High performance catalysts for carbometallic oil conversion and their manufacturing and use
Assignee: HETTINGER JR WILLIAM P
•
Filing: 1983-04-07
•
Granted: 1984-10-30
•
Expires: 2003-04-07
Abstract
Abstract A catalyst nominally containing zeolite, preferably HY zeolite and/or ultrastable HY zeolite, clay, alumina and an acidic silica-alumina co-gel matrix. The zeolite is preferably partially exchanged with high La/Ce ratio solution in a wetting step, and rare earths are precipitated onto the matrix. The catalyst has high metals tolerance and is capable of cracking heavy reduced crude oils, producing higher LCO/slurry oil ratio.
Inventors
- 👤 H. Wayne Beck
- 👤 James D. Carruthers
- 👤 Edward B. Cornelius
- 👤 Ronald A. Kmecak
- 👤 Stephen M. Kovach
- 👤 William P. Hettinger, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 22:07
CPC Classifications
B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; B01J29/08; B01J29/084; C; C10; C10G; C10G11/00; C10G11/02; C10G11/04; C10G11/05
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
208 words
A low coke, high octane, high activity, high selectivity, metal tolerant, thermally stable, low slurry oil producing catalyst for the conversion of hydrocarbons contaminated with high Conradson carbon metals to produce lower molecular weight products, said catalyst comprising in combination: (a) from about 8 to about 25% by weight of a zeolite comprising a zeolite selected from the group consisting of a HY zeolite and an ultrastable HY zeolite having a silica-alumina mole ratio of at least about 5, and having a cell dimension of about 24.30 to about 24.70 angstroms; (b) from about 20 to about 70 wt. % of a clay comprising kaolin, having a crystalline size of from about 0.5 to about 2 microns; (c) from about 35 to about 70% of an acidic silica-alumina co-gel matrix comprising at least about 13 wt. % alumina; (d) from about 0.1 to about 3 wt. % of rare earths comprising lanthanum and cerium in a ratio of from about 1 to about 6; (e) from about 15 to about 60 wt. % alumina; (f) wherein said zeolite is partially exchanged with said rare earths from a solution and wherein said zeolite is contained in said acidic matrix and wherein rare earthes have been precipitated onto said matrix;
Claim 2
Dependent Claim
208 words
A low coke, high octane, high activity, high selectivity, metal tolerant, thermally stable, low slurry oil producing catalyst for the conversion of hydrocarbons contaminated with high Conradson carbon metals to produce lower molecular weight products, said catalyst comprising in combination: (a) from about 8 to about 25% by weight of a zeolite comprising a zeolite selected from the group consisting of a HY zeolite and an ultrastable HY zeolite having a silica-alumina mole ratio of at least about 5, and having a cell dimension of about 24.30 to about 24.70 angstroms; (b) from about 20 to about 70 wt. % of a clay comprising kaolin, having a crystalline size of from about 0.5 to about 2 microns; (c) from about 35 to about 70% of an acidic silica-alumina co-gel matrix comprising at least about 13 wt. % alumina; (d) from about 0.1 to about 3 wt. % of rare earths comprising lanthanum and cerium in a ratio of from about 1 to about 6; (e) from about 15 to about 60 wt. % alumina; (f) wherein said zeolite is partially exchanged with said rare earths from a solution and wherein said zeolite is contained in said acidic matrix and wherein rare earthes have been precipitated onto said matrix;
Claim 3
Dependent Claim
23 words
A catalyst composition as claimed in claim 1 comprising a pore volume greater than 0.4 cc per gram as determined by water titration.
Claim 4
Dependent Claim
38 words
A catalyst composition as claimed in claim 1 having from about 40 to 70% of all pores in the 100-1000 Å diameter range and less than 35% of all pores between 20-100 Å as measured by mercury porosimetry.
Claim 5
Dependent Claim
24 words
A catalyst composition as claimed in claim 1 containing at least 10% or more of all pores in the greater than 1000 Å range.
Claim 6
Dependent Claim
28 words
A catalyst composition as claimed in claim 1 comprising from about a ratio of 0.5 to 1.5 acidity in the matrix relative to the acidity in the zeolite.
