Method for making alignment-enhancing feed-through conductors for stackable silicon-on-sapphire
Assignee: General Electric Co
•
Filing: 1982-11-29
•
Granted: 1985-02-19
•
Expires: 2002-11-29
Abstract
Abstract Alignment-enhancing electrically conductive feed-through paths are provided for the high-speed low-loss transfer of electrical signals between integrated circuits of a plurality of silicon-on-sapphire bodies arrayed in a stack. The alignment-enhancing feed-throughs are made by a process of this invention involving the drilling of holes through the body, double-sided sputtering, electroplating, and the filling of the holes with solder by capillary action. The alignment-enhancing feed-throughs are activated by forming a stack of wafers and remelting the solder whereupon the wafers, and the feed-through paths, are pulled into alignment by surface tension forces.
Inventors
- 👤 Thomas R. Anthony
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 09:54
CPC Classifications
H; H10; H10W; H10W90/00; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/34; H05K3/341; H05K3/3431; H05K3/3436; H10W70/00; H10W70/60; H10W70/611; H10W90/401; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K2201/00; H05K2201/09; H05K2201/09209; H05K2201/095; H05K2201/096; H05K2201/10; H05K2201/10613; H05K2201/10621; H05K2201/10666; H05K2203/00; H05K2203/04; H05K2203/0455; H05K3/36; H05K3/368; H10W90/20; H10W90/297; H10W90/701; H10W90/721; H10W90/722; Y; Y02; Y02P; Y02P70/00; Y02P70/50; Y10; Y10S; Y10S438/00; Y10S438/94; Y10S438/975
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
130 words
A process for making alignment-enhancing electrically conductive feed-through conductors in a body comprising the steps of: (a) providing a stackable semiconductor body, said body having top and bottom major opposed surfaces substantially parallel to each other and an outer peripheral edge area interconnecting said major surfaces; (b) providing a plurality of holes through said body, each of said holes having apertures lying in said major opposed surfaces and an inner surface interconnecting said apertures; (c) depositing a first thin layer of a first metal onto each of said inner surfaces; (d) applying a second thin layer of a second metal over each of said first thin layers; and (e) filling the remaining hole volume with a third metal forming thereby an alignment-enhancing electrically conductive feedthrough in a stackable semiconductor body.
Claim 2
Dependent Claim
130 words
A process for making alignment-enhancing electrically conductive feed-through conductors in a body comprising the steps of: (a) providing a stackable semiconductor body, said body having top and bottom major opposed surfaces substantially parallel to each other and an outer peripheral edge area interconnecting said major surfaces; (b) providing a plurality of holes through said body, each of said holes having apertures lying in said major opposed surfaces and an inner surface interconnecting said apertures; (c) depositing a first thin layer of a first metal onto each of said inner surfaces; (d) applying a second thin layer of a second metal over each of said first thin layers; and (e) filling the remaining hole volume with a third metal forming thereby an alignment-enhancing electrically conductive feedthrough in a stackable semiconductor body.
Claim 3
Dependent Claim
45 words
The process of claim 1 further including the process steps of: (1) forming a stack of the stackable bodies and (2) remelting said third metal, forming thereby a stacked self-aligned array of the bodies, said bodies having a plurality of electrically conductive paths communicating therebetween.
Claim 4
Dependent Claim
13 words
The process of claim 2 wherein said third metal is a lead-tin alloy.
Claim 5
Dependent Claim
25 words
The process of claim 2 wherein said remelting is accomplished by heating said stack to a temperature sufficient to cause melting of said third metal.
Claim 6
Dependent Claim
38 words
The process of claim 1 wherein said body is composed of a single material, said single material being one selected from the group consisting of silicon, germanium, gallium arsenide, gallium phosphide, indium antimonide, cadmium telluride, and zinc sulfide.
Claim 7
Dependent Claim
69 words
The process of claim 1 wherein said body is a composite, said body having a single crystal sapphire substrate and a contiguous overlaying epitaxially-grown layer of single crystal silicon, said top major surface being the exposed surface of said silicon layer, said bottom major surface being the exposed surface of said sapphire substrate and said outer peripheral edge area encompassing both said sapphire substrate and said layer of silicon.
Claim 8
Dependent Claim
31 words
The process of claim 1 wherein said body is composed of an insulating material, said insulating material being one selected from the group consisting of alumina, quartz, glass and beryllium oxide.
Claim 9
Dependent Claim
15 words
The process of claim 1 wherein said holes are provided by a laser drilling process.
Claim 10
Dependent Claim
11 words
The process of claim 1 wherein said first metal is gold.
Claim 11
Dependent Claim
11 words
The process of claim 1 wherein said first metal is nichrome.
Claim 12
Dependent Claim
14 words
The process of claim 1 wherein said first thin layer is deposited by sputtering.
Claim 13
Dependent Claim
16 words
The process of claim 1 wherein said second thin layer is applied by an electrodeposition process.
Claim 14
Dependent Claim
24 words
The process of claim 12 wherein said electrodeposition process includes agitation of said body substantially perpendicular to said major surfaces during said electrodeposition process.
Claim 15
Dependent Claim
15 words
The process of claim 1 wherein the metal of said second thin layer is copper.
Claim 16
Dependent Claim
35 words
The process of claim 14 further including the process step of arresting said agitation prior to completion of said electrodeposition process for a time sufficient to cause a relief electroplate of predetermined height to form.
References Cited (Backward Citations)
US3259049A
Cited
US3301939A
Cited
US3654097A
Cited
US3798136A
Cited
US4312897A
Cited
US4285780A
Cited
US4278511A
Cited
US4368106A
Cited
US4396467A
Cited
US4399004A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-02-19 | 1988-08-20 | 1989-02-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-02-19 | 1992-08-20 | 1993-02-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-02-19 | 1996-08-20 | 1997-02-19 | $7700.00 | Window Closed / Lapsed |