Method of forming metallic coatings on polymeric substrates
Assignee: United States Department of Energy
•
Filing: 1983-02-16
•
Granted: 1984-08-07
•
Expires: 2003-02-16
Abstract
Abstract Very smooth polymeric coatings or films graded in atomic number and densityan readily be formed by first preparing the coating or film from the desired monomeric material and then contacting it with a fluid containing a metal or a mixture of metals for a time sufficient for such metal or metals to sorb and diffuse into the coating or film. Metal resinate solutions are particularly advantageous for this purpose. A metallic coating can in turn be produced on the metal-loaded film or coating by exposing it to a low pressure plasma of air, oxygen, or nitrous oxide. The process permits a metallic coating to be formed on a heat sensitive substrate without the use of elevated temperatures.
Inventors
- 👤 Raimond Liepins
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 08:07
CPC Classifications
G; G21; G21B; G21B1/00; G21B1/11; G21B1/19; C; C03; C03C; C03C17/00; C03C17/34; C03C17/3405; C23; C23C; C23C16/00; C23C18/00; C23C18/02; C23C18/08; Y; Y02; Y02E; Y02E30/00; Y02E30/10
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
87 words
A method of forming a metallic coating on a polymeric substrate, comprising the steps of (a) contacting said polymeric substrate with a fluid containing a metal compound or mixture of metal compounds at a temperature below 150° C. for a time sufficient for said metal compound or mixture of metal compounds to sorb or diffuse into said polymeric substrate, and (b) subjecting said substrate containing said sorbed or diffused metal to a low pressure plasma for a time sufficient to form a metallic coating on said substrate.
Claim 2
Independent Claim
87 words
A method of forming a metallic coating on a polymeric substrate, comprising the steps of (a) contacting said polymeric substrate with a fluid containing a metal compound or mixture of metal compounds at a temperature below 150° C. for a time sufficient for said metal compound or mixture of metal compounds to sorb or diffuse into said polymeric substrate, and (b) subjecting said substrate containing said sorbed or diffused metal to a low pressure plasma for a time sufficient to form a metallic coating on said substrate.
Claim 3
Dependent Claim
21 words
The method of claim 1, wherein said plasma is formed in a low pressure atmosphere of oxygen, air, or nitrous oxide.
Claim 4
Dependent Claim
26 words
The method of claim 2 wherein said fluid containing a metal compound or mixture of metal compounds is a solution of one or more metal resinates.
Claim 5
Dependent Claim
25 words
The method of claim 2 or claim 3 wherein said metal or metals comprise Ta, W, Re, Os, Ir, Pt, Au, Hg, Pb, or Bi.
Claim 6
Dependent Claim
12 words
The method of claim 4 wherein said metal is Au or Pt.
Claim 7
Dependent Claim
23 words
The method of claim 2 or claim 3 wherein said polymeric substrate is an aliphatic or aromatic hydrocarbon coating or a perfluorocarbon coating.
Claim 8
Dependent Claim
11 words
The method of claim 6 wherein said polymeric coating is polycyclooctatetraene.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-08-07 | 1988-02-06 | 1988-08-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-08-07 | 1992-02-06 | 1992-08-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-08-07 | 1996-02-06 | 1996-08-07 | $7700.00 | Window Closed / Lapsed |