AC Etching of aluminum capacitor foil
Assignee: SPAGUE ELECTRIC Co N ADAMS MA A MA CORP
•
Filing: 1982-09-24
•
Granted: 1984-01-24
•
Expires: 2002-09-24
Abstract
Abstract In the AC etching of aluminum foil in a hydrochloric acid electrolyte containing at least one additive, the presence of 200 to 500 ppm sulfate permits etching thicker foil for higher voltage use than is possible without the sulfate. The additive is chosen from phosphoric, nitric, and tartaric acids or salts. The presence of the relatively small amount of sulfate yields a foil with higher capacitance and generally allows lower temperatures and frequencies to be used.
Inventors
- 👤 Trung H. Nguyen
- 👤 John J. Randall, Jr.
- 👤 Allan B. McPherson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 22:46
CPC Classifications
H; H01; H01G; H01G9/00; H01G9/004; H01G9/04; H01G9/048; H01G9/055; C; C25; C25F; C25F3/00; C25F3/02; C25F3/04
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
120 words
In a process for the etching of aluminum capacitor foil comprising passing said foil under the influence of alternating current through hydrochloric acid-based electrolyte containing at least one additive selected from the group consisting of phosphoric, nitric, and tartaric acids, the hydrochloric acid concentration being 0.5 to 1.5 M, the concentration of said additive being 0.1 to 0.3 M, the frequency of said alternating current being 10 up to 15 Hz, and the temperature being 24° to 37° C., the addition of 200 to 500 ppm sulfate to the etchant permits etching of 3.0 to 5 mil thick foil for the production of foil for higher voltage use than that obtained with the same electrolyte in the absence of sulfate.
Claim 2
Dependent Claim
120 words
In a process for the etching of aluminum capacitor foil comprising passing said foil under the influence of alternating current through hydrochloric acid-based electrolyte containing at least one additive selected from the group consisting of phosphoric, nitric, and tartaric acids, the hydrochloric acid concentration being 0.5 to 1.5 M, the concentration of said additive being 0.1 to 0.3 M, the frequency of said alternating current being 10 up to 15 Hz, and the temperature being 24° to 37° C., the addition of 200 to 500 ppm sulfate to the etchant permits etching of 3.0 to 5 mil thick foil for the production of foil for higher voltage use than that obtained with the same electrolyte in the absence of sulfate.
Claim 3
Dependent Claim
32 words
A process according to claim 1 wherein said etchant is 0.5 to 1 M hydrochloric acid, 0.1 to 0.2 M phosphoric acid, 0.1 to 0.3 M nitric acid, and 200-500 ppm sulfate.
Claim 4
Dependent Claim
32 words
A process according to claim 1 wherein the etchant is 1.0 to 1.5 M hydrochloric acid, 0.1 to 0.3 M nitric acid, 0.1 to 0.2 M tartaric acid, and 200-500 ppm sulfate.
Claim 5
Dependent Claim
26 words
A process according to claim 1 wherein said etchant is 0.5 to 1.5 M hydrochloric acid, 0.1 to 0.3 M nitric acid, and 200-500 ppm sulfate.
References Cited (Backward Citations)
US3284326A
Cited
US3321389A
Cited
US3728237A
Cited
US3887447A
Cited
US4052275A
Cited
US4297184A
Cited
US4276129A
Cited
US4332652A
Cited
US4376686A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-01-23 | 1987-07-25 | 1988-01-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-01-23 | 1991-07-25 | 1992-01-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-01-23 | 1995-07-25 | 1996-01-24 | $7700.00 | Window Closed / Lapsed |