Claim 7
Dependent Claim
74 words
A catalyst as claimed in claim 1 wherein the acidic silica-alumina co-gel matrix has an acidic component which is composed of one or more of the materials selected from the group consisting of an alumina coated silica gel, designated in the trade as low or high alumina; acid leached and alumina reprecipitated calcined kaolin or halloysite; synthetic montmorillonite, designated SMM; magnesium; titanium and zirconium promoted silica gels; and fluoride and phosophate promoted alumina gels.
Claim 8
Dependent Claim
25 words
A catalyst as claimed in claim 1 wherein the kaolin consists of a clay having 80% or more of the particles less than one micron.
Claim 9
Dependent Claim
18 words
A catalyst as claimed in claim 1 wherein the zeolite content is between 10 and 25% by weight.
Claim 10
Dependent Claim
15 words
A catalyst as claimed in claim 1 wherein the zeolite is an ultrastable HY zeolite.
Claim 11
Dependent Claim
19 words
A catalyst as claimed in claim 1 wherein the rare earth content is between 0.01 and 3% by weight.
Claim 12
Dependent Claim
19 words
A catalyst as claimed in claim 1 wherein at least 10% of the alumina is present as alumina gel.
Claim 13
Dependent Claim
41 words
A catalyst as claimed in claim 1 wherein 10 to 50% of the exchange sites on the HY zeolite or ultra stable HY zeolite are exchanged with rare earth, wherein the ratio of lanthanum to cerium is between 1 and 6.
Claim 14
Dependent Claim
40 words
A catalyst as claimed in claim 1 wherein 10 to 70% of the catalyst on the HY zeolite or ultra stable HY zeolite are exchanged with rare earth, wherein the ratio of lanthanum to cerium is between 3 and 6.
Claim 15
Dependent Claim
36 words
A catalyst as claimed in claim 1 wherein 25 to 75% of the total rare earth in the catalyst is precipitated in the matrix wherein the ratio of lanthanum to cerium is between 1 and 6.
Claim 16
Dependent Claim
18 words
A catalyst composition as claimed in claim 1 incorporating additional 10% of titania gel as a vanadia immobilizer.
Claim 17
Dependent Claim
21 words
A catalyst as claimed in claim 1 wherein 20% colloidal alumina is added in the catalyst during formation for nickel immobilization.
Claim 18
Dependent Claim
20 words
A catalyst as claimed in claim 1 wherein 1 to 5% of silicic acid is added to enhance attrition resistance.
Claim 19
Dependent Claim
23 words
A catalyst as claimed in claim 1 in which 20% carbon black is added during preparation in order to enhance micro pore structure.
Claim 20
Dependent Claim
18 words
A catalyst as claimed in claim 1 comprising a pore volume between 0.5 to 0.6 cc per gram.
Claim 21
Dependent Claim
268 words
A process for the preparation of the catalyst of claim 14 comprising in combination, the steps of: (a) adding a sodium silicate solution to a batch tank so as to yeild a concentration of 3 to 6% SiO 2 ; (b) dispersing kaolin clay in water in a concentration of 20 to 60% and combining with "a" in such proportions as to yield a catalyst containing 20 to 70% of kaolin; (c) adding a solution of alum to "b", so as to bring the pH to 8 to 10 and holding at 24° C. to 49° C. (75° F. to 120° F.) for 1/2 hour or more; (d) adding a sodium aluminate solution to "c" so as to raise the pH back to 12; (e) adding alum solution to "d" so as to drop the pH to 3; (f) adding a slurry of NH 4 HY zeolite to "e" so as to produce a final content of 8 to 35% zeolite in the finished catalyst, said HY zeolite to have been exchanged with rare earth to the extent of 10-80% of full rare earth capacity; (g) adding NH 3 to this slurry so as to neutralize the alum and return the pH to 6-9 by precipitating alumina gel; (h) dewatering "g" by filtration, homogenizing, adusting viscosity, and spray drying to a desirable particle size; (i) washing said spray dried particles to remove additional sodium and sulfate ions; (j) contacting with additional rare earth solution at a pH of about 5 so as to precipitate rare earth in the matrix; (k) rinsing, dewatering and drying to a final product.
Claim 22
Dependent Claim
22 words
A process as decribed in claim 20 in which the sodium silicate solution additionally comprises sodium aluminate solution in the catalyst preparation.
