Method for producing a MISFET
Assignee: UK Secretary of State for Defence
•
Filing: 1982-07-12
•
Granted: 1984-06-12
•
Expires: 2002-07-12
Abstract
Abstract A method for producing a MISFET having a gate electrode formed at the base of a grooved recess. The grooved recess is formed with steep side-walls (e.g., be reactive ion etching, ion beam milling or by using an orientation dependent etchant) and gate and source and drain contacts are formed by the simultaneous deposition of conductive material (e.g., metal evaporated from a point source.) Steepness of the side-walls of the recess ensures separation of the conductive material, isolating the gate electrode from the remaining conductive material providing the source and drain contacts. A silicon MISFET may be produced, using a diazine catalyzed ethylenediamine-pyrocatechol-water solution etchant, and exposing the (110) crystal plane face of the silicon to the etchant to form the recess.
Inventors
- 👤 Timothy W. Janes
- 👤 John C. White
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 14:51
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/20; H10D64/27; H10D64/311; H10D64/411; H10D64/511; H10D64/512; H10D64/513; H10D30/00; H10D30/60; H10D64/01; H10D64/011; H10D64/025; H10D64/027; H10P; H10P50/00; H10P50/60; H10P50/64; H10P50/642; H10P50/644; H10D62/00; H10D62/40; H10D62/405
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
161 words
A method for producing a MISFET (metal-insulator-semiconductor field-effect transistor), the method comprising the following steps: (a) providing a substrate of single crystal semiconductor material; forming an excess doped region of semiconductor material of opposite conductivity type for (b) providing the source and drain regions of the MISFET; (c) forming, between and immediately adjacent the source and drain regions, a steep-walled groove extending depthwise at least to the interface between the excess doped material and the underlying substrate material; (d) forming an insulating layer over the surface of the groove and over the excess doped material, windows being provided in the layer to expose the source and drain regions of the excess doped material; (e) depositing conductive material so to cover simultaneously the exposed source and drain regions and the base of the groove, to exclusion of the steep side-walls of the groove; and (f) annealing the whole to consolidate the contact junctions between the conductive material and the excess doped material.
Claim 2
Independent Claim
161 words
A method for producing a MISFET (metal-insulator-semiconductor field-effect transistor), the method comprising the following steps: (a) providing a substrate of single crystal semiconductor material; forming an excess doped region of semiconductor material of opposite conductivity type for (b) providing the source and drain regions of the MISFET; (c) forming, between and immediately adjacent the source and drain regions, a steep-walled groove extending depthwise at least to the interface between the excess doped material and the underlying substrate material; (d) forming an insulating layer over the surface of the groove and over the excess doped material, windows being provided in the layer to expose the source and drain regions of the excess doped material; (e) depositing conductive material so to cover simultaneously the exposed source and drain regions and the base of the groove, to exclusion of the steep side-walls of the groove; and (f) annealing the whole to consolidate the contact junctions between the conductive material and the excess doped material.
Claim 3
Dependent Claim
29 words
A method as claimed in claim 1 wherein the steep-walled groove is formed by etching, using an orientation dependant etchant to define the steep side walls of the groove.
Claim 4
Dependent Claim
59 words
A method as claimed in claim 2 wherein the substrate and the doped region are silicon semiconductor material, and the etchant is a diazine catalyzed ethylenediamine-pyrocatechol-water solution; the steep-walled groove being formed exposing (110) crystal plane face of the doped silicon material to the etchant through a mask window the edges of which are aligned with {111} crystal planes.
Claim 5
Dependent Claim
30 words
A method as claimed in claim 3 wherein an electrical bias is applied across the doped silicon interface to stop etching action when the groove extends depthwise to the interface.
Claim 6
Dependent Claim
27 words
A method as claimed in claim 4 wherein the bias is removed once the etching action has stopped, and etching recontinued for a controlled period of time.
Claim 7
Dependent Claim
26 words
A method as claimed in claim 4 wherein once the etching action has stopped the pyrocatechol etchant is replaced by a slow-action etchant and etching recontinued.
Claim 8
Dependent Claim
23 words
A method as claimed in claim 1 wherein the conductive material is a metal, and is deposited by evaporation from a point source.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-12 | 1987-12-12 | 1988-06-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-12 | 1991-12-12 | 1992-06-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-12 | 1995-12-12 | 1996-06-12 | $7700.00 | Window Closed / Lapsed |