Multiple pass method of applying printing paste upon a substrate

Claim 2

A multiple pass method of applying printing paste upon a substrate comprising the steps of: applying to a substrate a first coat of a printing paste including about 80-92 weight percent of at least one finely divided, particulate inorganic material which can be fused, vitrified or crystallized at temperatures above about 200° F. and about 8-20 weight percent of a liquid vehicle comprising: a thermally stable organic binder which practically completely pyrolyzes while possessing the property of being substantially thermally stable at temperatures below about 200° F. and constituting about 10-35 weight percent of said vehicle, and a solvent system for said binder comprising a low boiling temperature organic solvent constituting about 30-70 weight percent of said vehicle and having a vapor pressure of less than about 2 mm Hg at a temperature in the temperature range about 20° C.-25° C. and having a vapor pressure in the vapor pressure range of about 2-100 mm Hg at a temperature in the temperature range of about 120° F.-200° F., and a high boiling temperature organic solvent constituting about 20-40 weight percent of said vehicle and having a vapor pressure of about 1 mm Hg or less at a temperature in the temperature range of about 120° F.-200° F. and having a vapor pressure in the vapor pressure range of about 2-100 mm Hg at a temperature in the temperature range of above about 200° F. to about 400° F.; exposing said first coat to a temperature in the temperature range of about 120° F.-200° F. for a time sufficient to remove substantially all of said low boiling temperature solvent without substantially removing said high boiling temperature solvent, thereafter superposing on said first coat an additional coat of printing paste having the above-defined characteristics of said first coat, exposing said superposed additional coat to a temperature in the temperature range of about 120° F.-200° F. for a time sufficient to remove substantially all of said low boiling temperature solvent from said superposed additional coat, subsequently exposing said first coat and said superposed additional coat to a temperature in the temperature range of above about 200° F. for a time sufficient to remove substantially all of said high boiling temperature solvent therefrom and practically completely pyrolyze said thermally stable binder and to fuse, vitrify or crystallize said particulate inorganic material.

Claim 3

The method according to claim 1, with said first coat and said additional coat being applied in a predetermined thickness selected to provide a resulting coating thickness of about 5-6 mils thickness upon removal of substantially all of said low boiling temperature organic solvent therefrom.

Claim 4

The method according to claim 1, wherein said substrate consists essentially of alumina.

Claim 5

The method according to claim 1, wherein said thermally stable organic binder is selected to possess a pyrolyzation temperature in the temperature range of about 150° C.-400° C., and wherein said step of subsequently exposing said first coat and said additional coat to a temperature in the temperature range of above about 200° F. includes exposing said first coat and said additional coat to a temperature in the temperature range of about 150° C.-400° C. to pyrolyze essentially all of said thermally stable organic binder in each said coat.

Claim 6

The method according to claim 1, wherein said finely divided, particulate inorganic material and said substrate are selected to possess properties compatible for use in microelectronic devices.

Claim 7

The method according to claim 1, wherein of the total amount of said thermally stable organic binder and said organic solvent system, said organic binder comprises about 10-30 weight percent, said low boiling temperature organic solvent comprises about 40-70 weight percent and said high boiling temperature organic solvent comprises about 20-40 weight percent.

Claim 8

The method according to claim 6, wherein said thermally stable organic binder is a poly (alpha-methyl) styrene having a molecular weight of about 250-1000, said low boiling temperature organic solvent is a mixture of isomeric terpineols composed predominantly of alpha-terpineol with minor amounts of beta-terpineol and gamma-terpineol, and said high boiling temperature organic solvent is diisobutyl adipate or a polypropylene glycol having an average molecular weight of about 200 or 400 or mixtures of polypropylene glycols having such average molecular weights.

Claim 9

The method according to claim 7, wherein said thermally stable organic binder has a specific gravity at 60/60° C. of about 1.01 and a refractive index at 60° C. of about 1.58.

Claim 10

The method according to claim 1, wherein said thermally stable organic binder is a poly (n-butyl methacrylate), said low boiling temperature organic solvent is a mixture of isomeric terpineols composed predominantly of alpha-terpineol with minor amounts of beta-terpineol and gamma-terpineol, and said high boiling temperature organic solvent comprises diisobutyl adipate.

Claim 11

The method according to claim 9, wherein of the total amount of said liquid vehicle said terpineol mixture comprises about 50 weight percent and a mixture of said thermally stable organic binder and said diisobutyl adipate comprise about 50 weight percent, and wherein the weight ratio of said diisobutyl adipate to said poly (n-butyl methacrylate) is about 3:1.

Claim 12

The method according to claim 1, wherein said printing paste consists essentially of about 10-14 weight percent of said thermally stable organic binder and about 86-90 weight percent of said particulate inorganic material as a sealing glass.

Claim 13

The method according to claim 11, wherein said printing paste has a viscosity of about 38,000-46,000 centipoise.

Claim 14

The method according to claim 1, wherein said thermally stable organic binder comprises poly(alpha-methyl) styrene having a molecular weight of about 259-1000.