Claim 23
Dependent Claim
21 words
A process for catalyst preparation as described in claim 20 in which the sodium silicate solution is neutralized with sulfuric acid.
Claim 24
Dependent Claim
265 words
A process for the preparation of the catalyst of claim 1 comprising in combination, the steps of: (a) adding a sodium silicate solution to a batch tank so as to yield a concentration of 3 to 6% SiO 2 ; (b) dispersing kaolin clay in water in a concentration of 20 to 60% and combining with "a" in such proportions as to yield a catalyst containing 20 to 70% kaolin; (c) adding a solution of alum to "b", so as to being the pH to 8 to 10 and holding at 24° C. to 49° C. (75° F. to 120° F.) for 2/3 hour or more. (d) adding a sodium aluminate solution to "c" so as to raise the pH back to 12; (e) adding alum solution to "d" so as to drop the pH to 3; (f) adding a slurry of ultra stable HY zeolite to "e" so as to produce a final content of 8 to 35% zeolite in the finished catalyst, said HY zeolite being exchanged with rare earth to the extend of 10-80% of full rare earth capacity; (g) adding NH 3 to this slurry so as to neutralize the alum and return the pH to 6-9 by precipitating alumina gel; (h) dewatering "g" by filtration, homogenizing, adjusting viscosity, and spray drying to a desirable particle size; (i) washing said spray dried particles to remove additional sodium and sulfate ions; (j) contacting with additional rare earth solution at a pH of about 5 so as to precipitate rare earth onto the matrix; (k) rinsing, dewatering and drying to a final product.
Claim 25
Dependent Claim
274 words
A process for the preparation of the catalyst of claim 14 comprising in combination, the steps of: (a) adding a sodium silicate solution to a batch tank so as to yield a concentration of 3 to 6% SiO 2 ; (b) dispersing kaolin clay in water in a concentration of 20 to 60% and combining with "a" in such proportions as to yield a catalyst containing 20 to 70% kaolin; (c) adding a solution of alum to "b", so as to bring the pH to 8 to 10 and holding at 24° C. to 49° C. (75° F. to 120° F.) for 1/2 hour or more; (d) adding a sodium aluminate solution to "c" so as to raise the pH back to 12; (e) adding to "d" an acid leached kaolin clay, which has been previously calcined, so as to drop the pH of "d" to 3; (f) adding a slurry of ammonium HY zeolite to "e" so as to produce a final content of 8 to 35% zeolite in the finished catalyst, said HY zeolite being exchanged with rare earth to the extend of 10-80% of full rare earth capacity; (g) adding NH 3 to this slurry so as to neutralize the alum and return the pH to 6-9 by precipitating alumina gel; (h) dewatering "g" by filtration, homogenizing, adjusting viscosity; and spray drying to a desirable particle size; (i) washing said spray dried particles to remove additional sodium and sulfate ions; (j) contacting with additional rare earth solution at a pH of about 5 so as to precipitate rare earth onto the matrix; (k) rinsing, dewatering and drying to a final product.
Claim 26
Dependent Claim
276 words
A process for the preparation of the catalyst of claim 1 comprising in combination, the steps of: (a) adding a sodium silicate solution to a batch tank so as to yeild a concentration of 3 to 6% SiO 2 ; (b) dispersing kaolin clay in water in a concentration of 20 to 60% and combining with "a" in such proportions as to yield a catalyst containing 20 to 70% kaolin; (c) adding a solution of alum to "b", so as to bring the pH to 8 to 10 and holding at 24° C. to 49° C. (75° F. to 120° F.) for 1/2 hour or more; (d) adding a sodium aluminate solution to "c" so as to raise the pH back to 12; (e) adding a reaction product of sulfuric acid with calcined kaolin or halloysite to "d" so as to drop the pH to 3; (f) adding a slurry of partially rare earth exchanged ammonium HY zeolite to "e" so as to produce a final content of 8 to 35% by weight zeolite in the finished catalyst, wherein said rare earth is exchange to the extent of 10-80% of available exchange capacity; (g) adding NH 3 to this slurry so as to neutralize the alum and return the pH to 6-9 by precipitating alumina gel; (h) dewatering "h" by filtration, homogenizing, adjusting viscosity, and spray drying to a desirable particle size; (i) washing said spray dried particles to remove additional sodium and sulfate ions; (j) contacting with additional rare earth solution at a pH of about 5 so as to precipitate rare earth onto the matrix; (k) rinsing, dewatering and drying to a final product.
