Patent US4495253A successfully refreshed from Google Patents.
US4495253A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Solderable plated plastic components and process for plating _
Assignee: Raytheon Co
•
Filing: 1983-05-31
•
Granted: 1985-01-22
•
Expires: 2003-05-31
Abstract
Abstract A particular plastic material is formed into the desired component shape and then is plated by a process comprising; a particular surface preparation step, electroless deposition and electrolytic deposition which results in excellent plating adhesion. The plated component is then assembled with other components manufactured in the same manner or with compatible metal components such as aluminum and soldered together in a disclosed hot oil dip soldering process. In the soldering process, the plated plastic substrate is completely immersed in a hot oil medium at a temperature of approximately 243° C. (470° F.) for a time of approximately 60 seconds for solder reflow.
Inventors
- 👤 Hal P. Abel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 22:29
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/22; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/0353; H05K1/0373; H05K3/00; H05K3/10; H05K3/18; H05K3/181; H05K3/38; H05K3/381; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12528; Y10T428/12535; Y10T428/12556; Y10T428/31504; Y10T428/31533
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
113 words
A metal plated plastic article formed by a process comprising the steps of: a. selecting a plastic having a deflection temperature and a melting temperature of at least 204° C. and having a predetermined amount of glass fill; b. forming the plastic into the article shape; c. roughening the surface of the article by means of physical abrasion; d. exposing the roughened surface of the formed article to a chemical etch solution comprising ammonium bifluoride, nitric acid, and sulfuric acid; e. chemically depositing a first layer of conductive metal on the chemically etched surface of the artcle; and f. electrolytically depositing a second layer of metal on the first layer of conductive metal.
Claim 2
Dependent Claim
113 words
A metal plated plastic article formed by a process comprising the steps of: a. selecting a plastic having a deflection temperature and a melting temperature of at least 204° C. and having a predetermined amount of glass fill; b. forming the plastic into the article shape; c. roughening the surface of the article by means of physical abrasion; d. exposing the roughened surface of the formed article to a chemical etch solution comprising ammonium bifluoride, nitric acid, and sulfuric acid; e. chemically depositing a first layer of conductive metal on the chemically etched surface of the artcle; and f. electrolytically depositing a second layer of metal on the first layer of conductive metal.
Claim 3
Dependent Claim
26 words
The article as set forth in claim 1 wherein the step of selecting a plastic comprises selecting from the group consisting of polyethersulfone, polyphenylenesulfide and polyimide-polyamide.
Claim 4
Dependent Claim
19 words
The article as set forth in claim 2 wherein the polyethersulfone comprises substantially 30% glass fill with chopped fibers.
Claim 5
Dependent Claim
133 words
A metal plated plastic article having a plastic substrate of polyethersulfone with substantially 30% glass fill with chopped fibers, the article being produced by a process comprising the steps of: a. forming the substrate of polyethersulfone with substantially 30% glass fill with chopped fibers into the article shape; b. drying the article; c. roughening the surface of the article by means of physical abrasion; d. exposing the roughened surface of the formed article to a chemical etch solution comprising ammonium bifluoride, nitric acid, and sulfuric acid; e. chemically depositing a first layer of conductive metal on the surface of the article after the step of exposing the roughened surface of the article to the chemical etch solution; and f. electrolytically depositing a second layer of metal on the first layer of conductive metal.
Claim 6
Dependent Claim
133 words
A metal plated plastic article having a plastic substrate of polyethersulfone with substantially 30% glass fill with chopped fibers, the article being produced by a process comprising the steps of: a. forming the substrate of polyethersulfone with substantially 30% glass fill with chopped fibers into the article shape; b. drying the article; c. roughening the surface of the article by means of physical abrasion; d. exposing the roughened surface of the formed article to a chemical etch solution comprising ammonium bifluoride, nitric acid, and sulfuric acid; e. chemically depositing a first layer of conductive metal on the surface of the article after the step of exposing the roughened surface of the article to the chemical etch solution; and f. electrolytically depositing a second layer of metal on the first layer of conductive metal.
Claim 7
Dependent Claim
24 words
The metal plated plastic article as set forth in claim 1 wherein the step of roughening comprises blasting the surface with 100-200 size grit.
Claim 8
Dependent Claim
18 words
The metal plated plastic article as set forth in claim 5 wherein the grit size is approximately 120.
Claim 9
Dependent Claim
23 words
The metal plated plastic article as set forth in claim 2 wherein the polyphenylene sulfide comprises substantially 40% glass fill with chopped fibers.
