Method of producing zeolitic catalysts with silica alumina matrix
Assignee: HARSHAW/FILTROL PARTNERSHIP A PARTNERSHIP OF
•
Filing: 1978-02-03
•
Granted: 1980-04-15
•
Expires: 1998-02-03
Abstract
Abstract This invention relates to zeolitic catalysts composed of an exchanged zeolite of the faujasite type and a matrix composed of clay and an alumina-silica component.
Inventors
- 👤 Hamid Alafandi
- 👤 Dennis Stamires
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 14:19
CPC Classifications
C; C10; C10G; C10G11/00; C10G11/02; C10G11/04; C10G11/05; B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; B01J29/08; B01J29/084
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
41 words
In a process for forming a catalyst comprising mixing in a slurry a zeolite of the faujasite type, a silica-alumina gel containing silica in the range of about 50 to about 70 mole percent, and clay and spray drying said slurry.
Claim 2
Dependent Claim
41 words
In a process for forming a catalyst comprising mixing in a slurry a zeolite of the faujasite type, a silica-alumina gel containing silica in the range of about 50 to about 70 mole percent, and clay and spray drying said slurry.
Claim 3
Dependent Claim
69 words
The process of claim 1, in which the ratio of the zeolite, silica-alumina gel and clay are in the ratios of from about 10 to about 30 parts by weight of zeolite, and about 60 to 10 parts by weight of silica-alumina and about 70 to about 10 parts by weight of clay, the parts all components adding to a 100 parts by weight all on a volatile-free basis.
Claim 4
Dependent Claim
18 words
In the process of claim 2 in which said slurry contains about 10 to about 25% of pseudoboehmite.
Claim 5
Dependent Claim
26 words
In the process of claim 1, preparing said silica-alumina gel and adding said silica-alumina gel to said slurry separately from the addition of the other components.
Claim 6
Dependent Claim
31 words
In the process of claim 2, preparing said silica-alumina gel and separately mixing the zeolite with silica-alumina gel and then mixing the same with hydrated alumina and clay in said slurry.
Claim 7
Dependent Claim
35 words
The process of claim 1 exchanging said zeolite with a cation or cations chosen from the group consisting of H and NH 4 and polyvalent cations prior to mixing with said silica-alumina gel and claim.
Claim 8
Dependent Claim
21 words
The process of claim 2, exchanging said zeolite with a polyvalent cation prior to mixing with the silica-alumina gel and clay.
Claim 9
Dependent Claim
70 words
The process which comprises forming a mixture of a silica-alumina gel, said silica-alumina gel containing from about 50 to about 70 mole percent of SiO 2 , in a slurry containing a zeolite of the faujasite type and spray drying the mixture exchanging the spray dried mixture of the zeolite and silica-alumina with a cation or cations chosen from the group consisting of H and NH 4 and polyvalent cations.
Claim 10
Dependent Claim
70 words
The process which comprises forming a mixture of a silica-alumina gel, said silica-alumina gel containing from about 50 to about 70 mole percent of SiO 2 , in a slurry containing a zeolite of the faujasite type and spray drying the mixture exchanging the spray dried mixture of the zeolite and silica-alumina with a cation or cations chosen from the group consisting of H and NH 4 and polyvalent cations.
Claim 11
Dependent Claim
16 words
The process of claim 8 in which pseudoboehmite is added to the slurry before spray drying.
Claim 12
Dependent Claim
72 words
The process of claim 8 in which the ratio of the zeolite, hydrated alumina, silica-alumina gel and clay are in the ratios of from about 10 to about 30 parts by weight of zeolite, and about 60 to about 10 parts by weight of silica-alumina and about 70 to about 10 parts by weight of clay, the parts all four components adding to 100 parts by weight all on a volatile-free basis.
Claim 13
Dependent Claim
17 words
The process of claim 10 in which said slurry contains about 10 to about 25% of pseudoboehmite.
Claim 14
Dependent Claim
68 words
The process of forming a catalyst which comprises mixing a zeolite of the faujasite type with silica-alumina gel and clay in a water slurry, said silica-alumina gel containing from about 50 to about 70 mole percent of SiO 2 , and spray drying said slurry to form microspheres and exchanging said microspheres with a cation or cations chosen from the group of H, NH 4 and polyvalent cations.
Claim 15
Dependent Claim
68 words
The process of forming a catalyst which comprises mixing a zeolite of the faujasite type with silica-alumina gel and clay in a water slurry, said silica-alumina gel containing from about 50 to about 70 mole percent of SiO 2 , and spray drying said slurry to form microspheres and exchanging said microspheres with a cation or cations chosen from the group of H, NH 4 and polyvalent cations.
Claim 16
Dependent Claim
73 words
The process of claim 7 in which the ratio of the zeolite, silica-alumina gel and clay in the slurry are in the ratios of from about 10 to about 30 parts by weight of zeolite, and about 60 to about 10 parts by weight of silica-alumina and about 70 to about 10 parts by weight of clay, the parts all four components adding to 100 parts by weight all on a volatile-free basis.
Claim 17
Dependent Claim
17 words
The process of claim 13 in which the slurry contains about 10 to about 25% of pseudoboehmite.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-15 | 1983-10-15 | 1984-04-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-15 | 1987-10-15 | 1988-04-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-15 | 1991-10-15 | 1992-04-15 | $7700.00 | Window Closed / Lapsed |