Claim 27
Dependent Claim
107 words
The process of claim 20 in which the ammonium zeolite of "f" was obtained as a reaction product of the following sequence: washing a sodium Y zeolite with an ammonium ion solution to remove about 30 to about 60% of all sodium ions and treating the ammonium exchanged zeolite with a solution of rare earth chloride in a pressure reaction vessel for one to five hours at a temperature between about 121° C. to 232° C. (250° F. to 450° F.) so as to prepare an HY zeolite in which rare earth ion is caused to replace sodium in the sodalite cage of the ammonium Y zeolite.
Claim 28
Dependent Claim
267 words
A process for the preparation of the catalyst of claim 1 comprising in combination, the steps of: (a) adding a sodium silicate solution to a batch tank so as to yield a concentration of 3 to 6% SiO 2 ; (b) dispersing kaolin clay in water in a concentration of 20 to 60% and combining with "a" in such proportions as to yield a catalyst containing 20 to 70% kaolin; (c) adding a solution of alum to "b", so as to bring the pH to 8 to 10 and holding at 24° C. to 49° C. (75° F. to 120° F.) for 1/2 hour or more; (d) adding a sodium aluminate solution to "c" so as to raise the pH back to 12; (e) adding alum solution to "d" so as to drop the pH to 3; (f) adding a slurry of partially rare earth exhanged ammonium HY zeolite to "e" so as to produce a final content of 8 to 35% by weight zeolite in the finished catalyst, wherein said rare earth is exchange to the extent of 10-80% of available exchange capacity; (g) adding NH 3 to this slurry so as to neutralize the alum and return the pH to 6-9 by precipitating alumina gel; (h) dewatering "g" by filtration, homogenizing, adjusting viscosity, and spray drying to a desirable particle size; (i) washing said spray dried particles to remove additional sodium and sulfate ions; (j) contacting with additional rare earth solution at a pH of about 5 so as to precipitate rare earth onto the matrix; (k) rinsing, dewatering and drying to a final product.
Claim 29
Dependent Claim
27 words
A process as claimed in claim 20 in which said HY zeolite has been exchanged with rare earth to the extent to 30-60% full rare earth capacity.
Claim 30
Dependent Claim
17 words
A catalyst composition as described in claim 11 in which the alumina gel is present as pseudoboehmite.
Claim 31
Dependent Claim
21 words
A process as described in claim 20 wherein each step in the process occurs in a batch tank in batch operations.
Claim 32
Dependent Claim
31 words
A process as described in claim 20 wherein each step in the process is carried out continuously from one tank to another so as to result in a continuous flow system.
References Cited (Backward Citations)
US2840530A
Cited
US3816342A
Cited
US3553104A
Cited
US3449265A
Cited
US3556988A
Cited
US3790471A
Cited
US3717587A
Cited
US3696025A
Cited
US3867310A
Cited
US3912619A
Cited
US4144194A
Cited
US3930987A
Cited
US3867308A
Cited
US4199556A
Cited
US4010116A
Cited
US4086187A
Cited
US4164465A
Cited
US4100108A
Cited
US4085069A
Cited
US4192778A
Cited
US4058484A
Cited
US4088605A
Cited
US4148713A
Cited
US4203869A
Cited
US4142995A
Cited
US4198319A
Cited
US4310441A
Cited
US4215016A
Cited
US4224188A
Cited
US4253989A
Cited
US4219446A
Cited
US4333857A
Cited
US4206085A
Cited
US4246138A
Cited
US4259210A
Cited
US4237031A
Cited
US4226743A
Cited
US4309277A
Cited
US4239654A
Cited
US4234457A
Cited
US4252684A
Cited
US4263174A
Cited
US4228137A
Cited
US4325845A
Cited
US4319983A
Cited
US4269815A
Cited
US4325847A
Cited
US4339354A
Cited
US4415438A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-30 | 1988-04-30 | 1988-10-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-30 | 1992-04-30 | 1992-10-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-30 | 1996-04-30 | 1996-10-30 | $7700.00 | Window Closed / Lapsed |