Claim 15

The method according to claim 1, wherein said thermally stable organic binder comprises poly(alpha-methyl) styrene having a molecular weight of about 250-1000, and wherein said low boiling temperature organic solvent comprises a mixture of isomeric terpineols composed predominantly of alpha-terpineol with minor amounts of beta-terpineol and gamma terpineol, and wherein said high boiling temperature organic solvent comprises polypropylene glycol having an average molecular weight of about 200 or 400 or mixtures of polypropylene glycols having such average molecular weights.

Claim 16

The method according to claim 1, wherein said low boiling temperature organic solvent comprises a mixture of isomeric terpineols composed predominantly of alpha-terpineol with minor amounts of beta-terpineol and gamma-terpineol.

Claim 17

The method according to claim 1, wherein said high boiling temperature organic solvent comprises diisobutyl adipate.

Claim 18

The method according to claim 1, wherein said high boiling temperature organic solvent comprises polypropylene glycol having an average molecular weight of about 200 or 400 or mixtures of polypropylene glycols having such molecular weights.

Claim 19

The method according to claim 1, wherein said printing paste has a viscosity of about 38,000-46,000 centipoise.

Claim 20

A multiple pass method of applying printing paste upon a substrate comprising the steps of: applying to a substrate a first coat of a printing paste including about 80-92 weight percent of at least one finely divided, particulate inorganic material which can be fused, vitrified, or crystallized at temperatures above about 200° F. and about 8-20 weight percent of a liquid vehicle comprising: a thermally stable organic binder which practically completely pyrolyzes while possessing the property of being substantially thermally stable at temperatures below about 200° F. and constituting about 10-35 weight percent of said vehicle, and a solvent system for said binder, comprising a low boiling temperature organic solvent constituting about 30-70 weight percent of said vehicle and having a vapor pressure of less than about 2 mm Hg at a temperature in the temperature range about 20° C.-25° C. and having a vapor pressure in the vapor pressure range of about 2-100 mm Hg at a temperature in the temperature range of about 120° F.-- 200° F., and a high boiling temperature organic solvent constituting about 20-40 weight percent of said vehicle and having a vapor pressure of about 1 mm Hg or less at a temperature in the temperature range of about 120° F.-200° F. and having a vapor pressure in the vapor pressure range of about 2-100 mm Hg at a temperature in the temperature range of above about 200° F. to about 400° F.; exposing said first coat to a temperature in the temperature range of about 120° F.-200° F. for a time sufficient to remove substantially all of said low boiling temperature solvent without substantially removing said high boiling temperature solvent, thereafter superposing on said first coat a plurality of additional coats of printing paste having the above-defined characteristics of said first coat and successively exposing each of said superposed additional coats to a temperature in the temperature range of about 120° F.-200° F. for a time sufficient to remove substantially all of said low boiling temperature solvent without substantially evaporating said high boiling temperature solvent prior to applying the next additional superposed coat, subsequently exposing said first coat and each of said plurality of additional coats to a temperature in the temperature range of above about 200° F. for a time sufficient to remove substantially all of said high boiling temperature solvent therefrom and practically completely pyrolyze said thermally stable binder and to fuse, vitrify or crystallize said particulate inorganic material.

Claim 21

A multiple pass method of applying printing paste upon a substrate comprising the steps of: applying to a substrate a first coat of a printing paste including about 80-92 weight percent of at least one finely divided, particulate inorganic material which can be fused, vitrified, or crystallized at temperatures above about 200° F. and about 8-20 weight percent of a liquid vehicle comprising: a thermally stable organic binder which practically completely pyrolyzes while possessing the property of being substantially thermally stable at temperatures below about 200° F. and constituting about 10-35 weight percent of said vehicle, and a solvent system for said binder, comprising a low boiling temperature organic solvent constituting about 30-70 weight percent of said vehicle and having a vapor pressure of less than about 2 mm Hg at a temperature in the temperature range about 20° C.-25° C. and having a vapor pressure in the vapor pressure range of about 2-100 mm Hg at a temperature in the temperature range of about 120° F.-- 200° F., and a high boiling temperature organic solvent constituting about 20-40 weight percent of said vehicle and having a vapor pressure of about 1 mm Hg or less at a temperature in the temperature range of about 120° F.-200° F. and having a vapor pressure in the vapor pressure range of about 2-100 mm Hg at a temperature in the temperature range of above about 200° F. to about 400° F.; exposing said first coat to a temperature in the temperature range of about 120° F.-200° F. for a time sufficient to remove substantially all of said low boiling temperature solvent without substantially removing said high boiling temperature solvent, thereafter superposing on said first coat a plurality of additional coats of printing paste having the above-defined characteristics of said first coat and successively exposing each of said superposed additional coats to a temperature in the temperature range of about 120° F.-200° F. for a time sufficient to remove substantially all of said low boiling temperature solvent without substantially evaporating said high boiling temperature solvent prior to applying the next additional superposed coat, subsequently exposing said first coat and each of said plurality of additional coats to a temperature in the temperature range of above about 200° F. for a time sufficient to remove substantially all of said high boiling temperature solvent therefrom and practically completely pyrolyze said thermally stable binder and to fuse, vitrify or crystallize said particulate inorganic material.