Abstract A method of etching aluminum by applying an alternating electric current to aluminum which is in contact with an electrolyte containing hydrochloric acid, in which the alternating current has a symmetrical waveform wherein the current rises rapidly from zero to a maximum, then subsequently decreases rapidly in a first stage to an intermediate value which is about one-third to about one-half of the maximum, and thereafter decreases more slowly to zero in a second stage. Thereafter the current rises and falls in the opposite direction with the same waveform. The ratio of time of the second stage to time of the first stage of the waveform is in the range from 1 to 6. By this procedure higher capacitance values of the etched aluminum are obtained in comparison to prior procedures.
In a method of etching aluminum by applying an alternating electric current to aluminum which is in contact with an electrolyte containing hydrochloric acid, the improvement in which the alternating current has a wave form wherein the current rises rapidly from zero to a maximum, then subsequently decreases rapidly in a first stage to an intermediate value which is about one-third to about one-half of the maximum, and thereafter decreases more slowly to zero in a second stage, the ratio of time of the second stage to time of the first stage being in the range from 1 to 6, whereby higher capacitance values of the etched aluminum are obtained.
Claim 2
Dependent Claim
110 words
In a method of etching aluminum by applying an alternating electric current to aluminum which is in contact with an electrolyte containing hydrochloric acid, the improvement in which the alternating current has a wave form wherein the current rises rapidly from zero to a maximum, then subsequently decreases rapidly in a first stage to an intermediate value which is about one-third to about one-half of the maximum, and thereafter decreases more slowly to zero in a second stage, the ratio of time of the second stage to time of the first stage being in the range from 1 to 6, whereby higher capacitance values of the etched aluminum are obtained.
Claim 3
Dependent Claim
24 words
The method of claim 1 wherein the ratio of the second stage to the first stage is in the range from 1 to 3.
Claim 4
Independent Claim
20 words
The method of claims 1 or 2 wherein the waveform of the first stage of current is a triangular wave.
Claim 5
Independent Claim
20 words
The method of claims 1 or 2 wherein the waveform of the first stage of current is a sine wave.
Claim 6
Independent Claim
20 words
The method of claims 1 or 2 wherein the waveform of the first stage of current is a square wave.
Claim 7
Independent Claim
26 words
The method of claims 1 or 2 wherein the current density is in the range from 100 to 300 milliamperes (rms) per square centimeter of aluminum.
Claim 8
Dependent Claim
23 words
The method of claim 1 or 2 wherein the frequency of the alternating current is in the range from 15 to 25 hertz.