Use of additional alumina for extra zeolite stability in FCC catalyst
Assignee: HARSHAW/FILTROL PARTNERSHIP A PARTNERSHIP OF
•
Filing: 1980-06-19
•
Granted: 1982-04-20
•
Expires: 2000-06-19
Abstract
Abstract This invention relates to improvements in catalysts formed by spray drying water slurries of a faujasite type zeolite of relatively low sodium content in a matrix, containing pseudoboehmite and added anionically derived alumina gel.
Inventors
- 👤 John C. Lim
- 👤 Adrian P. Humphries
- 👤 Dennis M. Stamires
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 00:26
CPC Classifications
C; C10; C10G; C10G11/00; C10G11/14; C10G11/18; B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; B01J29/08; B01J29/084; C10G11/02; C10G11/04; C10G11/05; B01J2229/00; B01J2229/30; B01J2229/37; B01J2229/42
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
65 words
A method of forming a catalyst which comprises mixing a sodium containing zeolite with an anionic aluminum source in water at a pH substantially above 7, adding an acidic compound and reducing the pH to substantially less than 7 and forming alumina hydrate gel in said water-zeolite mixture adding pseudoboehmite and clay to said water mixture to form a slurry and spray drying said slurry.
Claim 2
Independent Claim
65 words
A method of forming a catalyst which comprises mixing a sodium containing zeolite with an anionic aluminum source in water at a pH substantially above 7, adding an acidic compound and reducing the pH to substantially less than 7 and forming alumina hydrate gel in said water-zeolite mixture adding pseudoboehmite and clay to said water mixture to form a slurry and spray drying said slurry.
Claim 3
Independent Claim
79 words
A method of forming a catalyst which comprises mixing a sodium containing zeolite with an anionic aluminum source in water at a pH substantially above 7, adding an acid or an acidic salt and exchanging the sodium with a cation of said acidic compound, and reducing the pH to substantially less than 7 and forming alumina hydrate gel in said water-zeolite mixture adding pseudoboehmite and clay to said water mixture to form a slurry and spray dring said slurry.
Claim 4
Independent Claim
79 words
A method of forming a catalyst which comprises mixing a sodium containing zeolite with an anionic aluminum source in water at a pH substantially above 7, adding an acid or an acidic salt and exchanging the sodium with a cation of said acidic compound, and reducing the pH to substantially less than 7 and forming alumina hydrate gel in said water-zeolite mixture adding pseudoboehmite and clay to said water mixture to form a slurry and spray dring said slurry.
Claim 5
Independent Claim
67 words
A method of forming a catalyst which comprises mixing a sodium containing zeolite with an anionic aluminum source in water at a pH substantially above 7, adding an acidic compound and reducing the pH to substantially less than 7 and forming alumina hydrate gel in said water-zeolite mixture adding Type A pseudoboehmite and clay to said water mixture to form a slurry and spray drying said slurry.
Claim 6
Independent Claim
67 words
A method of forming a catalyst which comprises mixing a sodium containing zeolite with an anionic aluminum source in water at a pH substantially above 7, adding an acidic compound and reducing the pH to substantially less than 7 and forming alumina hydrate gel in said water-zeolite mixture adding Type A pseudoboehmite and clay to said water mixture to form a slurry and spray drying said slurry.
Claim 7
Independent Claim
85 words
A method of forming a catalyst which comprises mixing a sodium containing zeolite with an anionic aluminum source in water at a pH substantially above 7, chosen from the group consisting of an acid or an acidic salt and exchanging sodium with a cation of said acidic component, and reducing the pH to substantially less than 7, and forming alumina hydrate gel in said water-zeolite mixture adding Type A pseudoboehmite and clay to said water mixture to form a slurry and spray drying said slurry.
Claim 8
Independent Claim
85 words
A method of forming a catalyst which comprises mixing a sodium containing zeolite with an anionic aluminum source in water at a pH substantially above 7, chosen from the group consisting of an acid or an acidic salt and exchanging sodium with a cation of said acidic component, and reducing the pH to substantially less than 7, and forming alumina hydrate gel in said water-zeolite mixture adding Type A pseudoboehmite and clay to said water mixture to form a slurry and spray drying said slurry.
Claim 9
Independent Claim
112 words
A method of forming a catalyst which comprises mixing a sodium containing zeolite with an anionic aluminum source in water at a pH substantially above 7, adding a component chosen from the group of an acid or an acidic salt and exchanging sodium with a cation of said acidic component, and reducing the pH to substantially less than 7 and forming alumina hydrate gel and reducing the sodium in said zeolite by exchange with a cation of said acid or acidic salt in said water-zeolite-alumina gel mixture, adding a mixture of Type A and Type B pseudoboehmite and clay to said water mixture to form a slurry and spray drying said slurry.
Claim 10
Independent Claim
112 words
A method of forming a catalyst which comprises mixing a sodium containing zeolite with an anionic aluminum source in water at a pH substantially above 7, adding a component chosen from the group of an acid or an acidic salt and exchanging sodium with a cation of said acidic component, and reducing the pH to substantially less than 7 and forming alumina hydrate gel and reducing the sodium in said zeolite by exchange with a cation of said acid or acidic salt in said water-zeolite-alumina gel mixture, adding a mixture of Type A and Type B pseudoboehmite and clay to said water mixture to form a slurry and spray drying said slurry.
Claim 11
Dependent Claim
34 words
The process of claim 1, 2, 3, 4, or 5, in which the sodium content of the catalyst is less than 1% by weight expressed as Na 2 O on a volatile free basis.
Claim 12
Dependent Claim
45 words
The process of claim 1, 2, 3, 4, or 5, in which the sodium content of the zeolite alumina hydrate mixture, prior to admixture with the pseudoboehmite in the slurry is less than about 5% by weight of the zeolite on a volatile free basis.
Claim 13
Dependent Claim
76 words
The process of claim 1, 2, 3, 4, or 5, in which the slurry contains from about 5% to 50% by weight of the zeolite and alumina hydrate gel from about 2% to about 30%, pseudoboehmite from about 10% to about 30%, and kaolin clay from about 20% to about 80%, and ammonium polysilicate equivalent to about 2% to 15% expressed as SiO 2 , all based on the composite catalyst on a volatile free basis.
Claim 14
Dependent Claim
61 words
The process of claim 1, 2, 3, 4, or 5, in which the ratio of the weight of alumina hydrate gel to the total weight of pseudoboehmite and alumina hydrate both expressed as equivalent Al 2 O 3 on a volatile free basis is from about 25% to about 75% of the total weight of alumina on a volatile free basis.
Claim 15
Dependent Claim
140 words
The process of claims 1, 2, 3, 4, or 5, in which the slurry contains from about 5% to about 50% by weight of the zeolite, and alumina hydrate gel from about 2% to about 30%, pseudoboehmite from about 10% to about 30%, and kaolin clay from about 20% to about 80%, and from about 2% to about 15% of ammonium polysilicate equivalent to about 2% to 15% expressed as SiO 2 , all on a volatile free basis based on the catalyst and the ratio of the weight of alumina hydrate gel to the total weight of the alumina hydrate gel and the pseudoboehmite both expressed as the equivalent Al 2 O 3 on a volatile free basis is in the range of about 2% to about 75% of said total weight of the Al 2 O 3 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-04-19 | 1985-10-19 | 1986-04-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-04-19 | 1989-10-19 | 1990-04-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-04-19 | 1993-10-19 | 1994-04-20 | $7700.00 | Window Closed / Lapsed |