Aromatic pitch from asphaltene-free steam cracker tar fractions
Assignee: EIDP Inc
•
Filing: 1982-02-08
•
Granted: 1984-02-14
•
Expires: 2002-02-08
Abstract
Abstract A process and a product of the process for preparing a pitch suitable for carbon artifact manufacture features a pitch having a weight content of between 80 and 100 percent toluene insolubles. The pitch is derived from a deasphaltenated middle fraction of a steam cracker tar feedstock. The middle fraction is rich in 2, 3, 4, and 5 polycondensed aromatic rings. The pitch is characterized as being relatively free of impurities and ash.
Inventors
- 👤 Ghazi Dickakian
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 18:25
CPC Classifications
D; D01; D01F; D01F9/00; D01F9/08; D01F9/12; D01F9/14; D01F9/145; D01F9/155; C; C10; C10C; C10C3/00; C10C3/002
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
68 words
A pitch suitable for carbon artifact manufacture, comprising by weight content between 80 and 100 percent toluene insolubles, said pitch having been derived, by heat soaking followed by vacuum stripping, from a deasphaltenated middle fraction of a steam cracker tar feedstock which is rich in 2, 3, 4 and 5 polycondensed aromatic rings, and wherein said pitch is further characterized as being relatively free of impurities and ash.
Claim 2
Dependent Claim
68 words
A pitch suitable for carbon artifact manufacture, comprising by weight content between 80 and 100 percent toluene insolubles, said pitch having been derived, by heat soaking followed by vacuum stripping, from a deasphaltenated middle fraction of a steam cracker tar feedstock which is rich in 2, 3, 4 and 5 polycondensed aromatic rings, and wherein said pitch is further characterized as being relatively free of impurities and ash.
Claim 3
Dependent Claim
28 words
The pitch of claim 1, wherein said middle fraction is a distillate fraction boiling off at temperatures approximately between 370° and 490° C. at 760 mm of mercury.
Claim 4
Dependent Claim
80 words
A pitch suitable for carbon artifact manufacture, such as the manufacture of carbon fibers, comprising by weight content between 80 and 100 percent toluene insolubles, and derived, by heat soaking followed by vacuum stripping, from a deasphaltenated middle fraction of a steam cracker tar bottom, said middle fraction being a distillate fraction boiling off at a temperature approximately between 370° and 490° C. at 760 mm mercury, said pitch being further characterized as being relatively free of impurities and ash.
Claim 5
Dependent Claim
80 words
A pitch suitable for carbon artifact manufacture, such as the manufacture of carbon fibers, comprising by weight content between 80 and 100 percent toluene insolubles, and derived, by heat soaking followed by vacuum stripping, from a deasphaltenated middle fraction of a steam cracker tar bottom, said middle fraction being a distillate fraction boiling off at a temperature approximately between 370° and 490° C. at 760 mm mercury, said pitch being further characterized as being relatively free of impurities and ash.
Claim 6
Dependent Claim
20 words
The pitch of claim 3, wherein said middle fraction is rich in 2, 3, 4, and 5 polycondensed aromatic rings.
Claim 7
Dependent Claim
71 words
A pitch suitable for carbon artifact manufacture, comprising by weight content between 80 and 100 percent toluene insolubles, said pitch having been derived, by heat soaking followed by vacuum stripping, from a deasphaltenated middle fraction of a steam cracker tar feedstock which is rich in 2, 3, 4, and 5 polycondensed aromatic rings, and wherein said pitch is further characterized as having approximately less than 15 percent quinoline insolubles by weight.
Claim 8
Dependent Claim
71 words
A pitch suitable for carbon artifact manufacture, comprising by weight content between 80 and 100 percent toluene insolubles, said pitch having been derived, by heat soaking followed by vacuum stripping, from a deasphaltenated middle fraction of a steam cracker tar feedstock which is rich in 2, 3, 4, and 5 polycondensed aromatic rings, and wherein said pitch is further characterized as having approximately less than 15 percent quinoline insolubles by weight.
Claim 9
Dependent Claim
28 words
The pitch of claim 5, wherein said middle fraction is a distillate fraction boiling off at temperatures approximately between 370° and 490° C. at 760 mm of mercury.
