Making an electroding ink for a monolithic ceramic capacitor
Assignee: MRA Laboratories Inc
•
Filing: 1977-09-07
•
Granted: 1980-03-11
•
Expires: 1997-09-07
Abstract
Abstract A smooth electroding ink containing a silver-alloy powder is prepared by milling and deagglomerating the silver-alloy powder in the same vehicle employed in the ink. This is accomplished at high production rates in a sand mill by establishing and maintaining during milling a splash-free laminar-flow vortex of the slurry, leading to very smooth buried silver-alloy electrode films in a monolithic ceramic capacitor.
Inventors
- 👤 John P. Maher
- 👤 Robert T. Jacobsen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 05:20
CPC Classifications
H; H01; H01G; H01G4/00; H01G4/002; H01G4/005; H01G4/008; H01G4/0085; B; B22; B22F; B22F9/00; B22F9/02; B22F9/04; B22F2009/041; B22F2998/00
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
155 words
A method for preparing a smooth electroding ink for use in making monolithic ceramic capacitors comprising: (a) forming a mixture of a metal powder selected from the group of silver and silver-palladium, milling elements, a surfactant and an organic vehicle, said metal amounting to from 65 to 95 percent of the sum of said metal plus said vehicle by weight; (b) milling said mixture in a non-violent mode, by means of a rotary impeller so as to establish a splash-free laminar flow, until said metal powder exhibits a fineness of grind of less than 8 microns and a surface of a dried sample film of said ink exhibits a peak to peak amplitude of less than 6 microns; (c) removing said milling elements from said milled mixture; and (d) blending into said mixture containing said vehicle an organic binder to obtain a screen printable electroding ink having a viscosity of from 20,000 to 150,000 centipoise.
Claim 2
Independent Claim
155 words
A method for preparing a smooth electroding ink for use in making monolithic ceramic capacitors comprising: (a) forming a mixture of a metal powder selected from the group of silver and silver-palladium, milling elements, a surfactant and an organic vehicle, said metal amounting to from 65 to 95 percent of the sum of said metal plus said vehicle by weight; (b) milling said mixture in a non-violent mode, by means of a rotary impeller so as to establish a splash-free laminar flow, until said metal powder exhibits a fineness of grind of less than 8 microns and a surface of a dried sample film of said ink exhibits a peak to peak amplitude of less than 6 microns; (c) removing said milling elements from said milled mixture; and (d) blending into said mixture containing said vehicle an organic binder to obtain a screen printable electroding ink having a viscosity of from 20,000 to 150,000 centipoise.
Claim 3
Dependent Claim
32 words
The method of claim 1 wherein at the introduction of said metal powder to said mixture, the characteristic effective surface area of said powder is greater than 1.5 square meters per milliliter.
Claim 4
Dependent Claim
21 words
The method of claim 1 wherein said vehicle is selected from dichlorotoluene, terpineol, cyclohexanol, kerosene and mono-butyl ether of diethylene glycol.
Claim 5
Dependent Claim
27 words
The method of claim 1 wherein said surfactant consists essentially of a mixture of equal molar amounts of the monophosphate and diphosphate esters of tridecyl alcohol ethoxylate.
Claim 6
Dependent Claim
21 words
The method of claim 1 wherein said silver in said metal powder amounts to from 20 to 95 percent by weight.
Claim 7
Dependent Claim
24 words
The method of claim 1 wherein said blending of said binder into said mixture is accomplished prior to said removing of said milling elements.
Claim 8
Dependent Claim
19 words
The method of claim 1 wherein the temperature of said mixture during said milling is maintained below 30° C.
Claim 9
Dependent Claim
20 words
The method of claim 7 wherein the temperature of said mixture during said milling is maintained at about 18° C.
Claim 10
Independent Claim
228 words
A method for making a monolithic ceramic capacitor including depositing a film of an electroding ink on a surface of each of a plurality of green ceramic layers having a thickness less than 0.001 inch, making a stack of said layers to form a body having a plurality of internal electroding ink films being spaced from each other by said ceramic layers and firing said body to mature said ceramic and to transform said ink films into metallic electrode films; wherein the improvement comprises preparing said electroding ink by (a) forming a mixture of a metal powder selected from the group of silver and silver-palladium, milling elements, a surfactant and an organic vehicle, said metal amounting to from 65 to 95 percent of the sum of said metal plus said vehicle by weight; (b) milling said mixture in a non-violent mode by means of a rotary impeller so as to establish a splash-free laminar flow until said metal powder exhibits a fineness of grind of less than 8 microns and a surface of a dried sample film of said ink exhibits a peak to peak amplitude of less than 6 microns; (c) removing said milling elements from said milled mixture; and (d) blending into said mixture containing said vehicle an organic binder to obtain a screen printable electroding ink having a viscosity of from 20,000 to 150,000 centipoise.
Claim 11
Independent Claim
228 words
A method for making a monolithic ceramic capacitor including depositing a film of an electroding ink on a surface of each of a plurality of green ceramic layers having a thickness less than 0.001 inch, making a stack of said layers to form a body having a plurality of internal electroding ink films being spaced from each other by said ceramic layers and firing said body to mature said ceramic and to transform said ink films into metallic electrode films; wherein the improvement comprises preparing said electroding ink by (a) forming a mixture of a metal powder selected from the group of silver and silver-palladium, milling elements, a surfactant and an organic vehicle, said metal amounting to from 65 to 95 percent of the sum of said metal plus said vehicle by weight; (b) milling said mixture in a non-violent mode by means of a rotary impeller so as to establish a splash-free laminar flow until said metal powder exhibits a fineness of grind of less than 8 microns and a surface of a dried sample film of said ink exhibits a peak to peak amplitude of less than 6 microns; (c) removing said milling elements from said milled mixture; and (d) blending into said mixture containing said vehicle an organic binder to obtain a screen printable electroding ink having a viscosity of from 20,000 to 150,000 centipoise.
References Cited (Backward Citations)
US2764359A
Cited
US3090567A
Cited
US3682766A
Cited
US3917487A
Cited
US3995815A
Cited
US4082906A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-03-11 | 1983-09-10 | 1984-03-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-03-11 | 1987-09-10 | 1988-03-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-03-11 | 1991-09-10 | 1992-03-11 | $7700.00 | Window Closed / Lapsed |