Claim 10
Dependent Claim
22 words
The metal plated plastic article as set forth in claim 2 wherein the polyimide-polyamide comprises substantially 40% glass fill with chopped fibers.
Claim 11
Dependent Claim
26 words
The metal plated plastic article as set forth in claim 4 wherein the step of roughening the surface comprises blasting the surface with 100-200 size grit.
Claim 12
Dependent Claim
18 words
The metal plated plastic article as set forth in claim 9 wherein the grit size is approximately 120.
Claim 13
Dependent Claim
135 words
A metal plated plastic article having a plastic substrate of polyphenylene sulfide with substantially 40% glass fill with chopped fibers, the article being produced by a process comprising the steps of: a. forming the substrate of polyphenylene sulfide with substantially 40% glass fill with chopped fibers into the article shape; b. drying the article; c. roughening the surface of the article by means of physical abrasion; d. exposing the roughened surface of the formed article to a chemical etch solution comprising ammonium bifluoride, nitric acid, and sulfuric acid; e. chemically depositing a first layer of conductive metal on the surface of the article after the step of exposing the roughened surface of the article to the chemical etch solution; and f. electrolytically depositing a second layer of metal on the first layer of conductive metal.
Claim 14
Dependent Claim
135 words
A metal plated plastic article having a plastic substrate of polyphenylene sulfide with substantially 40% glass fill with chopped fibers, the article being produced by a process comprising the steps of: a. forming the substrate of polyphenylene sulfide with substantially 40% glass fill with chopped fibers into the article shape; b. drying the article; c. roughening the surface of the article by means of physical abrasion; d. exposing the roughened surface of the formed article to a chemical etch solution comprising ammonium bifluoride, nitric acid, and sulfuric acid; e. chemically depositing a first layer of conductive metal on the surface of the article after the step of exposing the roughened surface of the article to the chemical etch solution; and f. electrolytically depositing a second layer of metal on the first layer of conductive metal.
Claim 15
Dependent Claim
26 words
The metal plated plastic article as set forth in claim 11 wherein the step of roughening the surface comprises blasting the surface with 100-200 size grit.
Claim 16
Dependent Claim
18 words
The metal plated plastic article as set forth in claim 12 wherein the grit size is approximately 120.
Claim 17
Dependent Claim
133 words
A metal plated plastic article having a plastic substrate of polyimide-polyamide with substantially 40% glass fill with chopped fibers, the article being produced by a process comprising the steps of: a. forming the substrate of polyimide-polyamide with substantially 30% glass fill with chopped fibers into the article shape; b. drying the article; c. roughening the surface of the article by means of physical abrasion; d. exposing the roughened surface of the formed article to a chemical etch solution comprising ammonium bifluoride, nitric acid, and sulfuric acid; e. chemically depositing a first layer of conductive metal on the surface of the article after the step of exposing the roughened surface of the article to the chemical etch solution; and f. electrolytically depositing a second layer of metal on the first layer of conductive metal.
Claim 18
Dependent Claim
133 words
A metal plated plastic article having a plastic substrate of polyimide-polyamide with substantially 40% glass fill with chopped fibers, the article being produced by a process comprising the steps of: a. forming the substrate of polyimide-polyamide with substantially 30% glass fill with chopped fibers into the article shape; b. drying the article; c. roughening the surface of the article by means of physical abrasion; d. exposing the roughened surface of the formed article to a chemical etch solution comprising ammonium bifluoride, nitric acid, and sulfuric acid; e. chemically depositing a first layer of conductive metal on the surface of the article after the step of exposing the roughened surface of the article to the chemical etch solution; and f. electrolytically depositing a second layer of metal on the first layer of conductive metal.
Claim 19
Dependent Claim
25 words
The metal plated plastic article as set forth in claim 14 wherein the step of roughening the surface comprises blasting the surface with 100-200 grit.
Claim 20
Dependent Claim
18 words
The metal plated plastic article as set forth in claim 15 wherein the grit size is approximately 120.
References Cited (Backward Citations)
US3681209A
Cited
US3953653A
Cited
US4248921A
Cited
US4192764A
Cited
US4296217A
Cited
GB2015414A
Cited
US4335164A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-22 | 1988-07-23 | 1989-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-22 | 1992-07-23 | 1993-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-22 | 1996-07-23 | 1997-01-22 | $7700.00 | Window Closed / Lapsed |