Claim 10
Dependent Claim
88 words
A process for preparing a pitch suitable for carbon artifact manufacture, comprising the steps of: (a) obtaining a deasphaltenated middle fraction of a steam cracker tar feedstock which is rich in 2, 3, 4 and 5 polycondensed aromatic rings; (b) subjecting said middle fraction to heat soaking to produce a pitch intermediate; and (c) stripping oils from said pitch intermediate to produce a pitch comprising between 80 and 100 percent by weight of toluene insolubles, and which is further characterized as being relatively free of impurities and ash.
Claim 11
Dependent Claim
88 words
A process for preparing a pitch suitable for carbon artifact manufacture, comprising the steps of: (a) obtaining a deasphaltenated middle fraction of a steam cracker tar feedstock which is rich in 2, 3, 4 and 5 polycondensed aromatic rings; (b) subjecting said middle fraction to heat soaking to produce a pitch intermediate; and (c) stripping oils from said pitch intermediate to produce a pitch comprising between 80 and 100 percent by weight of toluene insolubles, and which is further characterized as being relatively free of impurities and ash.
Claim 12
Dependent Claim
43 words
The process of claim 7, wherein said heat soaking of said middle fraction is accomplished at a temperature in an approximate range of between 390° and 450° C. for a duration of from 1 minute to 20 hours at 760 mm of mercury.
Claim 13
Dependent Claim
26 words
The process of claim 8, wherein said middle fraction is heat soaked at approximately 430° C. for 2 to 6 hours at 760 mm of mercury.
Claim 14
Dependent Claim
32 words
The process of claim 7, wherein said middle fraction is obtained by distilling said feedstock at a temperature in an approximate range of between 370° and 490° C. at 760mm of mercury.
Claim 15
Dependent Claim
36 words
The process of claim 10 wherein said oils are removed by vacuum stripping said intermediate at a temperature in an approximate range of between 370° to 420° C. at approximately 1 to 100 mm of mercury.
Claim 16
Dependent Claim
82 words
A process for preparing a pitch suitable for carbon artifact manufacture, comprising the steps of: (a) distilling a steam cracker tar feedstock to obtain a deasphaltenated middle fraction rich in 2, 3, 4, and 5 polycondensed aromatic rings; (b) heat soaking said middle fraction; and (c) vacuum stripping said heat soaked middle fraction to remove oils therefrom, resulting in a pitch comprising 80 to 100 percent by weight of toluene insolubles and further characterized as being relatively free of impurities and ash.
Claim 17
Dependent Claim
82 words
A process for preparing a pitch suitable for carbon artifact manufacture, comprising the steps of: (a) distilling a steam cracker tar feedstock to obtain a deasphaltenated middle fraction rich in 2, 3, 4, and 5 polycondensed aromatic rings; (b) heat soaking said middle fraction; and (c) vacuum stripping said heat soaked middle fraction to remove oils therefrom, resulting in a pitch comprising 80 to 100 percent by weight of toluene insolubles and further characterized as being relatively free of impurities and ash.
Claim 18
Dependent Claim
45 words
The process of claim 12, wherein said heat soaking step (b) includes heat soaking said middle fraction at a temperature in an approximate range of between 390° and 450° C. for a duration of from 1 minute to 20 hours at 760 mm of mercury.
Claim 19
Dependent Claim
26 words
The process of claim 13, wherein said middle fraction is heat soaked at approximately 430° C. for 2 to 6 hours at 760 mm of mercury.
Claim 20
Dependent Claim
31 words
The process of claim 12, wherein said distilling step (a) includes distilling said feedstock at a temperature in an approximate range of 370° to 490° C. at 760 mm of mercury.
Claim 21
Dependent Claim
40 words
The process of claim 12, wherein said vacuum stripping step (c) includes vacuum stripping said heat soaked middle fraction at a temperature in an approximate range of between 370° and 420° C. at approximately 1 to 100 mm of mercury.
Claim 22
Dependent Claim
82 words
A process for preparing a pitch suitable for carbon artifact manufacture, comprising the steps of: (a) distilling a steam cracker tar bottom to obtain a deasphaltenated middle fraction rich in 2, 3, 4, and 5 polycondensed aromatic rings; (b) heat soaking said middle fraction; and (c) vacuum stripping said heat soaked middle fraction to remove oils therefrom, resulting in a pitch comprising 80 to 100 percent by weight of toluene insolubles and further characterized as being relatively free of impurities and ash.
