Process for strengthening soft soil
Assignee: Chiyoda Corp
•
Filing: 1982-06-14
•
Granted: 1984-08-14
•
Expires: 2002-06-14
Abstract
Abstract A high water content soft soil, for example from the sea or river bed, may be improved in strength by incorporating thereinto a finely divided, quenched iron blast furnace slag treated with sulfuric acid, and a Portland cement. The sulfuric acid-treated slag is a product obtained by reacting a finely divided, quenched iron blast furnace slag, such as a water-granulated iron blast furnace slag, with sulfuric acid to convert a part of its calcium components into gypsum.
Inventors
- 👤 Hajime Miyoshi
- 👤 Etsuo Asanagi
- 👤 Osamu Terashima
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 02:40
CPC Classifications
C; C09; C09K; C09K17/00; C09K17/02; C09K17/10; C04; C04B; C04B18/00; C04B18/04; C04B18/14; C04B18/141; C04B28/00; C04B28/02; C04B28/04; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/91; Y10; Y10S; Y10S106/00; Y10S106/90
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
109 words
A process for improving the strength of a water-saturated soft soil comprising: providing a finely divided, non-crystalline, calcium-containing iron blast furnace slag; treating said slag with an aqueous solution containing 20-500 g sulfuric acid per 1 kg of slag to provide an acid-treated slag (A) with conversion of a part of the calcium content of said slag to gypsum; admixing said acid-treated slag with the soft soil to be treated; and admixing said acid treated slag and the soft soil with (B) a Portland cement to obtain an unconfined compressive strength of the soil greater than that obtained by using comparable amounts of cement, calcium sulfate and unacidified slag.
Claim 2
Dependent Claim
109 words
A process for improving the strength of a water-saturated soft soil comprising: providing a finely divided, non-crystalline, calcium-containing iron blast furnace slag; treating said slag with an aqueous solution containing 20-500 g sulfuric acid per 1 kg of slag to provide an acid-treated slag (A) with conversion of a part of the calcium content of said slag to gypsum; admixing said acid-treated slag with the soft soil to be treated; and admixing said acid treated slag and the soft soil with (B) a Portland cement to obtain an unconfined compressive strength of the soil greater than that obtained by using comparable amounts of cement, calcium sulfate and unacidified slag.
Claim 3
Dependent Claim
23 words
A process as recited in claim 1, wherein the ratio by weight of ingredient (A) to ingredient (B) is about 70/30 to 35/65.
Claim 4
Dependent Claim
19 words
A process as recited in claim 1, wherein the slag has a particle size of 300 μm or less.
Claim 5
Dependent Claim
17 words
A process as recited in claim 3, wherein the slag is a water-granulated iron blast furnace slag.
Claim 6
Dependent Claim
21 words
A process as recited in claim 1, wherein the soft soil is admixed with ingredient (A) before admixture with ingredient (B).
Claim 7
Dependent Claim
20 words
A process as recited in claim 1, wherein the soft soil is admixed with ingredient (A) and ingredient (B) simultaneously.
Claim 8
Dependent Claim
25 words
A process as recited in claim 6, comprising forming an aqueous slurry containing ingredients (A) and (B) and admixing the soft soil with said slurry.
Claim 9
Dependent Claim
32 words
A process as recited in claim 1, further comprising admixing said soft soil with a water-soluble ferrous salt, prior to the addition of ingredient (B), in amount effective to deodorize said soil.
Claim 10
Dependent Claim
25 words
The process of claim 1 wherein about 2-60% of the calcium components of the slag are converted into gypsum by reaction with the sulfuric acid.
Claim 11
Dependent Claim
25 words
The process of claim 1 wherein about 3-35% of the calcium components of the slag are converted into gypsum by reaction of the sulfuric acid.
References Cited (Backward Citations)
US3096188A
Cited
SU484200A1
Cited
US3953222A
Cited
SU759474A1
Cited
US4266980A
Cited
US4299516A
Cited
US4306910A
Cited
JPS56163204A
Cited
US4353749A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-08-14 | 1988-02-13 | 1988-08-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-08-14 | 1992-02-13 | 1992-08-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-08-14 | 1996-02-13 | 1996-08-14 | $7700.00 | Window Closed / Lapsed |