4/00; H01G4/30; C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/468; C04B35/4682; H01G4/002; H01G4/005; H01G4/008; H01G4/0085; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/1209; H01G4/1218; H01G4/1227
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
142 words
A multi layer ceramic capacitor comprising, in combination: (a) a plurality of ceramic tape pieces; (b) electrodes on the surfaces of the pieces with some of the pieces having electrodes terminating adjacent to their front edges and the remaining pieces having the electrodes terminating adjacent to their rear edges, the pieces with the electrodes terminating adjacent to their front edges being sandwiched between said remaining pieces to provide a stack; (c) top and bottom ceramic pieces without any electrodes positioned on the top and bottom of said stack to provide a multi layer ceramic capacitor with buried electrodes, the ceramic composition of each of said ceramic tape pieces including, by weight: (1) at least 50% barium titanate, and (2) from 0.25% to 10% lithium fluoride, and the electrode composition of each of the buried electrodes including, by weight, at least 50% silver.
Claim 2
Dependent Claim
142 words
A multi layer ceramic capacitor comprising, in combination: (a) a plurality of ceramic tape pieces; (b) electrodes on the surfaces of the pieces with some of the pieces having electrodes terminating adjacent to their front edges and the remaining pieces having the electrodes terminating adjacent to their rear edges, the pieces with the electrodes terminating adjacent to their front edges being sandwiched between said remaining pieces to provide a stack; (c) top and bottom ceramic pieces without any electrodes positioned on the top and bottom of said stack to provide a multi layer ceramic capacitor with buried electrodes, the ceramic composition of each of said ceramic tape pieces including, by weight: (1) at least 50% barium titanate, and (2) from 0.25% to 10% lithium fluoride, and the electrode composition of each of the buried electrodes including, by weight, at least 50% silver.
Claim 3
Dependent Claim
21 words
A capacitor according to claim 1, in which said ceramic composition further includes by weight from 0.1% to 30% strontium titanate.
Claim 4
Dependent Claim
21 words
A capacitor according to claim 1, in which said ceramic composition further includes by weight from 0.1% to 2% barium fluoride.
Claim 5
Dependent Claim
17 words
A capacitor according to claim 1, in which the balance of the electrode composition consists of palladium.
Claim 6
Dependent Claim
149 words
A multi layer ceramic capacitor comprising in combination: (a) a plurality of ceramic tape pieces; (b) electrodes on the surfaces of the pieces with some of the pieces having electrodes terminating adjacent to their front edges and the remaining pieces having the electrodes terminating adjacent to their rear edges, the pieces with the electrodes terminating adjacent to their front edges being sandwiched between said remaining pieces to provide a stack; (c) top and bottom ceramic pieces without any electrodes positioned on the top and bottom of said stack to provide a multi layer ceramic capacitor with buried electrodes, the ceramic composition of each of said ceramic tape pieces including, within plus or minus 1% by weight: 94.82% barium titanate 1.96% lithium fluoride 0.81% manganese nitrate 0.24% cerium oxide 0.95% cobalt nitrate 1.22% niobium oxalate; and the electrode composition of each of said buried electrodes being substantially 100% pure silver.
Claim 7
Dependent Claim
149 words
A multi layer ceramic capacitor comprising in combination: (a) a plurality of ceramic tape pieces; (b) electrodes on the surfaces of the pieces with some of the pieces having electrodes terminating adjacent to their front edges and the remaining pieces having the electrodes terminating adjacent to their rear edges, the pieces with the electrodes terminating adjacent to their front edges being sandwiched between said remaining pieces to provide a stack; (c) top and bottom ceramic pieces without any electrodes positioned on the top and bottom of said stack to provide a multi layer ceramic capacitor with buried electrodes, the ceramic composition of each of said ceramic tape pieces including, within plus or minus 1% by weight: 94.82% barium titanate 1.96% lithium fluoride 0.81% manganese nitrate 0.24% cerium oxide 0.95% cobalt nitrate 1.22% niobium oxalate; and the electrode composition of each of said buried electrodes being substantially 100% pure silver.
Claim 8
Dependent Claim
165 words
A process of making a multi-layer ceramic capacitor including the steps of: (a) forming a ceramic tape composition of, by weight, at least 50% barium titanate and from 0.25% to 10% lithium fluoride; (b) cutting the ceramic tape to provide a plurality of ceramic tape pieces; (c) forming an electrode composition of silver and palladium in which there is provided at least 50% by weight of silver; (d) silkscreening said electrode composition on the surfaces of the tape pieces with some of the pieces having the electrodes terminating adjacent to their front edges and the remaining pieces having the electrodes terminating adjacent to their rear edges; (e) sandwiching the pieces with the electrodes terminating adjacent to their front edges between the remaining pieces to provide a stack; (f) affixing ceramic pieces without any electrodes on the top and bottom of said stack to provide a multi-layer ceramic capacitor with buried electrodes; and (g) sintering the composition at a temperature between 750° C and 1250° C.
Claim 9
Dependent Claim
165 words
A process of making a multi-layer ceramic capacitor including the steps of: (a) forming a ceramic tape composition of, by weight, at least 50% barium titanate and from 0.25% to 10% lithium fluoride; (b) cutting the ceramic tape to provide a plurality of ceramic tape pieces; (c) forming an electrode composition of silver and palladium in which there is provided at least 50% by weight of silver; (d) silkscreening said electrode composition on the surfaces of the tape pieces with some of the pieces having the electrodes terminating adjacent to their front edges and the remaining pieces having the electrodes terminating adjacent to their rear edges; (e) sandwiching the pieces with the electrodes terminating adjacent to their front edges between the remaining pieces to provide a stack; (f) affixing ceramic pieces without any electrodes on the top and bottom of said stack to provide a multi-layer ceramic capacitor with buried electrodes; and (g) sintering the composition at a temperature between 750° C and 1250° C.
Claim 10
Dependent Claim
51 words
The process of claim 6, in which the step of forming the ceramic composition results in a composition including, by weight, from 90%- 95% barium titanate and from 1.0% to 3.0% lithium fluoride and in which the step of sintering said composition is carried out between 850° C and 900° C.
References Cited (Backward Citations)
US2443211A
Cited
US2402518A
Cited
US2972570A
Cited
US3074804A
Cited
US3035927A
Cited
US3069276A
Cited
US3179525A
Cited
US3529978A
Cited
US3612963A
Cited
US3753911A
Cited
US3862046A
Cited
US3969252A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-04-03 | 1981-10-03 | 1982-04-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-04-03 | 1985-10-03 | 1986-04-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-04-03 | 1989-10-03 | 1990-04-04 | $7700.00 | Window Closed / Lapsed |