Claim 23
Dependent Claim
82 words
A process for preparing a pitch suitable for carbon artifact manufacture, comprising the steps of: (a) distilling a steam cracker tar bottom to obtain a deasphaltenated middle fraction rich in 2, 3, 4, and 5 polycondensed aromatic rings; (b) heat soaking said middle fraction; and (c) vacuum stripping said heat soaked middle fraction to remove oils therefrom, resulting in a pitch comprising 80 to 100 percent by weight of toluene insolubles and further characterized as being relatively free of impurities and ash.
Claim 24
Dependent Claim
81 words
A pitch suitable for carbon artifact manufacture made by the process including the steps of: (a) distilling a steam cracker tar to obtain a deasphaltenated middle fraction rich in 2, 3, 4, and 5 polycondensed aromatic rings; (b) heat soaking said middle fraction; and (c) vacuum stripping said heat soaked middle fraction to remove oils therefrom, resulting in a pitch comprising 80 to 100 percent by weight of toluene insolubles and further characterized as being relatively free of impurities and ash.
Claim 25
Dependent Claim
81 words
A pitch suitable for carbon artifact manufacture made by the process including the steps of: (a) distilling a steam cracker tar to obtain a deasphaltenated middle fraction rich in 2, 3, 4, and 5 polycondensed aromatic rings; (b) heat soaking said middle fraction; and (c) vacuum stripping said heat soaked middle fraction to remove oils therefrom, resulting in a pitch comprising 80 to 100 percent by weight of toluene insolubles and further characterized as being relatively free of impurities and ash.
Claim 26
Dependent Claim
84 words
A process for preparing a pitch suitable for carbon artifact manufacture, comprising the steps of: (a) distilling a steam cracker tar bottom to obtain a deasphaltenated middle fraction rich in 2, 3, 4, and 5 polycondensed aromatic rings; (b) heat soaking said middle fraction; and (c) vacuum stripping said heat soaked middle fraction to remove oils therefrom, resulting in a pitch comprising 80 to 100 percent by weight of toluene insolubles and further characterized as having approximately less than 15% by weight quinoline insolubles.
Claim 27
Dependent Claim
84 words
A process for preparing a pitch suitable for carbon artifact manufacture, comprising the steps of: (a) distilling a steam cracker tar bottom to obtain a deasphaltenated middle fraction rich in 2, 3, 4, and 5 polycondensed aromatic rings; (b) heat soaking said middle fraction; and (c) vacuum stripping said heat soaked middle fraction to remove oils therefrom, resulting in a pitch comprising 80 to 100 percent by weight of toluene insolubles and further characterized as having approximately less than 15% by weight quinoline insolubles.
Claim 28
Dependent Claim
84 words
A pitch suitable for carbon artifact manufacture made by the process including the steps of: (a) distilling a steam cracker tar to obtain a deasphaltenated middle fraction rich in 2, 3, 4, and 5 polycondensed aromatic rings; p1 (b) heat soaking said middle fraction; and (c) vacuum stripping said heat soaked middle fraction to remove oils therefrom, resulting in a pitch comprising 80 to 100 percent by weight of toluene insolubles and further characterized as having approximately less than 15% by weight quinoline insolubles.
Claim 29
Dependent Claim
84 words
A pitch suitable for carbon artifact manufacture made by the process including the steps of: (a) distilling a steam cracker tar to obtain a deasphaltenated middle fraction rich in 2, 3, 4, and 5 polycondensed aromatic rings; p1 (b) heat soaking said middle fraction; and (c) vacuum stripping said heat soaked middle fraction to remove oils therefrom, resulting in a pitch comprising 80 to 100 percent by weight of toluene insolubles and further characterized as having approximately less than 15% by weight quinoline insolubles.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-02-13 | 1987-08-15 | 1988-02-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-02-13 | 1991-08-15 | 1992-02-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-02-13 | 1995-08-15 | 1996-02-14 | $7700.00 | Window Closed / Lapsed |